Coating composition for sealing surfaces

Patent metadata

Field	Value
Publication number	US-9309437-B2
Application number	US-201113640457-A
Country	US
Kind code	B2
Filing date	Apr 11, 2011
Priority date	Apr 23, 2010
Publication date	Apr 12, 2016
Grant date	Apr 12, 2016

Abstract

Weather resistant and water repellent surfacing compositions especially useful in roofing applications contain an alkoxysilane-terminated polymer and a reactive silane plasticizer containing a C 6-40 hydrocarbon group. The surfacing compositions are of low viscosity and may be used without non-reactive plasticizers or organic solvents.

First claim

The invention claimed is:

1. A moisture-curing coating composition, comprising
A) 100 parts by weight of at least one silane-terminated polymer having end groups of the formula (I)
-A-Si(OR 1 ) x R 2 3-x   (I),

B) 30 to 200 parts by weight of at least one reactive plasticizer of the formula (II),
R 3 —Si(OR 4 ) y R 5 3-y   (II),

C) 0 to 400 parts by weight of filler, and
D) 0.01 to 20 parts by weight of curing catalyst,
where

A is a linear or branched alkylene group having 1 to 10 carbon atoms,
R 1 and R 4 are each independently a linear or branched, unsubstituted or halogen-substituted alkyl group having 1 to 10 carbon atoms,
R 2 and R 5 are each independently a linear or branched, unsubstituted or halogen-substituted alkyl group having 1 to 5 carbon atoms,
R 3 is an aryl group or a linear, branched or cyclic alkyl group or alkenyl group having 6 to 40 carbon atoms, in which individual hydrogen atoms may be substituted by organic radicals, and, if R 3 is a linear, branched or cyclic alkyl group or alkenyl group, the carbon chain may be interrupted by oxygen atoms, and
x and y are 1, 2 or 3, and
wherein the silane-terminated polymers are polyesters, polyethers, polyalkylenes, and/or polyacrylates, and
wherein the reactive plasticizer of formula (II) is present in an amount of at least 15% by weight relative to the total weight of the coating composition.

2. The moisture-curing coating composition of claim 1 , wherein the polymer(s) comprise end groups of the formula (IV)
˜O—C(═O)—NH-A-Si(OR 1 ) x R 2 3-x   (IV).

3. The moisture-curing coating composition of claim 1 , wherein A is a propylene or methylene group.

4. The moisture-curing coating composition of claim 2 , wherein A is a propylene or methylene group.

5. The moisture-curing coating composition of claim 1 , which comprises at least 20 parts by weight of filler.

6. The moisture-curing coating composition of claim 1 , wherein at least one filler is selected from the group consisting of aluminum trihydroxide, calcium carbonate, barium sulfate, talc, mica, kaolin, silica, quartz, heavy spar, and carbon black.

7. The moisture-curing coating composition of claim 1 , wherein at least one curing catalyst is selected from the group consisting of organic titanium and tin compounds, aminosilanes, organic amines, and acidic compounds.

8. A method for sealing surfaces, comprising applying a coating composition of claim 1 to the surface to be sealed.

9. The method of claim 8 , wherein the coating composition applied to the surface to be sealed is cured at temperatures from 0 to 50° C.

10. The composition of claim 1 , which contains one or more aminosilanes and is free of metal-containing catalysts.

11. A moisture-curing coating composition comprising
A) 100 parts by weight of at least one condensation curable polymer consisting of silane-terminated polymer(s) terminated at each polymer terminus by end groups of the formula (I)
-A-Si(OR 1 ) x R 2 3-x   (I),

B) 30 to 200 parts by weight of at least one reactive plasticizer of the formula (V),
R 3 —Si(OR 1 ) y R 2 3-x   (V),

C) 0 to 400 parts by weight of filler, and
D) 0.01 to 20 parts by weight of curing catalyst,
where

A is a linear or branched alkylene group having 1 to 10 carbon atoms,
R 1 is a linear or branched, unsubstituted or halogen-substituted alkyl group having 1 to 10 carbon atoms,
R 2 is a linear or branched, unsubstituted or halogen-substituted alkyl group having 1 to 5 carbon atoms,
R 3 is an aryl group or a linear, branched or cyclic alkyl group or alkenyl group having 6 to 40 carbon atoms, in which individual hydrogen atoms may be substituted by organic radicals, and, if R 3 is a linear, branched or cyclic alkyl group or alkenyl group, the carbon chain may be interrupted by oxygen atoms, and
x and y are 1, 2 or 3, and
wherein the silane-terminated polymers are polyesters, polyethers, polyalkylenes, and/or polyacrylates.

12. The moisture-curing coating composition of claim 11 , wherein A is a propylene or methylene group.

13. A moisture-curing coating composition comprising
A) 100 parts by weight of at least one silane-terminated polymer having end groups of the formula (I)
-A-Si(OR 1 ) x R 2 3-x   (I),

B) 7 to 200 parts by weight of at least one reactive plasticizer of the formula (II),
R 3 —Si(OR 4 ) y R 5 3-y   (II),

C) 0 to 400 parts by weight of filler, and
D) 0.01 to 20 parts by weight of curing catalyst,
where

A is a linear or branched alkylene group having 1 to 10 carbon atoms,
R 1 and R 4 are each independently a linear or branched, unsubstituted or halogen-substituted alkyl group having 1 to 10 carbon atoms,
R 2 and R 5 are each independently a linear or branched, unsubstituted or halogen-substituted alkyl group having 1 to 5 carbon atoms,
R 3 is an aryl group or a linear, branched or cyclic alkyl group or alkenyl group having 6 to 40 carbon atoms, in which individual hydrogen atoms may be substituted by organic radicals, and, if R 3 is a linear, branched or cyclic alkyl group or alkenyl group, the carbon chain may be interrupted by oxygen atoms, and
x and y are 1, 2 or 3,
with the proviso that at least one reactive plasticizer (RW) is selected from the group consisting of decyltrimethoxysilane, decyltriethoxysilane, dodecyltrimethoxysilane, dodecyltriethoxysilane, tetradecyltrimethoxysilane, tetradecyltriethoxysilane, hexadecyltrimethoxsilane, hexadecyltriethoxysilane, and silanes having C 16 alkyl groups,

wherein the polymer(s) comprise end groups of the formula (IV)
˜O—C(═O)—NH-A-Si(OR 1 ) x R 2 3-x   (IV).

14. The moisture-curing coating composition of claim 13 , wherein A is a propylene or methylene group.

15. A moisture-curing coating composition, comprising
A) 100 parts by weight of at least one silane-terminated polymer having end groups of the formula (I)
-A-Si(OR 1 ) x R 2 3-x   (I),

B) 30 to 200 parts by weight of at least one reactive plasticizer of the formula (II),
R 3 —Si(OR 4 ) y R 5 3-y   (II),

C) 0 to 400 parts by weight of filler, and
D) 0.01 to 20 parts by weight of curing catalyst,
where

A is a linear or branched alkylene group having 1 to 10 carbon atoms,
R 1 and R 4 are each independently a linear or branched, unsubstituted or halogen-substituted alkyl group having 1 to 10 carbon atoms,
R 2 and R 5 are each independently a linear or branched, unsubstituted or halogen-substituted alkyl group having 1 to 5 carbon atoms,
R 3 is an aryl group or a linear, branched or cyclic alkyl group or alkenyl group having 6 to 40 carbon atoms, in which individual hydrogen atoms may be substituted by organic radicals, and, if R 3 is a linear, branched or cyclic alkyl group or alkenyl group, the carbon chain may be interrupted by oxygen atoms, and
x and y are 1, 2 or 3, and
wherein the silane-terminated polymers are polyesters, polyethers, polyalkylenes, and/or polyacrylates,
wherein the reactive plasticizer of formula (II) is present in an amount of at least 15% by weight relative to the total weight of the coating composition, and wherein the coating composition further comprises at least one tetraalkylsilicate of the formula
Si(OR 6 ) 4

where R 6 is a linear or branched, optionally halogenated alkyl group having 1-10 carbon atoms, or a partial hydrolysate thereof, or mixture thereof.

16. The coating composition of claim 15 , wherein the tetraalkylsilicate, partial hydrolysate thereof, or mixture thereof is present in an amount of 0.01 to 20 weight percent based on the weight of the coating

Assignees

• Stanjek Volker
• Bachmeier Bernd-Josef
• Bauer Andreas
• Wacker Chemie Ag

Inventors

• Stanjek Volker
• Bachmeier Bernd-Josef
• Bauer Andreas

Classifications

• C08G65/336

  containing silicon · CPC title

• C08J2300/108

  containing hydrolysable silane groups · CPC title

• C09D183/04 Primary

  Polysiloxanes · CPC title

• C09D201/10

  containing hydrolysable silane groups · CPC title

• C09D171/02 Primary

  Polyalkylene oxides · CPC title