Synthesis of nanosized metal carbides on graphitized carbon as supporting materials for electrocatalysts

Patent metadata

Field	Value
Publication number	US-9295979-B2
Application number	US-201114002408-A
Country	US
Kind code	B2
Filing date	Mar 1, 2011
Priority date	Mar 1, 2011
Publication date	Mar 29, 2016
Grant date	Mar 29, 2016

Abstract

Particles of a macro-porous ion exchange resin are dispersed in a solution of a transition metal compound, such as a compound of molybdenum, tungsten, or vanadium. The resin may be composed for anion exchange or cation ion exchange and, correspondingly, anions or cations of the metal are exchanged onto active ion exchange sites on the molecular chains of the resin. The resin is then carbonized and graphitized to form nanometer-size particles of transition metal carbide on particles of graphite. The composite metal carbide and graphite particles are electrically conductive and serve well as support particles for later deposited particles of a platinum group metal or other catalyst material in, for example, a catalytic electrode member in an electrochemical cell.

First claim

The invention claimed is:

1. A method of forming particles of a transition metal carbide compound on larger particles of graphite; the method comprising:
dispersing particles of a carbon-based macro-porous anion exchange resin in a volume of an aqueous solution of a transition metal compound to exchange anions of the transition metal from the solution onto active ion exchange sites on molecular chains of particles of an anion exchange resin to obtain a transition metal content in and on the particles of the anion exchange resin, the anion exchange resin having anions at the active ion exchange sites on the molecular chains of the resin which are exchangeable with anions of the transition metal from the solution;
dispersing particles of the transition metal-containing resin particles in a volume of an aqueous solution of a compound of a metal, for catalyzing carbonization of the resin particles, to deposit anions of the catalyst metal into the resin particles;
heating the transition metal containing and catalyst metal-containing resin particles to initiate carbonization of the resin particles;
further heating the particles to a higher temperature to complete carbonization and graphitization of the initial resin material and to form particles of transition metal carbide compound on larger formed particles of graphite; and
removing catalyst metal material from the graphite to leave a composite material consisting essentially of particles of transition metal carbide compound on larger graphite particles, the metal carbide particles having maximum average dimensions up to about fifteen nanometers.

2. A method as recited in claim 1 in which the transition metal is one or more selected from the group consisting of molybdenum, tungsten, and vanadium.

3. A method as recited in claim 1 in which the anion exchange resin is an acrylic acid anion exchange resin or a styrene anion exchange resin.

4. A method as recited in claim 1 in which the anion exchange resin is an acrylic acid anion exchange resin or a styrene anion exchange resin, and the resin is treated with an aqueous solution of sodium hypochlorite to provide suitable exchangeable ions at the active exchange sites on the molecular chains of the resin before ions of a transition metal are exchanged onto the active exchange sites of the resin.

5. A method as recited in claim 1 in which particles of a platinum group metal are subsequently deposited on the particles of transition metal carbide and graphite composite material.

6. A method of forming particles of a transition metal carbide compound on larger particles of graphite; the method comprising:
dispersing particles of a carbon-based macro-porous anion exchange resin in a volume of an aqueous solution of anions of a transition metal compound to deposit anions of the transition metal onto active anion exchange sites of the resin particles, the transition metal being selected from the group consisting of molybdenum and vanadium, the macro-porous anion resin having ions at the active ion exchange sites on the molecular chains of the anion exchange resin which are exchangeable with the anions of the transition metal from the aqueous solution;
dispersing particles of the transition metal-containing resin particles in a volume of an aqueous solution of anions of a metal, for catalyzing carbonization of the resin particles, to deposit anions of the catalyst metal into the resin particles;
heating the transition metal containing and catalyst metal-containing resin particles to a temperature up to about 350° C. to initiate carbonization of the resin particles;
further heating the particles to a temperature up to about 1000° C. to complete carbonization and graphitization of the initial resin material and to form particles of transition metal carbide compound on larger formed particles of graphite; and
removing catalyst metal material from the graphite to leave a composite material consisting essentially of particles of transition metal carbide compound on larger graphite particles, the metal carbide particles having maximum dimensions up to about fifteen nanometers.

7. A method as recited in claim 6 in which the anion exchange resin is an acrylic acid anion exchange resin or a styrene anion exchange resin.

8. A method as recited in claim 6 in which the anion exchange resin is an acrylic acid anion exchange resin or a styrene anion exchange resin and the resin is treated in sodium hypochlorite solution before ions of a transition metal are deposited into pores of particles of the resin.

9. A method as recited in claim 6 in which particles of a platinum group metal are subsequently deposited on the particles of transition metal carbide and graphite composite material.

Assignees

• Cai Mei
• Shen Peikang
• He Guoqiang
• Yan Zaoxue
• Meng Hui
• He Chunyong
• Gm Global Tech Operations Inc
• Univ Sun Yat Sen

Inventors

• Cai Mei
• Shen Peikang
• He Guoqiang
• Yan Zaoxue
• Meng Hui
• He Chunyong

Classifications

• C01B32/21

  After-treatment · CPC title

• C01B32/205

  Preparation · CPC title

• B01J27/22 Primary

  Carbides · CPC title

• B01J37/084

  Decomposition of carbon-containing compounds into carbon · CPC title

• H01M4/926

  on carbon or graphite · CPC title