High purity ferritic stainless steel sheet excellent in corrosion resistance and anti-glare property

Patent metadata

Field	Value
Publication number	US-9289964-B2
Application number	US-201214001920-A
Country	US
Kind code	B2
Filing date	Mar 5, 2012
Priority date	Mar 14, 2011
Publication date	Mar 22, 2016
Grant date	Mar 22, 2016

Abstract

An alloy-saving type high purity ferritic stainless steel sheet, comprising a steel sheet which contains, by mass %, C: 0.001 to 0.03%, Si: 0.01 to 1%, Mn: 0.01 to 1.5%, P: 0.005 to 0.05%, S: 0.0001 to 0.01%, Cr: 13 to 30%, N: 0.001 to 0.03%, Al: 0.005 to 1%, and Sn: 0.01 to 1% and has a balance of Fe and unavoidable impurities and which has a surface film, the surface film containing one or both of Al and Si in a total of 5 to 50 at % and Sn, an average concentration of Cr in the surface film being 1.1 to 3 times the concentration of Cr inside the steel sheet, and the surface film having a surface roughness of an arithmetic average roughness Ra of 0.1 to 1.5 μm.

First claim

The invention claimed is:

1. A high purity ferritic stainless steel sheet excellent in corrosion resistance and anti-glare property, which comprises a steel sheet which contains, by mass %,
C: 0.001 to 0.03%,
Si: 0.01 to 1%,
Mn: 0.01 to 1.5%,
P: 0.005 to 0.05%,
S: 0.0001 to 0.01%,
Cr: 13 to 30%,
N: 0.001 to 0.03%,
Al: 0.005 to 1%, and
Sn: 0.06 to 0.48%, and
has a balance of Fe and unavoidable impurities, and which further comprises a surface film,
said surface film containing, by ratio of only cations which make up said surface film other than C, O, and N, one or both of Al and Si in a total of 5 to 50 at %, and 1 to 10 at % Sn, and an average concentration of Cr in said surface film being, by ratio of only cations which make up said surface film other than C, O, and N, 1.1 to 3 times the concentration of Cr inside said steel sheet, and
said surface film having a surface roughness of an arithmetic average roughness Ra of 0.3 to 1.2 μm.

2. The high purity ferritic stainless steel sheet excellent in corrosion resistance and anti-glare property as set forth in claim 1 wherein said steel sheet further contains, by mass %, one or more of types of elements selected from
Nb: 0.03 to 0.5%,
Ti: 0.03 to 0.5%,
Ni: 0.1 to 0.5%,
Cu: 0.1 to 0.5%,
Mo: 0.1 to 0.5%,
V: 0.01 to 0.5%,
Zr: 0.01 to 0.5%,
Co: 0.01 to 0.5%,
Mg: 0.0001 to 0.005%,
B: 0.0003 to 0.005%, and
Ca: 0.005% or less, and
said surface film further contains, by ratio of only cations which make up said surface film other than C, O, and N, one or more types of Al, Si, Nb, and Ti in a total of 5 to 50 at %.

3. The high purity ferritic stainless steel sheet excellent in corrosion resistance and anti-glare property as set forth in claim 1 wherein said steel sheet further contains, by mass %, one or more types of elements selected from:
La: 0.001 to 0.1%,
Y: 0.001 to 0.1%,
Hf: 0.001 to 0.1%, and
REM: 0.001 to 0.1%.

4. The high purity ferritic stainless steel sheet excellent in corrosion resistance and anti-glare property as set forth in claim 2 wherein said steel sheet further contains, by mass %, one or more types of elements selected from:
La: 0.001 to 0.1%,
Y: 0.001 to 0.1%,
Hf: 0.001 to 0.1%, and
REM: 0.001 to 0.1%.

Assignees

• Hatano Masaharu
• Matsuyama Hiroyuki
• Yamagishi Akihito
• Hansaki Naoto
• Ishimaru Eiichiro
• Nippon Steel & Sumikin Sst

Inventors

• Hatano Masaharu
• Matsuyama Hiroyuki
• Yamagishi Akihito
• Hansaki Naoto
• Ishimaru Eiichiro

Classifications

• C22C38/06

  containing aluminium · CPC title

• C22C38/001 Primary

  containing N · CPC title

• C22C38/18

  containing chromium · CPC title

• C21D8/0268

  between cold rolling steps · CPC title

• C21D2211/005

  Ferrite · CPC title