Polycondensation catalyst for producing polyester and production of polyester using the polycondensation catalyst

Patent metadata

Field	Value
Publication number	US-9289749-B2
Application number	US-201313955529-A
Country	US
Kind code	B2
Filing date	Jul 31, 2013
Priority date	Jul 31, 2012
Publication date	Mar 22, 2016
Grant date	Mar 22, 2016

Abstract

The invention provides a polycondensation catalyst for producing polyester by an esterification reaction or a transesterification reaction between a dicarboxylic acid or an ester-forming derivative thereof and a glycol, wherein the polycondensation catalyst comprises particles of a solid base having on the surfaces an inner coating layer of titanic acid in an amount of from 0.1 to 50 parts by weight in terms of TiO 2 per 100 parts by weight of the solid base, and an outer coating layer either of an oxide of at least one element selected from aluminum, zirconium and silicon, or of a composite oxide of at least two elements selected from aluminum, zirconium and silicon on the surface of the inner coating layer in an amount of from 1 to 50 parts by weight per 100 parts by weight of the solid base.

First claim

The invention claimed is:

1. A polycondensation catalyst for producing polyester by an esterification reaction or a transesterification reaction between a dicarboxylic acid or an ester-forming derivative thereof and a glycol, wherein the polycondensation catalyst comprises particles of a solid base having on the surfaces an inner coating layer of titanic acid in an amount of from 0.1 to 50 parts by weight in terms of TiO 2 per 100 parts by weight of the solid base, and an outer coating layer either of an oxide of at least one element selected from aluminum, zirconium and silicon, or of a composite oxide of at least two elements selected from aluminum, zirconium and silicon on the surface of the inner coating layer in an amount of from 1 to 50 parts by weight per 100 parts by weight of the solid base.

2. The polycondensation catalyst according to claim 1 , wherein the solid base is magnesium hydroxide.

3. The polycondensation catalyst according to claim 1 , wherein the solid base is hydrotalcite.

4. A method for producing polyester comprising preparing an oligomer comprising a bis(hydroxyalkyl) ester of an aromatic dicarboxylic acid by an esterification reaction or a transesterification reaction between the aromatic dicarboxylic acid or an ester-forming derivative thereof and an alkylene glycol, and then subjecting the oligomer to melt-polycondensation in the presence of the polycondensation catalyst according to claim 1 .

5. A method for producing polyester comprising subjecting a dicarboxylic acid or an ester-forming derivative thereof and a glycol to melt-polycondensation in the presence of the polycondensation catalyst according to claim 1 .

6. The method for producing polyester according to claim 5 , wherein the resulting polyester is further subjected to solid-polycondensation.

7. A method for producing a polycondensation catalyst for producing polyester by an esterification reaction or a transesterification reaction between a dicarboxylic acid or an ester-forming derivative thereof and a glycol, the polycondensation catalyst comprising particles of a solid base having on the surfaces an inner coating layer and an outer coating layer, wherein the method comprises:
adding an aqueous solution of a titanium compound and an aqueous solution of an alkali to an aqueous slurry of particles of a solid base so that the aqueous slurry has a pH in a range of 5 to 12 thereby to form an inner coating layer of titanic acid on the surfaces of the particles of the solid base;
adding an aqueous solution of at least one selected from a water-soluble aluminum salt and a water-soluble zirconium salt and an aqueous solution of an alkali to the resulting aqueous slurry of the particles of the solid base thereby to form an outer coating layer of an oxide of at least one element selected from aluminum and zirconium, or of a composite oxide of aluminum and zirconium on the surface of the inner coating layer; and
filtering the aqueous slurry of the particles of the solid base having the inner coating layer and the outer coating layer thereon, washing with water and drying the obtained cake, followed by disintegrating the obtained dried product.

8. A method for producing a polycondensation catalyst for producing polyester by an esterification reaction or a transesterification reaction between a dicarboxylic acid or an ester-forming derivative thereof and a glycol, the polycondensation catalyst comprising particles of a solid base having on the surfaces an inner coating layer and an outer coating layer, wherein the method comprises:
adding an aqueous solution of a titanium compound and an aqueous solution of an alkali to an aqueous slurry of particles of a solid base so that the aqueous slurry has a pH in a range of 5 to 12 thereby to form an inner coating layer of titanic acid on the surfaces of the particles of the solid base;
adding an aqueous solution of a water-soluble silicate and an acid to the resulting aqueous slurry of the particles of the solid base thereby to form an outer coating layer of an oxide of silicon on the surface of the inner coating layer; and
filtering the aqueous slurry of the particles of the solid base having the inner coating layer and the outer coating layer thereon, washing with water and drying the obtained cake, followed by disintegrating the obtained dried product.

9. A method for producing a polycondensation catalyst for producing polyester by an esterification reaction or a transesterification reaction between a dicarboxylic acid or an ester-forming derivative thereof and a glycol, the polycondensation catalyst comprising particles of a solid base having on the surfaces an inner coating layer and an outer coating layer, wherein the method comprises:
adding an aqueous solution of a titanium compound and an aqueous solution of an alkali to an aqueous slurry of particles of a solid base so that the aqueous slurry has a pH in a range of 5 to 12 thereby to form an inner coating layer of titanic acid on the surfaces of the particles of the solid base;
adding an aqueous solution of at least one selected from a water-soluble aluminum salt and a water-soluble zirconium salt, and an aqueous solution of a water-soluble silicate to the resulting aqueous slurry of the particles of the solid base thereby to form an outer coating layer of a composite oxide of at least one element selected from aluminum and zirconium, and silicon on the surface of the inner coating layer; and
filtering the aqueous slurry of the particles of the solid base having the inner coating layer and the outer coating layer thereon, washing with water and drying the obtained cake, followed by disintegrating the obtained dried product.

Assignees

• Sakai Chemical Industry Co

Inventors

• Tabata Keiichi
• Kamon Akihiro
• Ikegawa Keiichi
• Naito Jun

Classifications

• C08G63/84

  Boron, aluminium, gallium, indium, thallium, rare-earth metals, or compounds thereof {(C08G63/823 takes precedence)} · CPC title

• C08G63/85 Primary

  Germanium, tin, lead, arsenic, antimony, bismuth, titanium, zirconium, hafnium, vanadium, niobium, tantalum, or compounds thereof {(C08G63/823 takes precedence)} · CPC title

• B01J21/063 Primary

  Titanium; Oxides or hydroxides thereof · CPC title

• B01J21/10

  Magnesium; Oxides or hydroxides thereof · CPC title

• B01J21/066

  Zirconium or hafnium; Oxides or hydroxides thereof · CPC title