Method of preparing a transparent polumer material comprising a thermoplastic polycarbonate and mineral nanoparticles

Patent metadata

Field	Value
Publication number	US-9284422-B2
Application number	US-74601108-A
Country	US
Kind code	B2
Filing date	Dec 9, 2008
Priority date	Dec 13, 2007
Publication date	Mar 15, 2016
Grant date	Mar 15, 2016

Abstract

A method of preparing a transparent polymer material includes mixing mineral nanoparticles selected from nanoparticles of alkaline-earth metal carbonates, alkaline-earth metal sulfates, metallic oxides, oxides of metalloids, and siloxanes, and a composition A including at least one thermoplastic polymer in the molten state selected from polycarbonate (PC), polystyrene (PS) and polymethyl methacrylate (PMMA) in order to obtain a master-batch, the mixture of step i) including at least 25% and at most 75% by weight of the mineral nanoparticles. The master-batch obtained in step i) is mixed with a composition B of a thermoplastic polycarbonate matrix (PCm) in the molten state, to obtain a transparent polymer material including at most 10% by weight of the mineral nanoparticles, preferably at most 5% by weight of the mineral nanoparticles.

First claim

The invention claimed is:

1. A method of preparing a transparent polymer material, the method comprising the following steps:
i) mixing mineral nanoparticles selected from the group consisting of nanoparticles of alkaline-earth metal carbonates and alkaline-earth metal sulfates and a composition A including at least one thermoplastic polymer in the molten state selected from the group consisting of polycarbonate (PC), polystyrene (PS) and polymethyl methacrylate (PMMA) in order to obtain a master-batch, the mixture of step i) including at least 25% and at most 75% by weight of said mineral nanoparticles; and
ii) mixing the master-batch obtained in step i) with a composition B comprising a transparent thermoplastic polycarbonate matrix (PCm) in the molten state, to obtain the transparent polymer material including at most 10% by weight of said mineral nanoparticles, wherein said addition of said master batch including said nanoparticles is added in an amount, concentration and manner to said transparent thermoplastic polycarbonate matrix (PCm) such that it results in said transparent thermoplastic polycarbonate matrix having no more than a 25% reduction in light transmission percentage relative to a reference material of a transparent thermoplastic polycarbonate matrix (PCm) having no master batch included, such that there is no significant loss of contrast to an object viewed therethrough
wherein said polymer material has a light transmission loss at 650 nm, compared with a reference material obtained solely from the thermoplastic polycarbonate matrix (PCm), of at most 25%, and
wherein said polymer material has a molecular weight loss, compared with a reference material obtained solely from the transparent thermoplastic polycarbonate matrix (PCm), of at most 30%.

2. The method according to claim 1 , wherein the mixture of step i) includes at least 40% and at most 60% by weight of said mineral nanoparticles.

3. The method according to claim 1 , wherein the dimension of the mineral nanoparticles is at most 300 nm.

4. The method according to claim 1 , wherein the mineral nanoparticles are selected from nanoparticles of calcium carbonate, and barium sulfate.

5. The method according to claim 1 , wherein the mixture of step ii) further includes at least one antioxidant.

6. The method according to claim 5 , wherein the composition B is prepared prior to step ii) by mixing an antioxidant with transparent thermoplastic polycarbonate matrix (PCm) in the molten state.

7. The method according to claim 6 , wherein the composition B includes at most 5% by weight of antioxidant.

8. The method according to claim 5 , wherein the composition A is prepared prior to step i) by mixing an antioxidant with the thermoplastic polymer in the molten state.

9. The method according to claim 8 , wherein composition A includes at most 15% by weight of antioxidant.

10. The method according to claim 5 , wherein said antioxidant is added directly to the mixture of step ii) and/or to the mixture of step i).

11. The method according to claim 5 , wherein the mixture of step ii) includes at most 5% by weight of antioxidant.

12. The method according to claim 5 , wherein the antioxidant includes a phosphite.

13. The method according to claim 1 , wherein the mixture of step ii) further includes a compatibilizing agent when the mixture of step i) comprises polystyrene (PS) and/or polymethyl methacrylate (PMMA).

14. The method according to claim 13 , wherein the compatibilizing agent is a natural montmorillonite surface-modified with hydroxyl functional groups.

15. The method according to claim 13 , wherein the compatibilizing agent is a copolymer of polystyrene and maleic anhydride.

16. The method according to claim 13 , wherein the mixture of step ii) includes at most 5% by weight of compatibilizing agent.

17. A transparent polymer material obtained by the method defined in claim 1 .

18. The polymer material according to claim 17 , wherein said polymer material has a bending modulus increase, compared with a reference material obtained solely from the transparent thermoplastic polycarbonate matrix (PCm), of at least 10%.

19. A method for manufacturing optical articles of aiming instrumentation lenses, helmet visores, or ophthalmic lenses, said method comprising the step of:
forming said optical articles with the polymer material according to claim 17 .

20. A method for manufacturing optical articles of the automobile glass, said method comprising the step of:
forming said optical articles with the polymer material according to claim 17 .

21. A method for manufacturing optical articles with a thickness of at most 15 mm, said method comprising the step of:
forming said optical articles with the transparent polymer material according to claim 17 .

22. The method of claim 1 , wherein said transparent polymer material includes at most 5% by weight of said mineral nanoparticles.

23. The method according to claim 3 , wherein the dimension of the mineral nanoparticles is at most 100 nm.

24. The method according to claim 3 , wherein the dimension of the mineral nanoparticles is in the range 10 nm to 70 nm.

25. The method according to claim 7 , wherein the composition B is in the range 0.5% to 2% by weight of antioxidant.

26. The method according to claim 9 , wherein the composition A is in the range 2% to 12% by weight of antioxidant.

27. The method according to claim 9 , wherein the composition A is 10% by weight of antioxidant.

28. The method according to claim 11 , wherein the mixture of step ii) is in the range 1% to 2% by weight of antioxidant.

29. The method according to claim 16 , wherein the mixture of step ii) includes in the range 0.1% to 2% by weight of compatibilizing agent.

30. The method according to claim 16 , wherein the mixture of step ii) includes in the range 0.3% to 1% by weight of compatibilizing agent.

31. The polymer material according to claim 17 , wherein said polymer material has a light transmission loss at 650 nm, compared with a reference material obtained solely from the transparent thermoplastic polycarbonate matrix (PCm), of at most 10.

32. The polymer material according to claim 17 , wherein said polymer material has a light transmission loss at 650 nm, compared with a reference material obtained solely from the transparent thermoplastic polycarbonate matrix (PCm), of at most 1% to 3%.

33. The polymer material according to claim 18 wherein said polymer material has a bending modulus increase, compared with a reference material obtained solely from the transparent thermoplastic polycarbonate matrix (PCm), in the range 20% to 60%.

34. The polymer material according to claim 17 , wherein said polymer material has a molecular weight loss, compared with a reference material obtained solely from the transparent thermoplastic polycarbonate matrix (PCm), of at most 20%.

35. The polymer material according to claim 17 , wherein said polymer material has a molecular weight loss, compared with a reference material obtained solely from the transparent thermoplastic polycarbonate matrix (PCm), of at most 10%.

36. A method for manufacturing optical articles with a thickness in the range 0.1 mm to 5 mm, said method comprising t

Assignees

• Boucher Virginie
• Roos Alexandra
• Duquesne Sophie
• Bourbigot Serge
• Meynie Laure
• Cavalier Karine
• Sy Didier
• Lacroix Marc
• Essilor Int
• Renault S A S ; Solvay Sa

Inventors

• Boucher Virginie
• Roos Alexandra
• Duquesne Sophie
• Bourbigot Serge
• Meynie Laure
• Cavalier Karine
• Sy Didier
• Lacroix Marc

Classifications

• C08L2666/02

  Organic macromolecular compounds, natural resins, waxes or and bituminous materials · CPC title

• C08L33/12

  Homopolymers or copolymers of methyl methacrylate · CPC title

• C08L25/04

  Homopolymers or copolymers of styrene · CPC title

• C08J5/005

  Reinforced macromolecular compounds with nanosized materials, e.g. nanoparticles, nanofibres, nanotubes, nanowires, nanorods or nanolayered materials · CPC title

• C08J2425/00

  Characterised by the use of homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by an aromatic carbocyclic ring; Derivatives of such polymers · CPC title