Method of forming a film made of a fluoropolymer of the polyvinylidene fluoride type that can be used as a separator for a lithium battery

Patent metadata

Field	Value
Publication number	US-9276245-B2
Application number	US-201113638405-A
Country	US
Kind code	B2
Filing date	Mar 22, 2011
Priority date	Apr 1, 2010
Publication date	Mar 1, 2016
Grant date	Mar 1, 2016

Abstract

A film made of a fluorinated polymer of the polyvinylidene fluoride type having suitable properties for use as a lithium storage battery separator is produced using a phase inversion technique in which a solution containing the fluorinated polymer is brought into the presence of an atmosphere laden with water vapor to precipitate the fluorinated polymer. The fluorinated polymer can be precipitated by placing the support on which the solution is deposited, in which the fluorinated polymer has been previously dissolved, in an enclosure containing an atmosphere laden with water vapor and thermostatically regulated to a temperature comprised between 30° C. and 70° C. The relative humidity content during precipitation of the fluorinated polymer is advantageously between about 60% and about 98%.

First claim

The invention claimed is:

1. A method of forming a separator for a lithium storage battery, the separator comprising a fluorinated polymer film of polyvinylidene fluoride, the method consisting of the following steps:
depositing on a support a solution containing a solvent in which a fluorinated polymer is dissolved; and
precipitating the fluorinated polymer by phase inversion with water by placing said solution in the presence of an atmosphere laden with water vapor,
thereby forming the separator comprising the fluorinated polymer film of polyvinylidene fluoride,
wherein:
the method does not comprise an immersion step in a liquid non-solvent; and
the mass proportion of fluorinated polymer in the solution is from 11% to 20%.

2. The method according to claim 1 , wherein the precipitating step of the fluorinated polymer is performed at a temperature from 30° C. to 70° C.

3. The method according to claim 1 , wherein the solvent is selected from the group consisting of acetone, butanone, N-methylpyrrolidone, tetrahydrofuran, dimethylsulfoxide, cyclopentanone, γ-butyrolactone, and mixtures thereof.

4. The method according to claim 1 , wherein the mass proportion of fluorinated polymer in the solution is from 13% to 17%.

5. The method according to claim 1 , wherein the precipitating step of the fluorinated polymer is carried out by placing the support on which the solution is deposited in an enclosure containing an atmosphere laden with water vapor.

6. The method according to claim 5 , wherein the enclosure is thermostatically regulated at a temperature from 30° C. to 70° C. during precipitation of the fluorinated polymer.

7. The method according to claim 1 , wherein the relative humidity content during precipitation of the fluorinated polymer is from 60% to 98%.

8. The method according to claim 7 , wherein the relative humidity content during precipitation of the fluorinated polymer is from 85% to 98%.

9. The method according to claim 1 , wherein the precipitation step of the fluorinated polymer is followed by a step of vacuum drying at a temperature from 40° C. to 80° C.

10. The method according to claim 1 , wherein the duration of the precipitation step of the fluorinated polymer is from 1 minute to 60 minutes.

11. The method according to claim 1 , wherein the support comprises an electrode for a lithium storage battery.

12. The method according to claim 1 , wherein the solution is deposited on said support via a film applicator with an adjustable slot height.

13. The method according to claim 1 , wherein the deposition has a thickness comprised between 10 μm and 100 μm.

14. The method according to claim 1 , wherein the film has a rate of porosity from 35% to 95%.

15. The method according to claim 1 , wherein the film has pores having a mean size from 0.5 μm to 10 μm.

16. The method according to claim 15 , wherein the film presents pores having a mean size comprised between 0.5 μm and 4 μm.

17. A separator for a lithium storage battery formed by the method according to claim 1 .

Assignees

• Patoux Sébastien
• Alloin Fannie
• Daniel Lise
• Commissariat À L En Atomique Et Aux En Alternatives
• Centre Nat Rech Scient

Inventors

• Patoux Sébastien
• Alloin Fannie
• Daniel Lise

Classifications

• H01M10/052 Primary

  Li-accumulators · CPC title

• H01M50/426

  Fluorocarbon polymers · CPC title

• H01M50/491

  Porosity · CPC title

• Y02E60/10

  Energy storage using batteries · CPC title

• H01M2/145

  Electricity · mapped topic