Calcium carbonate based sulfonate grease compositions and method of manufacture

Patent metadata

Field	Value
Publication number	US-9273265-B2
Application number	US-201213664574-A
Country	US
Kind code	B2
Filing date	Oct 31, 2012
Priority date	Oct 31, 2011
Publication date	Mar 1, 2016
Grant date	Mar 1, 2016

Abstract

An overbased calcium sulfonate grease composition comprising a reduced amount of overbased calcium sulfonate, added calcium carbonate, base oil, one or more converting agents, and one or more complexing acids if a complex grease is desired. The calcium sulfonate grease composition improves thickener yield and expected high temperature utility as demonstrated by dropping point. The calcium carbonate may be used to react with complexing acids when making a complex grease, such that the addition of calcium oxide or calcium hydroxide is not required. A method of making the composition comprising the steps of mixing the overbased calcium sulfonate and base oil, adding the calcium carbonate, adding one or more converting agents, and adding one or more complexing acids. All or a portion of one or more of the complexing acids may be added with or prior to the one or more converting agents.

First claim

I claim:

1. A calcium sulfonate complex grease composition comprising the following ingredients:
around 10% to 36% overbased oil-soluble calcium sulfonate containing 28% to 36% dispersed calcium carbonate and 0% to 8% residual calcium oxide or calcium hydroxide;
2% to 20% crystalline calcium carbonate added in addition to the amount of dispersed calcium carbonate contained in the overbased oil-soluble calcium sulfonate;
wherein the calcium sulfonate complex grease has a worked 60 stroke penetration between 220 and 295 and a dropping point of 575 F or higher;
wherein the amount of dispersed calcium carbonate and residual calcium oxide or calcium hydroxide are by weight of the overbased oil-soluble calcium sulfonate and all other amounts are by weight of the final complex grease; and
wherein no calcium oxide or calcium hydroxide is added in addition to the amount of residual calcium oxide or calcium hydroxide contained in the overbased oil-soluble calcium sulfonate.

2. The calcium sulfonate complex grease composition according to claim 1 further comprising:
2% to 10% water;
one or more other converting agents in a total amount of 0.5% to 5%; and
one or more complexing acids in a total amount of 2.8% to 11%.

3. The calcium sulfonate complex grease composition according to claim 2 wherein the one or more other converting agents are selected from the group consisting of alcohols, ethers, glycols, glycol ethers, glycol polyethers, carboxylic acids, inorganic acids, organic nitrates, compounds that contain active hydrogen or compounds that contain tautomeric hydrogen; and
wherein the one or more complexing acids are selected from the group consisting of a long chain carboxylic acid, a short chain carboxylic acid, boric acid, and phosphoric acid.

4. The calcium sulfonate complex grease composition according to claim 3 further comprising 0.5% to 5% dodecylbenzene sulfonic acid.

5. The calcium sulfonate complex grease composition of claim 1 wherein the amount of overbased oil-soluble calcium sulfonate is around 10% to 32%.

6. The calcium sulfonate complex grease composition of claim 1 wherein the amount of overbased calcium sulfonate is around 10% to 32%.

7. The calcium sulfonate complex grease composition of claim 3 further comprising 0.5% to 5% facilitating acid.

8. A calcium sulfonate complex grease composition comprising the following ingredients:
oil-soluble overbased calcium sulfonate having 28% to 36% dispersed calcium carbonate and 0% to 8% residual calcium oxide or calcium hydroxide dispersed therein, such amounts by weight of the oil-soluble overbased calcium sulfonate;
crystalline calcium carbonate added in addition to the amount of dispersed calcium carbonate contained in the oil-soluble overbased calcium sulfonate;
one or more converting agents;
one or more complexing acids;
wherein no calcium oxide or calcium hydroxide is added in addition to any amount of residual calcium oxide or calcium hydroxide contained in the oil-soluble overbased calcium sulfonate.

9. The calcium sulfonate complex grease composition according to claim 8 wherein the grease has a worked 60 stroke penetration between 265 and 295 and a dropping point of 575 F or higher.

10. The calcium sulfonate complex grease composition according to claim 9 comprising around 10% to 45% oil-soluble overbased calcium sulfonate.

11. The calcium sulfonate grease composition according to claim 8 wherein the crystalline calcium carbonate is added in a stoichiometrically excess amount relative to the total amount of complexing acids.

12. A simple calcium sulfonate grease composition comprising the following ingredients:
around 10% to 45% overbased calcium sulfonate containing calcium carbonate dispersed therein, wherein the dispersed calcium carbonate is in an amorphous state when the overbased calcium sulfonate is first added to the other ingredients and is converted to a crystalline state in the final simple grease product;
2% to 20% crystalline calcium carbonate added in addition to the amount of amorphous calcium carbonate contained in the overbased calcium sulfonate;
wherein the simple grease has a worked penetration between 240 and 475; and
wherein the overbased calcium sulfonate contains 0% to 8% residual dispersed calcium oxide or calcium hydroxide and wherein no additional calcium oxide or calcium hydroxide is separately added.

13. The simple calcium sulfonate grease composition according to claim 12 further comprising:
0.5% to 5.0% C12 alkylbenzene sulfonic acid; and
one or more converting agents selected from the group consisting of alcohols, ethers, glycols, glycol ethers, glycol polyethers, carboxylic acids, inorganic acids, organic nitrates, compounds that contain active hydrogen or compounds that contain tautomeric hydrogen, in a total amount of 0.1% to 5.0%.

14. A method for making an overbased calcium sulfonate complex grease comprising the steps of:
providing 10 to 45 parts overbased calcium sulfonate having 28% to 36% amorphous calcium carbonate and 0% to 8% residual calcium oxide or calcium hydroxide dispersed therein;
providing 2 to 20 parts of crystalline calcium carbonate as a separately added ingredient in addition to the amount of amorphous calcium carbonate contained in the overbased calcium sulfate;
mixing the overbased calcium sulfonate with 30 to 60 parts of a base oil, the separately added crystalline calcium carbonate, 2 to 10 parts water, and 0.5 to 5 total parts of one or more other converting agents to form a pre-conversion mixture;
converting the pre-conversion mixture to a converted mixture by heating until conversion of the amorphous calcium carbonate contained in the overbased calcium sulfonate to a crystalline form has occurred; and
mixing 2.8 to 11 total parts of one or more complexing acids with the pre-conversion mixture, converted mixture, or both;
wherein no additional calcium oxide or calcium hydroxide is added in addition to any amount of residual calcium oxide or calcium hydroxide contained in the overbased calcium sulfonate and the separately added crystalline calcium carbonate is the sole calcium containing base added as a separate ingredient for reacting with the one or more complexing acids; and
wherein the amount of amorphous calcium carbonate and residual calcium oxide or calcium hydroxide is by weight of the overbased calcium sulfonate and all other amounts are by weight of the final complex grease product.

15. The method according to claim 14 further comprising the steps of:
mixing 0.5 to 5 parts of a facilitating acid prior to addition of the one or more converting agents; and
heating the mixture after addition of the one or more complexing acids to the converted mixture.

16. The method according to claim 14 wherein 15% to 45% of the total weight of a first complexing acid is added to the pre-conversion mixture prior to adding any converting agents with the other 85% to 55% of the total weight of such first complexing acid being added to the converted mixture.

17. The method according to claim 14 wherein the one or more complexing acids mixed with the pre-conversion mixture are different than the one or more complexing acids mixed with the converted mixture.

18. The method according to claim 14 wherein the pre-conversion mixture is mixed at ambient temperature for 5 to 20 minutes before applying heat.

19. The method according to claim 14 wherein 15% to 45% of the total weight of the one or more complexing acids is mixed with the pre-conversion mixture and 85% to 55% of the total

Assignees

• Waynick J Andrew
• Nch Corp

Inventors

• Waynick J Andrew

Classifications

• C10N2020/017

  Specific gravity or density · CPC title

• C10N2030/52

  Base number [TBN] · CPC title

• C10N2020/06

  Particles of special shape or size · CPC title

• C10N2030/06

  Oiliness; Film-strength; Anti-wear; Resistance to extreme pressure · CPC title

• C10N2040/04

  Oil-bath; Gear-boxes; Automatic transmissions; Traction drives · CPC title