Chloroprene rubber composition, and vulcanizates and moldings thereof

Patent metadata

Field	Value
Publication number	US-9260592-B2
Application number	US-201113884458-A
Country	US
Kind code	B2
Filing date	Sep 12, 2011
Priority date	Nov 12, 2010
Publication date	Feb 16, 2016
Grant date	Feb 16, 2016

Abstract

To provide a chloroprene rubber composition that provides excellent low temperature characteristics such as low temperature permanent compression set and dynamic characteristics at low temperature and provides good permanent compression set, mechanical strength, and processing characteristics also at high temperature thus to achieve excellent characteristics within a wide temperature region, and a vulcanizate and a molding thereof.
To a chloroprene rubber including a 2,3-dichlorobutadiene unit in an amount of 5 to 20% by mass, a natural rubber is added so as to give a ratio (chloroprene rubber/natural rubber) of 60/40 to 95/5 by mass ratio. Then, with respect to 100 parts by mass of the rubber components, ethylene thiourea is added in an amount of 0.1 to 3.0 parts by mass and dipentamethylenethiuram tetrasulfide is added in an amount of 0.1 to 3.0 parts by mass, thereby preparing the chloroprene rubber composition.

First claim

The invention claimed is:

1. A chloroprene rubber composition comprising rubber components consisting entirely of a chloroprene rubber and a natural rubber in an amount of 100 parts by mass;
ethylene thiourea in an amount of 0.1 to 3.0 parts by mass; and
dipentamethylenethiuram tetrasulfide in an amount of 0.1 to 3.0 parts by mass;
wherein the chloroprene rubber includes a 2,3-dichlorobutadiene unit in an amount of 5 to 20% by mass; and
the blending ratio of the chloroprene rubber and the natural rubber (chloroprene rubber/natural rubber) is 60/40 to 95/5 by mass ratio, said rubber components being free of sulfur used as a vulcanization agent.

2. A vulcanizate obtained by vulcanization of the chloroprene rubber composition according to claim 1 .

3. A molding obtained by vulcanization of the chloroprene rubber composition according to claim 1 after or during molding of the composition.

4. The chloroprene rubber composition according to claim 1 , wherein the chloroprene rubber is a copolymer of 2-chloro-1,3-butadiene and 2,3-dichlorobutadiene.

5. A chloroprene rubber composition consisting essentially of a chloroprene rubber and a natural rubber in a total amount of 100 parts by mass;
ethylene thiourea in an amount of 0.1 to 3.0 parts by mass;
dipentamethylenethiuram tetrasulfide in an amount of 0.1 to 3.0 parts by mass;
the chloroprene rubber contains a 2,3-dichlorobutadiene unit in an amount of 5 to 20% by mass; and
a blending ratio of the chloroprene rubber and the natural rubber (chloroprene rubber/natural rubber) is 60/40 to 95/5 by mass ratio, said composition being free of sulfur used as a vulcanization agent.

6. A vulcanizate obtained by vulcanization of the chloroprene rubber composition according to claim 5 .

7. The vulcanizate according to claim 6 including at least one additive selected from the group consisting of a softener, a filler, a reinforcement, a plasticizer, a process aid, a lubricant, an antioxidant agent, a stabilizer and a silane coupling agent.

8. A molding obtained by vulcanization of the chloroprene rubber composition according to claim 5 after or during molding of the composition.

9. A chloroprene rubber composition according to claim 5 , wherein the chloroprene rubber is a copolymer of 2-chloro-1,3-butadiene and 2,3-dichlorobutadiene.

10. The vulcanizate according to claim 2 including at least one additive selected from the group consisting of a softener, a filler, a plasticizer, a process aid, a lubricant, an antioxidant, a stabilizer and a silane coupling agent.

11. The chloroprene rubber composition according to claim 1 , wherein the chloroprene rubber contains the 2,3-dichlorobutadiene unit in an amount of 7% to 20% by mass.

12. The chloroprene rubber composition according to claim 5 , wherein the chloroprene rubber contains the 2,3-dichlorobutadiene unit in an amount of 7% to 20% by mass.

Assignees

• Yamagishi Uichiro
• Denka Company Ltd

Inventors

• Yamagishi Uichiro

Classifications

• C08L11/00 Primary

  Compositions of homopolymers or copolymers of chloroprene · CPC title

• C08L7/00 Primary

  Compositions of natural rubber · CPC title

• C08L9/00 Primary

  Compositions of homopolymers or copolymers of conjugated diene hydrocarbons · CPC title

• C08K5/405

  Thioureas; Derivatives thereof · CPC title

• C08K5/40

  Thiurams, {i.e. compounds containing[IMAGE cpc-sch-C08K-1011.gif] groups} · CPC title