Abstract

A method for manufacturing a titanium acetabular cup shell includes obtaining a titanium powder. A three part mold having a first part with a part-spherical inner surface, a second ram part with a part-spherical outer impact surface and a third ram part with an annular impact surface are provided to compact the titanium powder. The second and third parts are aligned along an axis within the first part. The second part is aligned along a center axis within the annular impact surface of the third part. The first mold part is filled with the titanium powder. The second mold part-spherical outer surface and the third part annular surface are moved towards the part-spherical inner surface of the first part into contact with the powder. The powder is compacted with the second part part-spherical outer impact surface and the third part annular impact surface to about 50% of its initial volume.

First claim

The invention claimed is:

1. A method for manufacturing a titanium acetabular cup shell comprising:
obtaining a titanium sponge powder;
providing a three part mold having a first part with a part-spherical inner surface, a second part comprising a first ram with a part-spherical outer impact surface and a third part comprising a second ram with an annular impact surface, the second and third parts aligned along an axis within the first part and the second part aligned along the axis within the third part and surrounded by the annular impact surface thereof;
filling the first part with the titanium sponge powder;
moving the second mold part-spherical outer surface and the third part annular surface towards the part-spherical inner surface of the first part into contact with the powder; and
compacting the powder with the second part part-spherical outer impact surface and the third part annular impact surface.

2. The method as set forth in claim 1 wherein the second and third mold parts contact the powder simultaneously.

3. The method as set forth in claim 2 wherein the third mold part moves at a greater velocity relative to the first mold part than the second mold part.

4. The method as set forth in claim 1 wherein the second mold part contacts the powder prior to the third mold part contacting the powder.

5. The method of claim 4 wherein the second mold part remains in contact with the powder until after the third mold part contacts the powder.

6. The method as set forth in claim 1 wherein the powder is compacted to about 50% of its original volume by the mold parts.

7. The method as set forth in claim 6 wherein the third mold part moves three times as far relative to the first mold part after initially contacting the powder compared to the second mold part.

8. The method as set forth in claim 1 wherein a central axis of the annular impact surface is coaxial with an axis through a center and a pole of the first and second mold part part-spherical surfaces.

9. The method as set forth in claim 8 wherein the mold parts move with respect to each other in a direction parallel to the axis.

10. The method as set forth in claim 8 wherein the cylindrical impact surface of the third mold moves three times further with respect to the first part compared to the movement of the second part with respect to the first part.

11. The method as set forth in claim 1 wherein the second and third mold parts impact surface produce a pressure of 30 to 50 tons per square inch.

12. A method for manufacturing a titanium acetabular cup outer shell comprising:
providing titanium sponge powder having an average size less than 20 mesh;
providing a mold having three parts aligned along an axis, the mold having a first part comprising a part-spherical inner surface, a second part comprising a part-spherical outer impact surface and a third part having an annular impact surface, the second part and third part moveable with respect to the first part part-spherical inner surface;
the axis forming a central axis of the first and second part spherical surfaces and the third part impact surface, the third mold part annular impact surface formed by concentric inner and outer cylindrical surfaces, the diameter of the inner cylindrical surface of the third part greater than a maximum diameter of the part-spherical outer surface of the second part and the outer cylindrical surface diameter of the third mold part being less than a maximum diameter of the part-spherical inner surface of the first mold part wherein the second mold part is slidably nested within the third mold part and the third part is nested in the first mold part; and
filling the first mold part with powder and compacting the powder with the second and third parts to form a part-spherical shell.

13. The method as set forth in claim 12 wherein the second and third mold parts contact the powder simultaneously.

14. The method as set forth in claim 13 wherein the third mold part moves at a greater velocity relative to the first mold part than the second mold part.

15. The method as set forth in claim 12 wherein the second mold part contacts the powder prior to the third mold part contacting the powder.

16. The method of claim 15 wherein the second mold part remains in contact with the powder until after the third mold part contacts the powder.

17. The method as set forth in claim 12 wherein the powder is compacted to about 50% of its original volume by the mold parts.

18. The method as set forth in claim 17 wherein the third mold part moves three times as far relative to the first mold part after initially contacting the powder compared to the second mold part.

19. The method as set forth in claim 12 wherein a central axis of the annular impact surface is coaxial with an axis through a center and a pole of the first and second mold part part-spherical surfaces.

20. The method as set forth in claim 19 wherein the cylindrical impact surface of the third mold moves three times further with respect to the first part compared to the movement of the second part with respect to the first part.

21. The method as set forth in claim 12 wherein the second and third mold parts impact surface produce a pressure of 30 to 50 tons per square inch.

Assignees

• Howmedica Osteonics Corp

Inventors

• Lapszynski John
• Fuentes Jr Lionel

Classifications

• A61F2002/30968

  Sintering · CPC title

• B30B11/04

  co-operating with a fixed mould · CPC title

• B22F5/10 Primary

  of articles with cavities or holes, not otherwise provided for in the preceding subgroups · CPC title

• A61F2/3094

  Designing or manufacturing processes · CPC title

• A61F2002/30957

  using a positive or a negative model, e.g. moulds · CPC title