Composite separator for polymer electrolyte membrane fuel cell and method for manufacturing the same

Patent metadata

Field	Value
Publication number	US-9257706-B2
Application number	US-201514605300-A
Country	US
Kind code	B2
Filing date	Jan 26, 2015
Priority date	Nov 30, 2009
Publication date	Feb 9, 2016
Grant date	Feb 9, 2016

Abstract

The present invention provides a method for manufacturing a composite separator for a polymer electrolyte membrane fuel cell. The method comprises: preparing a prepreg as a continuous carbon fiber-reinforced composite and a graphite foil; allowing the cut prepreg and graphite foil to pass through a stacking/compression roller to be compressed; allowing the prepreg in which the graphite foil is integrally stacked to be heated and pressed by a hot press such that hydrogen, air, and coolant flow fields are formed or to pass through a hot roller to be formed into a separator; removing unnecessary portions from the heated and pressed separator using a trim cutter; and post-curing the thus formed separator, wherein the graphite foil may be stacked on the prepreg as the continuous carbon fiber-reinforced composite such that a graphite layer is integrally formed with the prepreg.

First claim

What is claimed is:

1. A method for manufacturing a composite separator for a polymer electrolyte membrane fuel cell, the method comprising:
preparing a prepreg as a continuous carbon fiber-reinforced composite;
preparing a mixed solution by mixing at least one selected from the group consisting of graphite flake, graphite powder, and carbon black nanoparticles with a solvent;

applying the mixed solution to both surfaces of the prepreg while the prepreg passes through a cutting means to be cut in the longitudinal direction of the separator or applying the mixed solution to both surfaces of the prepreg while the prepreg cut by the cutting roller with the cutter passes through a stacking/compression roller;
allowing the prepreg to which the mixed solution is applied to be heated and pressed by a hot press such that hydrogen, air, and coolant flow fields are formed or to pass through a hot roller to be formed into a separator, wherein the applying the mixed solution to both surfaces of the prepreg is spraying the mixed solution onto the prepreg as the continuous carbon fiber-reinforced composite;
removing unnecessary portions from the heated and pressed separator using a trim cutter; and post-curing the thus formed separator,
wherein the mixed solution is applied to the prepreg as the continuous carbon fiber-reinforced composite such that a graphite layer is integrally formed with the prepreg.

2. The method of claim 1 , wherein the mixed solution is prepared by mixing graphite flake or graphite powder having a particle size of 3 to 500 μm (5,000mesh-35 mesh), or carbon black nanoparticles with a-pesinthe solvent and applied to the prepreg.

3. A separator for a fuel cell prepared by the method of claim 1 , wherein the graphite layer is integrally formed on the outer surface of the prepreg.

4. The separator of claim 3 , wherein a small amount of surplus resin of the prepreg is impregnated into the graphite layer formed by the graphite foil stacked on the outermost end of the prepreg to be mechanically bonded thereto.

5. A method for manufacturing a composite separator for a polymer electrolyte membrane fuel cell, the method comprising:
preparing a prepreg as a continuous carbon fiber-reinforced composite the prepreg being a semi-cured sheet-like prepreg, the continuous carbon fiber-reinforced composite including continuous carbon fibers each of which is surrounded by a thermosetting polymer binder, the continuous carbon fibers having a length of several meters to several tens of meters; preparing a mixed solution by mixing at least one selected from the group consisting of graphite flake, graphite powder, and carbon black nanoparticles with a solvent;
applying the mixed solution to both surfaces of the prepreg while the prepreg passes through a cutting means to be cut in the longitudinal direction of the separator or applying the mixed solution to both surfaces of the prepreg while the prepreg cut by the cutting roller with the cutter passes through a stacking/compression roller, wherein the mixed solution is applied to the prepreg as the continuous carbon fiber-reinforced composite such that a graphite layer is integrally formed with the prepreg and hydrogen, air, and coolant flow fields are formed on the graphite layer at the same time when hydrogen, air, and coolant flow fields are formed on the prepreg;
allowing the prepreg to which the mixed solution is applied to be heated and pressed by a hot press such that hydrogen, air, and coolant flow fields are formed or to pass through a hot roller to be formed into a separator;
removing unnecessary portions from the heated and pressed separator using a trim cutter; and post-curing the thus formed separator.

6. The method of claim 5 , wherein the applying the mixed solution to both surfaces of the prepreg is spraying the mixed solution onto the prepreg as the continuous carbon fiber-reinforced composite.

Assignees

• Hyundai Motor Co Ltd
• Korea Advanced Inst Sci & Tech

Inventors

• Lee Dai Gil
• Yu Ha Na
• Lim Jun Woo
• Kim Sae Hoon
• Suh Jung Do
• Ahn Byung Ki

Classifications

• H01M8/0239

  Organic resins; Organic polymers · CPC title

• B32B2309/12

  Pressure · CPC title

• H01M8/0245

  in the form of layered or coated products · CPC title

• H01M8/0221

  Organic resins; Organic polymers · CPC title

• B32B2305/076

  Prepregs · CPC title