Process for the preparation of ethylene copolymers in the presence of free-radical polymerization initiator by copolymerizing ethylene, a bi- or multifunctional comonomer and optionally further comonomers

Patent metadata

Field	Value
Publication number	US-9238700-B2
Application number	US-201113996415-A
Country	US
Kind code	B2
Filing date	Dec 19, 2011
Priority date	Dec 22, 2010
Publication date	Jan 19, 2016
Grant date	Jan 19, 2016

Abstract

Process for preparing ethylene copolymers in the presence of free-radical polymerization initiator at pressures in the range of from 160 MPa to 350 MPa and temperatures in the range of from 100° C. to 350° C. in a tubular reactor by copolymerizing ethylene, a bi- or multifunctional comonomer and optionally further comonomers, wherein the bi- or multifunctional comonomer bears at least two different functional groups, of which at least one is a unsaturated group, which can be incorporated into the growing polymer chain, and at least another functional group can act as chain transfer agent in radical ethylene polymerization, ethylene copolymers obtainable by such a process, the use of the ethylene copolymers for extrusion coating and a process for extrusion coating a substrate selected from the group consisting of paper, paperboard, polymeric film, and metal, with such ethylene copolymers.

First claim

The invention claimed is:

1. A process for preparing ethylene copolymers in the presence of free-radical polymerization initiator at pressures in the range of from 160 MPa to 350 MPa and temperatures in the range of from 100° C. to 350° C. in a tubular reactor by copolymerizing ethylene, a bi- or multifunctional comonomer and optionally further comonomers, wherein the bi- or multifunctional comonomer has a structure represented by general formula (I):

wherein
R 1 is methyl or hydrogen,
X 1 is —O— or —NH—,
R 2 each R 2 can be identical or different and is selected from —Si(CH 3 ) 2 —, —CH 2 —O— or —Si(CH 3 ) 2 —O—,
n is from 1 to 32,
X 2 is —C(O)—, —CHOH— or —CHSH—, and
R 3 is C 1 -C 10 -alkyl or hydrogen,
or the unit X 2 —R 3 stands for —CH═CH 2 ,

wherein the bi- or multi-functional comonomer bears at least two different functional groups, of which at least one is an unsaturated group and at least another functional group can act as chain transfer agent in radical ethylene polymerization.

2. A process according to claim 1 , wherein a reactivity ratio of the bi- or multifunctional comonomer in the copolymerization with ethylene at 200 MPa and 180° C. is in the range of 0.1 to 500.

3. A process according to claim 1 , wherein the unsaturated group is an acrylate group, a methacrylate group or a double bond.

4. A process according to claim 1 , wherein the functional group that can act as a chain transfer agent is an aldehyde group, a ketone group, an alcohol group, a thiol group or a double bond.

5. A process according to claim 1 , wherein the bi- or multi-functional comonomer is acrylic acid 4 oxo-butyl ester, methacrylic acid 4-oxo-butyl ester, acrylic acid 2-oxo-propyl ester, methacrylic acid 2-oxo-propyl ester, acrylic acid 2-oxo-propyl ester or methacrylic acid 2 oxo-propyl ester.

6. A process according to claim 1 , wherein the free-radical polymerization initiator is added to a mixture comprising ethylene and the bi- or multifunctional comonomer.

7. The process of claim 1 , further comprising the step of preparing an article comprising the ethylene copolymer.

8. The process of claim 7 , wherein the article is prepared by the process of extrusion coating.

9. The process of claim 8 , wherein during the process of extrusion coating a substrate is coated with the ethylene copolymer wherein the substrate is selected from the group consisting of paper, paperboard, polymeric film, and metal.

Assignees

• Littmann Dieter
• Lilge Dieter
• Gall Barbara
• Vittorias Iakovos
• Mannebach Gerd
• Busch Markus
• Herrmann Thomas
• Basell Polyolefine Gmbh

Inventors

• Littmann Dieter
• Lilge Dieter
• Gall Barbara
• Vittorias Iakovos
• Mannebach Gerd
• Busch Markus
• Herrmann Thomas

Classifications

• C08F2/38 Primary

  Polymerisation using regulators, e.g. chain terminating agents {, e.g. telomerisation} · CPC title

• C08F210/02 Primary

  Ethene · CPC title

• C08F2/00

  Processes of polymerisation · CPC title

• C08F220/28

  containing no aromatic rings in the alcohol moiety · CPC title