Lithium ion secondary battery and process for manufacturing the same

Patent metadata

Field	Value
Publication number	US-9236594-B2
Application number	US-52743007-A
Country	US
Kind code	B2
Filing date	Feb 16, 2007
Priority date	Feb 16, 2007
Publication date	Jan 12, 2016
Grant date	Jan 12, 2016

Abstract

In multilayer wholly solid lithium ion secondary batteries, a laminate having a collector layer of material with high conductivity superimposed on an active material layer has been disposed so as to attain a lowering of battery impedance. Consequently, in the fabrication of each of positive electrode layer and negative electrode layer, stacking of three layers consisting of an active material layer, a collector layer and an active material layer has been needed, thereby posing the problem of complex processing and high production cost. In the invention, a positive electrode layer and a negative electrode layer are fabricated from paste consisting of active material mixed with conductive substance in a given mixing ratio, and no collector layer is disposed. This realizes process simplification and manufacturing cost reduction without deterioration of battery performance and has also been effective in enhancing of battery performance, such as improvement to cycle characteristics.

First claim

The invention claimed is:

1. A solid state lithium ion secondary battery, comprising a multilayer laminate in which a positive electrode layer and a negative electrode layer are stacked and alternately interposed by a solid electrolyte layer,
said positive electrode layer and/or said negative electrode layer having a structure where active material is supported by a conductive matrix comprising conductive material,
wherein the volume ratio of said active material to said conductive material is in a range of 20:80 to 65:35,
the conductive material is an oxidation resistant metal or oxidation resistant alloy having an electrical conductivity greater than 1×10 1 S/cm after sintering, and
the battery does not comprise a collector layer.

2. The battery according to claim 1 , comprising a plurality of battery unit cells, each unit cell comprising said laminate, and connected in parallel, in series, or in series-parallel combination.

3. The battery according to claim 2 , wherein said laminate is formed by stacking said positive electrode layer, said solid electrolyte layer, and said negative electrode layer to form said laminate, and then co-firing said laminate.

4. The battery according to claim 2 , wherein said active material comprises a transition metal oxide or transition metal composite oxide.

5. The battery according to claim 2 , wherein said active material comprises one or more compound selected from the group consisting of: lithium manganese composite oxide, lithium nickel composite oxide, lithium cobalt composite oxide, lithium vanadium composite oxide, lithium titanium composite oxide, manganese dioxide, titanium oxide, niobium oxide, vanadium oxide, and tungsten oxide.

6. The battery according to claim 1 , wherein said laminate is formed by stacking said positive electrode layer, said solid electrolyte layer, and said negative electrode layer to form said laminate, and then co-firing said laminate.

7. The battery according to claim 6 , wherein said active material comprises a transition metal oxide or transition metal composite oxide.

8. The battery according to claim 6 , wherein said active material comprises one or more compound selected from the group consisting of: lithium manganese composite oxide, lithium nickel composite oxide, lithium cobalt composite oxide, lithium vanadium composite oxide, lithium titanium composite oxide, manganese dioxide, titanium oxide, niobium oxide, vanadium oxide, and tungsten oxide.

9. The battery according to claim 1 , wherein said active material comprises a transition metal oxide or transition metal composite oxide.

10. The battery according to claim 9 , wherein said active material comprises one or more compound selected from the group consisting of: lithium manganese composite oxide, lithium nickel composite oxide, lithium cobalt composite oxide, lithium vanadium composite oxide, lithium titanium composite oxide, manganese dioxide, titanium oxide, niobium oxide, vanadium oxide, and tungsten oxide.

11. The battery according to claim 1 , wherein said active material comprises one or more compound selected from the group consisting of: lithium manganese composite oxide, lithium nickel composite oxide, lithium cobalt composite oxide, lithium vanadium composite oxide, lithium titanium composite oxide, manganese dioxide, titanium oxide, niobium oxide, vanadium oxide, and tungsten oxide.

12. The battery according to claim 1 , wherein said conductive material comprises a metal selected from the group consisting of: silver, palladium, gold, platinum, aluminum and an alloy of more than two metals selected from the group consisting of silver, palladium, gold, platinum, copper, and aluminum.

13. The battery according to claim 1 , wherein:
said active material in said positive electrode layer is lithium manganese composite oxide,
said active material in said negative electrode layer is lithium titanium composite oxide, and
said conductive material is silver palladium.

14. The battery according to claim 1 , wherein the multilayer laminate has been sintered at a temperature between 600-1100° C.

15. The battery according to claim 1 , wherein the conductive material has an electrical conductivity of greater than 1×10 3 S/cm after sintering.

16. The battery according to claim 1 , wherein said positive electrode layer and said negative electrode layer each have a structure where active material is supported by a conductive matrix comprising conductive material,
the volume ratio of said active material to said conductive material in the positive electrode is in a range of 29.7:70.3 to 48.1:51.9, and
the volume ratio of said active material to said conductive material in the negative electrode is in a range of 37.7:62.3 to 46.8:53.2.

Assignees

• Iwaya Shoichi
• Masumura Hitoshi
• Sakai Noriyuki
• Fujita Takayuki
• Sasagawa Hiroshi
• Sato Hiroshi
• Namics Corp

Inventors

• Iwaya Shoichi
• Masumura Hitoshi
• Sakai Noriyuki
• Fujita Takayuki
• Sasagawa Hiroshi
• Sato Hiroshi

Classifications

• H01M4/505 Primary

  of mixed oxides or hydroxides containing manganese for inserting or intercalating light metals, e.g. LiMn2O4 or LiMn2OxFy · CPC title

• H01M50/497

  Ionic conductivity · CPC title

• H01M50/40

  Separators; Membranes; Diaphragms; Spacing elements inside cells · CPC title

• H01M2/14 Primary

  Electricity · mapped topic

• H01M4/48

  of inorganic oxides or hydroxides · CPC title