Flame retardant

Patent metadata

Field	Value
Publication number	US-9234137-B2
Application number	US-201013516464-A
Country	US
Kind code	B2
Filing date	Dec 15, 2010
Priority date	Dec 16, 2009
Publication date	Jan 12, 2016
Grant date	Jan 12, 2016

Abstract

Use of a phosphorus compound of the formula (I) as flame retardant,

where the definitions of the symbols in the formula (I) are as follows:
A is one of the following groups:

Y is —P(═X 2 ) S R 3 R 4 , H, a straight-chain or branched C 1 -C 12 -alkyl group, C 5 -C 6 -cycloalkyl, C 6 -C 12 -aryl, or benzyl, where the four last-mentioned groups are unsubstituted or have substitution by one or more radicals from the group of C 1 -C 4 -alkyl or C 1 -C 4 -alkenyl;
R 1 , R 2 , R 3 , and R 4 are identical or different and are hydrogen, OH, C 1 -C 16 -alkyl, C 1 -C 16 -alkenyl, C 1 -C 16 -alkoxy, C 1 -C 16 -alkenoxy, C 3 -C 10 -cycloalkyl, C 3 -C 10 -cycloalkoxy, C 6 -C 10 -aryl, C 6 -C 10 -aryloxy, C 6 -C 10 -aryl-C 1 -C 16 -alkyl, C 6 -C 10 -aryl-C 1 -C 16 -alkoxy, SR 9 COR 10 , COOR 11 , CONR 12 R 13 or two radicals R 1 , R 2 , R 3 , or R 4 form, together with the phosphorus atom to which they are bonded, or the P—O-A-O—P group, a ring system;
R 5 , R 6 , R 7 , and R 8 are identical or different and are H, C 1 -C 16 -alkyl, C 1 -C 16 -alkenyl, C 1 -C 16 -alkoxy, C 1 -C 16 -alkenoxy;
R 9 , R 10 , R 11 , R 12 , R 13 are identical or different and are H, C 1 -C 16 -alkyl, C 1 -C 16 -alkenyl, C 6 -C 10 -aryl, C 6 -C 10 -aryl-C 1 -C 16 -alkyl, C 6 -C 10 -aryl-C 1 -C 16 -alkoxy;
X 1 and X 2 are identical or different and are S or O;
r and s are identical or different and are 0 or 1;
X 3 , X 4 , X 5 , and X 6 are identical or different and are S or O, and
n is a natural number from 1 to 50.

First claim

The invention claimed is:

1. A process for providing flame retardancy to a material, comprising adding a phosphorus compound selected from compounds II.1 to II.4 and compounds of the formula (I) to the material as flame retardant,

where the definitions of the symbols in the formula (I) are as follows:
A is one of the following groups:

Y is —P(═X 2 ) S R 3 R 4 , H, a straight-chain or branched C 1 -C 12 -alkyl group, C 5 -C 6 -cycloalkyl, C 6 -C 12 -aryl, or benzyl, where the four last-mentioned groups are unsubstituted or have substitution by one or more radicals C 1 -C 4 -alkyl or C 2 -C 4 -alkenyl;
R 1 , R 2 , R 3 , and R 4 are identical or different and are hydrogen, OH, C 1 -C 16 -alkyl, C 2 -C 16 -alkenyl, C 1 -C 16 -alkoxy, C 2 -C 16 -alkenoxy, C 3 -C 10 -cycloalkyl, C 3 -C 10 -cycloalkoxy, C 6 -C 10 -aryl, C 6 -C 10 -aryloxy, C 6 -C 10 -aryl-C 1 -C 16 -alkyl, C 6 -C 10 -aryl-C 1 -C 16 -alkoxy, SR 9 COR 10 , COOR 11 , CONR 12 R 13 or two radicals R 1 , R 2 , R 3 , or R 4 form, together with the phosphorus atom to which they are bonded, or the P—O-A-O—P group, a ring system;
R 5 , R 6 , R 7 , and R 8 are identical or different and are H, C 1 -C 16 -alkyl, C 2 -C 16 -alkenyl, C 1 -C 16 -alkoxy or C 2 -C 16 -alkenoxy;
R 9 , R 10 , R 11 , R 12 , R 13 are identical or different and are H, C 1 -C 16 -alkyl, C 2 -C 16 -alkenyl, C 6 -C 10 -aryl, C 6 -C 10 -aryl-C 1 -C 16 -alkyl or C 6 -C 10 -aryl-C 1 -C 16 -alkoxy;
X 1 and X 2 are identical or different and are S or O;
r and s are identical or different and are 0 or 1;
X 5 and X 6 are identical or different and are S or O, and
n is a natural number from 1 to 50.

2. The process according to claim 1 , wherein
A is a group of the formula (III) or (IV);
Y is (X 2 ) r PR 3 R 4 , or H;
R 1 , R 2 , R 3 , and R 4 are identical or different and are C 6 -C 10 -aryloxy, C 1 -C 10 -aryl-C 1 -C 16 -alkyl or C 6 -C 10 -aryl-C 1 -C 16 -alkoxy;
R 5 , R 6 , R 7 , and R 8 are identical or different and are H, C 1 -C 16 -alkyl, C 2 -C 16 -alkenyl, C 1 -C 16 -alkoxy, C 2 -C 16 -alkenoxy;
X 1 and X 2 are identical or different and are S or O;
r and s are identically 0 or 1;
X 5 and X 6 are O, and
n is a natural number from 1 to 30.

3. The process according to claim 1 , wherein
A is a group of the formula (III) or (IV);
Y is (X 2 ) r PR 3 R 4 ;
R 1 , R 2 , R 3 , and R 4 are identical or different and are phenyl, phenoxy, phenyl-C 1 -C 16 -alkyl, or phenyl-C 1 -C 16 -alkoxy;
R 5 , R 6 , R 7 , and R 8 are H;
X 1 and X 2 are identical or different and are S or O;
r and s are identically 0 or 1;
X 5 and X 6 are O, and
n is 1.

4. The process according to claim 1 , wherein
A is a group of the formula (III) or (IV);
Y is (X 2 ) r PR 3 R 4 ;
R 1 , R 2 , R 3 , and R 4 are identically phenyl or phenoxy;
R 5 , R 6 , R 7 , and R 8 are H;
X 1 and X 2 are identically S or O;
r and s are identically 0 or 1;
X 5 and X 6 are oxygen, and
n is 1.

5. The process according to claim 1 , wherein the compound of the formula (I) has been selected from:

6. The process according to claim 1 , wherein one compound of the formula (I) is added.

7. The process according to claim 1 , wherein at least two different compounds of the formula (I) are added.

8. The process according to claim 1 , wherein the compound(s) of the formula (I) is/are added in a mixture with one or more other flame-retardant compounds and/or with one or more synergists.

9. The process according to claim 8 , wherein the synergist is used from the group consisting of organic peroxides, organic polysulfides, C—C-cleaving initiators, and elemental sulfur.

10. The process according to claim 1 , wherein the material is a polymer material, comprising one or more polymers.

11. A polymer composition comprising one or more polymers and a flame retardant and wherein the flame retardant comprises a phosphorus compound selected from II.1 to II.4 and of the formula (I),

where the definitions of the symbols in the formula (I) are as follows:
A is one of the following groups:

Y is —P(═X 2 ) S R 3 R 4 , H, a straight-chain or branched C 1 -C 12 -alkyl group, C 5 -C 6 -cycloalkyl, C 6 -C 12 -aryl, or benzyl, where the four last-mentioned groups are unsubstituted or have substitution by one or more radicals C 1 -C 4 -alkyl or C 2 -C 4 -alkenyl;
R 1 , R 2 , R 3 , and R 4 are identical or different and are hydrogen, OH, C 1 -C 16 -alkyl, C 2 -C 16 -alkenyl, C 1 -C 16 -alkoxy, C 2 -C 16 -alkenoxy, C 3 -C 10 -cycloalkyl, C 3 -C 10 -cycloalkoxy, C 6 -C 10 -aryl, C 6 -C 10 -aryloxy, C 6 -C 10 -aryl-C 1 -C 16 -alkyl, C 6 -C 10 -aryl-C 1 -C 16 -alkoxy, SR 9 COR 10 , COOR 11 , CONR 12 R 13 or two radicals R 1 , R 2 , R 3 , or R 4 form, together with the phosphorus atom to which they are bonded, or the P—O-A-O—P group, a ring system;
R 5 , R 6 , R 7 , and R 8 are identical or different and are H, C 1 -C 16 -alkyl, C 2 -C 16 -alkenyl, C 1 -C 16 -alkoxy or C 2 -C 16 -alkenoxy;
R 9 , R 10 , R 11 , R 12 , R 13 are identical or different and are H, C 1 -C 16 -alkyl, C 2 -C 16 -alkenyl, C 6 -C 10 -aryl, C 6 -C 10 -aryl-C 1 -C 16 -alkyl or C 6 -C 10 -aryl-C 1 -C 16 -alkoxy;
X 1 and X 2 are identical or different and are S or O;
r and s are identical or different and are 0 or 1;
X 5 and X 6 are identical or different and are S or O, and
n is a natural number from 1 to 50.

12. The polymer composition according to claim 11 , comprising from 0.1 to 25% by weight (based on polymer content) of the flame retardant.

13. The polymer composition according to claim 11 , which is halogen-free.

14. The polymer composition according to claim 11 , comprising a styrene polymer.

15. The polymer composition according to claim 11 , wherein the polymer is a polymer foam.

16. The polymer composition according to claim 14 in the form of an expandable styrene polymer (EPS).

17. A process for the production of the expandable styrene polymer (EPS) according to claim 16 , comprising the following steps:
a) mixing to incorporate an organic blowing agent and one or more compounds of II.1 to II.4 and/or of the formula (I) according to claim 1 and optionally further auxiliaries and additives into a styrene polymer melt by means of static and/or dynamic mixers at a temperature of at least 150° C.,
b) cooling of the styrene polymer melt comprising blowing agent to a temperature of at least 120° C.,
c) discharging through a die plate with holes, the diameter of which at the exit from the die is at most 1.5 mm, and
d) pelletization of the melt comprising blowing agent directly behind the die plate under water at a pressure in the range from 1 to 20 bar.

18. A process for the production of the expandable styrene polymer according to claim 16 , comprising the following steps:
a) polymerizing one o

Assignees

• Fleckenstein Christoph
• Denecke Hartmut
• Bellin Ingo
• Kriha Olaf
• Spies Patrick
• Fuchs Sabine
• Massonne Klemens
• Hahn Klaus
• Deglmann Peter
• Hofmann Maximilian
• Kindler Alois
• Basf Se

Inventors

• Fleckenstein Christoph
• Denecke Hartmut
• Bellin Ingo
• Kriha Olaf
• Spies Patrick
• Fuchs Sabine
• Massonne Klemens
• Hahn Klaus
• Deglmann Peter
• Hofmann Maximilian
• Kindler Alois

Classifications

• C08K5/49

  Phosphorus-containing compounds {(C08K5/0091 takes precedence)} · CPC title

• C08K5/53

  bound to oxygen and to carbon only · CPC title

• C08K5/5313

  Phosphinic compounds, e.g. R2=P(:O)OR' · CPC title

• C08L2203/14

  used for foams · CPC title

• C09K21/12 Primary

  containing phosphorus · CPC title