Cement composition containing dune sand and limestone powder, concrete products and method for making concrete products

Patent metadata

Field	Value
Publication number	US-9039830-B2
Application number	US-201213647656-A
Country	US
Kind code	B2
Filing date	Oct 9, 2012
Priority date	Oct 9, 2012
Publication date	May 26, 2015
Grant date	May 26, 2015

Abstract

A raw batch composition for concrete or concrete wherein the raw batch composition comprises Portland cement of about 15 wgt. % to about 45 wgt. % and dune sand preferably red dune sand is present in an amount of about 40 wgt. %. The dune sand has a particle size of less than or equal to 45 microns. The composition also includes limestone powder ranging from about 15 wgt. % to 45 wgt. % with particle sizes less than or equal to 45 microns to form a base material. To this base material suitable amounts of fine aggregate, coarse aggregate, water and superplasticizer are added. A method for producing a cast concrete product having a compressive strength of between 62 MPa and 90 MPa is disclosed. The method comprises a step of providing Portland cement, dune sand and limestone powder.

First claim

What is claimed is:

1. A raw batch composition for concrete comprising:
Portland cement;
dune sand having a particle size of about 45 microns or less;
limestone powder having a particle size of about 45 microns or less;
aggregate other than dune sand;
a sufficient amount of water to effect hydraulic setting of the cementitious compound; and
wherein said Portland cement ranges from about 15 wgt. % to about 45 wgt. %, said dune sand is present in an amount of 40 wgt. % and said limestone powder ranges from about 15 wgt. % to about 45 wgt. % plus aggregate and water.

2. A raw batch composition according to claim 1 , in which said dune sand is red dune sand having a composition of about 91.4 wgt. % SiO 2 , about 0.99 wgt. % Al 2 O 3 , 0.56 wgt. % Fe 2 O 3 , 1.68 wgt. % MgO about 0.18 wgt. %, K 2 O 0.21 wgt. %, Na 2 O 0.17 wgt. %, SO 3 0.06 wgt. % and LOI los on ignition 1.15 wgt. %.

3. A raw batch composition according to claim 1 , in which an amount of superplasticizer, aggregate and water are added.

4. A raw batch composition according to claim 3 , in which the Portland cement, dune sand powder and limestone powder, fine aggregate, water and superplasticizer are provided in a ratio of the following amounts Portland cement (kg/m 3 ) 252, dune sand powder (kg/m 3 ) 224, limestone powder (kg/m 3 ) 84, fine aggregate (kg/m 3 ) 1680, water (kg/m 3 ) 168 and superplasticizer (kg/m 3 ) 9.

5. A raw batch composition according to claim 3 , in which the Portland cement, dune sand powder and limestone powder, fine aggregate, water and superplasticizer are provided in a ratio of the following amounts Portland cement (kg/m 3 ) 168, dune sand powder (kg/m 3 ) 224, limestone powder (kg/m 3 ) 168, fine aggregate (kg/m 3 ) 1680, water (kg/m 3 ) 168 and superplasticizer (kg/m 3 ) 12.

6. A raw batch composition according to claim 3 , in which the Portland cement, dune sand powder and limestone powder, fine aggregate, water and superplasticizer are provided in a ratio of the following amounts Portland cement (kg/m 3 ) 84, dune sand powder (kg/m 3 ) 224, limestone powder (kg/m 3 ) 252, fine aggregate (kg/m 3 ) 1680, water (kg/m 3 ) 168 and superplasticizer (kg/m 3 ) 12.

7. A raw batch composition for concrete consisting of:
Portland cement, red dune sand powder having a particle size of 45 microns or less, limestone powder having a particle size of 45 microns or less and wherein said Portland cement ranges from 15 wgt. % to 45 wgt. %, said red dune sand is about 40 wgt. % and said limestone powder ranges from about 15 wgt. % to 45 wgt. % to form a base mix; and
fine aggregate, water and superplasticizer.

8. A raw batch composition according to claim 7 , in which the following ingredients further consists of a ratio of the following amounts Portland cement (kg/m 3 ) 252, dune sand powder (kg/m 3 ) 224, limestone powder (kg/m 3 ) 84, fine aggregate (kg/m 3 ) 1680, water (kg/m 3 ) 168 and superplasticizer (kg/m 3 ) 9.

9. A raw batch composition according to claim 7 , in which the following ingredients further consists of a ratio of the following amounts Portland cement (kg/m 3 ) 168, dune sand powder (kg/m 3 ) 224, limestone powder (kg/m 3 ) 168, fine aggregate (kg/m 3 ) 1680, water (kg/m 3 ) 168 and superplasticizer (kg/m 3 ) 12.

10. A raw batch composition according to claim 7 , in which the following ingredients further consists of a ratio of the following amounts Portland cement (kg/m 3 ) 84, dune sand powder (kg/m 3 ) 224, limestone powder (kg/m 3 ) 252, fine aggregate (kg/m 3 ) 1680, water (kg/m 3 ) 168 and superplasticizer (kg/m 3 ) 12.

11. A method for producing a cast concrete product in which the steps consists of:
a) providing red dune sand and limestone;
b) grinding said red dune sand and said limestone to produce particle sizes of less than 45 microns;
c) mixing the dune sand and limestone with cement, aggregate other than red dune sand, water and superplasticizer to produce a cement mix with about 40% dune sand powder and a range of Portland cement from 15 wgt. % to 45 wgt. % and limestone powder from 15 wgt. % to 45 wgt. %;
d) casting the concrete mix in a predetermined shape by placing the concrete mix in a mold to produce a molded article;
e) within 24 hours of casting, steam curing the molded article for 12 hours under atmospheric pressure;
f) de-molding the molded article and placing the molded article inside a curing chamber and maintaining 100% humidity in the curing chamber;
g) raising the temperature in the curing chamber to between 160° C. and 200° C. within two hours to thereby raise the pressure to 10 bars and maintaining the 180° C. temperature at 100% humidity within the curing chamber for 4 to 5 hours;
h) releasing the pressure to reach atmospheric pressure within 20-30 minutes and the temperature is reduced gradually.

Assignees

• Univ King Saud

Inventors

• Alhozaimy Abdulrahman M
• Jaafar Mohd S
• Al-Negheimish Abdulaziz
• Alawad Omer A

Classifications

• C04B2103/32

  Superplasticisers · CPC title

• C04B28/04 Primary

  Portland cements · CPC title

• C04B14/28

  of calcium · CPC title

• C04B14/068

  Specific natural sands, e.g. sea -, beach -, dune - or desert sand · CPC title

• C04B40/024

  Steam hardening, e.g. in an autoclave · CPC title