Method for producing ammonium tungstate aqueous solution

Patent metadata

Field	Value
Publication number	US-8974674-B2
Application number	US-201013582644-A
Country	US
Kind code	B2
Filing date	Mar 5, 2010
Priority date	Mar 5, 2010
Publication date	Mar 10, 2015
Grant date	Mar 10, 2015

Abstract

A method for producing an ammonium tungstate aqueous solution includes the steps of: adding sulfuric acid to a solution containing tungstate ions; bringing the solution having the sulfuric acid added therein, into contact with an anion exchange resin; and bringing the anion exchange resin into contact with an aqueous solution containing ammonium ions.

First claim

The invention claimed is:

1. A method for producing an ammonium tungstate aqueous solution, comprising the steps of:
decreasing a pH of a solution containing tungstate ions and vanadate ions to not less than 7 and not more than 9 by using sulfuric acid to generate polyacid cluster ions of tungsten and vanadium;
bringing said solution having the pH decreased, into contact with an anion exchange resin;
eluting the vanadate ions from said anion exchange resin, by bringing said polyacid cluster ions of tungsten and vanadium adsorbed in said anion exchange resin into contact with a basic solution having a pH of 9 or higher to decompose said polyacid cluster ions of tungsten and vanadium into the tungstate ions and the vanadate ions;
eluting the tungstate ions remaining in said anion exchange resin with an aqueous solution after eluting the vanadate ions to obtain a discharged solution containing the tungstate ions;
adding sulfuric acid to said discharged solution containing the tungstate ions to generate poly tungstate ions;
bringing said discharged solution having said sulfuric acid added therein, into contact with said anion exchange resin;
bringing said anion exchange resin with which said discharged solution is brought into contact, into contact with an ammonia solution; and
recovering a solution discharged from said anion exchange resin in the step of bringing said anion exchange resin into contact with said ammonia solution.

2. The method for producing the ammonium tungstate aqueous solution according to claim 1 , wherein said solution containing the tungstate ions and the vanadate ions has a tungsten oxide concentration of not less than 20 g/L and not more than 150 g/L, and has a vanadium concentration of not less than 15 mg/L and not more than 1000 mg/L.

3. The method for producing the ammonium tungstate aqueous solution according to claim 1 , wherein in the step of bringing said solution having the pH decreased into contact with said anion exchange resin, said solution having the pH decreased is supplied to said anion exchange resin or said anion exchange resin is soaked in said solution having the pH decreased.

4. The method for producing the ammonium tungstate aqueous solution according to claim 1 , wherein a ratio of a content of vanadium to a content of tungsten is 1×10 −4 or smaller in the solution containing the vanadium ions from said anion exchange resin with which said solution having the pH decreased is brought into contact.

5. The method for producing the ammonium tungstate aqueous solution according to claim 1 , wherein said basic solution is a solution having a pH of 9 or greater and containing at least one selected from a group consisting of a sodium hydroxide aqueous solution, a potassium hydroxide aqueous solution, and ammonia solution.

6. The method for producing the ammonium tungstate aqueous solution according to claim 5 , wherein the aqueous solution containing at least one selected from a group consisting of chloride ions, sulfate ions, and nitrate ions is brought into contact with said anion exchange resin after the contact with said basic solution.

7. A method for producing the ammonium tungstate aqueous solution, comprising the steps of:
producing a polyacid solution containing poly tungstate ions and Mo-containing polyacid ions;
adsorbing said poly tungstate ions to a first anion exchange resin tower of an anion exchange resin and adsorbing said Mo-containing polyacid ions to a second anion exchange resin tower of said anion exchange resin tower by supplying said polyacid solution to said anion exchange resin tower constituted of said first anion exchange resin and said second anion exchange resin connected to each other, such that said first anion exchange resin is first supplied with said polyacid solution;
disconnecting said first anion exchange resin and said second anion exchange resin from each other; and
bringing an aqueous solution containing ammonium ions into contact with said first anion exchange resin after the step of disconnecting.

8. The method for producing the ammonium tungstate aqueous solution according to claim 7 , wherein in the step of bringing said aqueous solution containing the ammonium ions into contact, an ammonia solution is brought into contact with the first anion exchange resin.

9. The method for producing the ammonium tungstate aqueous solution according to claim 7 , wherein said polyacid solution has a pH of not less than 3.5 and not more than 8.

10. The method for producing the ammonium tungstate aqueous solution according to claim 8 , comprising the step of bringing a solution containing at least one selected from a group consisting of chloride ions, nitrate ions, and sulfate ions, into contact with said first anion exchange resin after the step of bringing said ammonia solution into contact therewith.

11. The method for producing the ammonium tungstate aqueous solution according to claim 10 , comprising the steps of:
obtaining a reconnected anion exchange resin by connecting said first anion exchange resin and said second anion exchange resin to each other, after the step of bringing said ammonia solution into contact with the first anion exchange resin, said second anion exchange resin being after the step of adsorbing said Mo-containing polyacid ions;
adsorbing said poly tungstate ions to said second anion exchange resin and adsorbing said Mo-containing polyacid ions to said first anion exchange resin by supplying said polyacid solution to said reconnected anion exchange resin such that said second anion exchange resin is first supplied with said polyacid solution; and
bringing ammonia solution into contact with said second anion exchange resin.

12. A method for producing an ammonium tungstate aqueous solution, comprising the steps of:
producing a polyacid solution containing poly tungstate ions and Mo-containing polyacid ions;
adsorbing said poly tungstate ions to a first anion exchange resin of an anion exchange resin tower without adsorbing said Mo-containing polyacid ions thereto, by supplying said polyacid solution to said anion exchange resin tower constituted of said first anion exchange resin, a second anion exchange resin, and a third anion exchange resin connected to one another in this order, such that said first anion exchange resin is first supplied with said polyacid solution;
disconnecting said first anion exchange resin and said second anion exchange resin from each other; and
bringing an ammonia solution into contact with said first anion exchange resin after the step of disconnecting.

13. The method for producing the ammonium tungstate aqueous solution according to claim 12 , comprising the step of bringing a solution containing at least one selected from a group consisting of chloride ions, nitrate ions, and sulfate ions, into contact with said first anion exchange resin after the step of bringing said ammonia solution into contact therewith.

14. The method for producing the ammonium tungstate aqueous solution according to claim 13 , comprising the steps of:
obtaining a reconnected anion exchange resin by connecting said second anion exchange resin, said third anion exchange resin, and said first anion exchange resin in this order, said second anion exchange resin being after the step of disconnecting, said third anion exchange resin being after the step of disconnecting, said first anion exchange resin being after the step of bringing said solution containing at least one selected from a group consisting of chloride ions, nitrate ions and sulfate ions into contact therewith;
adsorbing said poly tungstate ions to said second anion exchange

Assignees

• Ito Hideaki
• Itakura Takeshi
• Yamamoto Yoshiharu
• Sasaya Kazuo
• Okuno Takuya
• Sato Fumiatsu
• Yamanaka Syunsuke
• Ikegaya Akihiko
• Univ Nagoya Nat Univ Corp
• Almt Corp
• Sumitomo Elec Hardmetal Corp
• Sumitomo Electric Industries

Inventors

• Ito Hideaki
• Itakura Takeshi
• Yamamoto Yoshiharu
• Sasaya Kazuo
• Okuno Takuya
• Sato Fumiatsu
• Yamanaka Syunsuke
• Ikegaya Akihiko

Classifications

• G10L13/08

  Text analysis or generation of parameters for speech synthesis out of text, e.g. grapheme to phoneme translation, prosody generation or stress or intonation determination · CPC title

• G10L15/06

  Creation of reference templates; Training of speech recognition systems, e.g. adaptation to the characteristics of the speaker's voice (G10L15/14 takes precedence) · CPC title

• C01P2006/80

  Compositional purity · CPC title

• G10L15/187

  Phonemic context, e.g. pronunciation rules, phonotactical constraints or phoneme n-grams · CPC title

• C01G41/00 Primary

  Compounds of tungsten · CPC title