Aerogel composition for thermal insulation

Patent metadata

Field	Value
Publication number	US-2025313485-A1
Application number	US-202318865395-A
Country	US
Kind code	A1
Filing date	May 25, 2023
Priority date	May 27, 2022
Publication date	Oct 9, 2025
Grant date	—

Abstract

A heat control member comprises a mixture of a) silica aerogel particles having particle sizes in a range from 0.1 mm to 5 mm and b) hydrophobic silica-containing particles having a methanol number of at least 30 and a particle size D50 of 100 microns or less, the mixture having a particle size distribution of silica-containing particles having at least two peaks. The silica aerogel particles and hydrophobic silica containing particles are present in a ratio from 1:99 to 99:1; and the heat control member has a thermal conductivity at 25° C. of from 5 to 30 mW/m.K and a thickness of 0.1-10 mm.

First claim

What is claimed is:

1 . A heat control member comprising a mixture of a) silica aerogel particles having particle sizes in a range from 0.1 mm to 5 mm and b) hydrophobic silica-containing particles having a methanol number of at least 30 and a particle size D50 of 100 microns or less, the mixture having a particle size distribution of silica-containing particles having at least two peaks,
wherein the silica aerogel particles and hydrophobic silica containing particles are present in a ratio from 1:99 to 99:1; and wherein the heat control member has a thermal conductivity at 25° C. of approximately 5-30 mW/m.K and a thickness of 0.1-10 mm.

2 . The heat control member of claim 1 , wherein the hydrophobic silica-containing particles are selected from the group consisting of silica aerogel, fumed silica, silicon-treated carbon black, silica-coated carbon black, fumed mixed metal oxides, precipitated silica, silica-carbon black composite particles, rice husk silica, and sol-gel silica.

3 . The heat control member of claim 1 , wherein the hydrophobic silica-containing particles are selected from the group consisting of silica aerogel, fumed silica, precipitated silica, and sol-gel silica.

4 . The heat control member of claim 1 , wherein the hydrophobic silica-containing particles are hydrophobized by a silicone fluid, a cyclic siloxane, a hydrophobizing silane, a functionalized silane, or a silazane.

5 . The heat control member of claim 1 , wherein the hydrophobic silica-containing particles are hydrophobic fumed silica particles having a surface area from 30 to 550 m 2 /g, preferably from 30 to 250 m 2 /g.

6 . The heat control member of claim 1 , wherein the hydrophobizing silane is: R 4-n SiX n wherein n is 1-3, each R is independently selected from the group consisting of hydrogen, a C1-C30 branched and straight chain alkyl or alkenyl group, a C3-C18 haloalkyl group, C3-C10 cycloalkyl, and a C6-C14 aromatic group, and each X is independently a C1-C18 branched or straight chain alkoxy group or halo.

7 . The heat control member of claim 1 , wherein the functionalized silane comprises at least one functional group selected from the group consisting of acrylate, methacrylate, amino, anhydride, epoxy, halogen, hydroxyl, sulfur, vinyl, isocyanate, and combinations thereof.

8 . The heat control member of claim 1 , wherein the particle size D50 of the hydrophobic silica-containing particle is from 0.1 microns to 100 microns.

9 . The heat control member of claim 1 , wherein the mixture further comprises fibers.

10 . The heat control member of claim 1 , wherein the fibers are glass fibers, ceramic fibers, synthetic polymer fibers, carbon fiber, natural polymer fibers, mineral wool, or a mixture of two or more of these.

11 . The heat control member of claim 1 , wherein the fibers are blackened or coated with a metal.

12 . The heat control member of claim 1 , wherein at least a portion of the silica aerogel present in the heat control member incorporates an opacifier.

13 . The heat control member of claim 1 , wherein at least a portion of the silica aerogel is coated with or impregnated with a heat absorbing material.

14 . The heat control member of claim 1 , wherein the mixture further comprises one or more components selected from the group consisting of fiber, opacifier, fire retardant, heat absorbing material, phase change material, binder, defoamer, dispersant, emulsifier, surfactant, and flocculant.

15 . The heat control member of claim 1 , further comprising a sheet or mat comprising silicone, polyvinylidene fluoride, chlorinated polyethylene, aramid fibers, or aramid aerogel.

16 . The heat control member of claim 1 , further comprising an envelope encapsulating the mixture.

17 . The heat control member of claim 1 , wherein the heat control member is in the form of a blanket or pressed pad.

18 . The heat control member of claim 1 , wherein the heat control member meets the specifications of UL94 V0.

Assignees

• Cabot Corp

Inventors

• Zhang Xiaofeng
• Pescatore Peter F
• Sanchez Garcia Angelica M
• Bannon Clare

Classifications

• C01P2006/32

  Thermal properties · CPC title

• C01B33/183

  by oxidation or hydrolysis in the vapour phase of silicon compounds such as halides, trichlorosilane, monosilane · CPC title

• C01P2006/12

  Surface area · CPC title

• H01M10/052

  Li-accumulators · CPC title

• H01M10/65

  Means for temperature control structurally associated with the cells · CPC title