Method of manufacturing positive electrode active material for rechargeable lithium battery and rechargeable lithium battery

Patent metadata

Field	Value
Publication number	US-2025309391-A1
Application number	US-202519090823-A
Country	US
Kind code	A1
Filing date	Mar 26, 2025
Priority date	Mar 27, 2024
Publication date	Oct 2, 2025
Grant date	—

Abstract

A method of manufacturing a positive electrode active material comprises a first grinding step of grinding a positive electrode scrap of a lithium battery. The ground positive electrode scrap is heat treated. The heat treated positive electrode scrap is ground, and a current collector component and an active material component are separated from the heat treated and ground positive electrode scrap. A solvent is used to wash the separated active material component, solid is separated from liquid, and the solid is dried. With the method, positive electrode active material may be effectively recovered from a positive electrode scrap produced during the fabrication of a rechargeable lithium battery.

First claim

What is claimed is:

1 . A method of manufacturing a positive electrode active material, the method comprising:
a first grinding step of grinding a positive electrode scrap of a lithium battery; heat treating the ground positive electrode scrap; a second grinding step of grinding the heat treated positive electrode scrap; separating a current collector component and an active material component from the positive electrode scrap that was ground in the first and second grinding steps and heat treated in the heat treating step; washing the separated active material component with a solvent; separating the washed separated active material component into solid and liquid; and drying the solid.

2 . The method of claim 1 , wherein each of the first grinding step and the second grinding step uses at least one selected from a cut crusher, a shear, a pin mill, an impact mill, a ball mill, and a bead mill.

3 . The method of claim 1 , wherein the positive electrode scrap after the first grinding step has an average size of about 0.1 cm to about 1 cm.

4 . The method of claim 1 , wherein the heat treatment is performed at about 400° C. to about 600° C. for about 30 minutes to about 3 hours under vacuum condition.

5 . The method of claim 1 , wherein the positive electrode scrap after the second grinding step has an average particle diameter of about 1 mm to about 3 mm.

6 . The method of claim 1 , wherein separating the current collector component and the active material component includes the use of a sieve having a screen size in a range of about 100 mesh to about 1,000 mesh.

7 . The method of claim 1 , wherein the current collector component includes aluminum, and an amount of aluminum in the dried solid is in a range of about 0.001 wt % to about 3 wt %.

8 . The method of claim 7 , wherein the positive electrode active material in the dried solid has an average particle diameter (D 50 ) of about 1 μm to about 20 μm.

9 . The method of claim 1 , wherein washing the separated active material component includes performing an ultrasonic treatment for about 10 seconds to about 100 seconds.

10 . The method of claim 1 , wherein the solvent includes at least one of water, N-methyl-2-pyrrolidone (NMP), isopropanol (IPA), dimethyl sulfoxide (DMSO), dimethylformamide (DMF), N-cyclohexyl-2-pyrrolidone (CHP), ethanol, methanol, acetone, chlorobenzene, and dichlorobenzene.

11 . The method of claim 1 , wherein separating the solid and the liquid includes performing a centrifugal separation for 1 minute to about 20 minutes at about 1,000 rpm to about 5,000 rpm.

12 . The method of claim 1 , wherein drying the solid is performed for about 2 hours to about 24 hours at about 120° C. to about 180° C.

13 . A method of manufacturing a positive electrode active material, the method comprising:
a first grinding step of grinding a positive electrode scrap of a lithium battery; heat treating the positive electrode scrap at a temperature of about 400° C. to about 600° C.; a second grinding step of grinding the heat treated positive electrode scrap; and separating a current collector component and an active material component from the positive electrode scrap that was ground in the first and second grinding step and heat treated in the heat treating step.

14 . The method of claim 13 , wherein each of the first grinding step and the second grinding step uses at least one selected from a cut crusher, a shear, a pin mill, an impact mill, a ball mill, and a bead mill.

15 . The method of claim 13 , wherein the positive electrode scrap after the first grinding step has an average size of about 0.1 cm to about 1 cm.

16 . The method of claim 13 , wherein the positive electrode scrap after the second grinding step has an average particle diameter of about 1 mm to about 3 mm.

17 . The method of claim 13 , wherein separating the current collector component and the active material component includes the use of a sieve having a screen size in a range of about 100 mesh to about 1,000 mesh.

18 . The method of claim 13 , wherein the current collector component includes aluminum, and an amount of aluminum in the separated active material component is in a range of about 0.001 wt % to about 3 wt %.

19 . The method of claim 18 , wherein the positive electrode active material in the separate active material has an average particle diameter (D 50 ) of about 1 μm to about 20 μm.

20 . A rechargeable lithium battery comprising:
a positive electrode that includes the positive electrode active material manufactured according to the method of claim 1 ; a negative electrode that includes a negative electrode active material; and an electrolyte, wherein an amount of aluminum in the positive electrode active material is in a range of about 0.001 wt % to about 3 wt %.

Assignees

• Samsung Sdi Co Ltd

Inventors

• Lee Youngjun
• Son Jongsung
• Sohn Myungbeom
• Yoo Kwangyong
• Park Seongin
• You Yongchan

Classifications

• H01M2004/028

  Positive electrodes · CPC title

• B08B3/12

  by sonic or ultrasonic vibrations · CPC title

• B08B3/02

  Cleaning by the force of jets or sprays · CPC title

• C22B21/0023

  from waste materials · CPC title

• C22B7/006

  Wet processes · CPC title