METHOD OF COLLECTING FIBROUS FILLING MATERIAL AND e-CAPROLACTAM, AND METHOD OF PRODUCING POLYAMIDE 6

Patent metadata

Field	Value
Publication number	US-2024352217-A1
Application number	US-202218701126-A
Country	US
Kind code	A1
Filing date	Oct 17, 2022
Priority date	Oct 29, 2021
Publication date	Oct 24, 2024
Grant date	—

Abstract

A method of collecting a fibrous filling material and ε-caprolactam includes adding a polyamide 6 resin composition (A) containing at least a fibrous filling material (D) and at least one of water (B) heated to 290° C. or higher and 350° C. or lower and a polyamide 6 oligomer aqueous solution (B1) heated to 290° C. or higher and 350° C. or lower to make contact with each other to obtain a mixture (C) containing at least the fibrous filling material (D), ε-caprolactam, a polyamide 6 oligomer, and the water (B), and collecting the fibrous filling material (D) and the ε-caprolactam from the mixture (C).

First claim

1 . A method of collecting a fibrous filling material and ε-caprolactam, comprising
adding a polyamide 6 resin composition (A) containing at least a fibrous filling material (D) and at least one of water (B) heated to 290° C. or higher and 350° C. or lower and a polyamide 6 oligomer aqueous solution (B1) heated to 290° C. or higher and 350° C. or lower to make contact with each other to obtain a mixture (C) containing at least the fibrous filling material (D), ε-caprolactam, a polyamide 6 oligomer, and the water (B), and
collecting the fibrous filling material (D) and the ε-caprolactam from the mixture (C), wherein steps (a) to (c) are performed in this order:
(a) preparing the mixture (C) by adding the polyamide 6 resin composition (A) containing the fibrous filling material (D) and at least one of the water (B) and the polyamide 6 oligomer aqueous solution (B1) to make contact with each other under a condition that a product of X and Y is 2,000 or less when a mass ratio of water to polyamide 6 or a mass ratio of water to a sum of polyamide 6 and the polyamide 6 oligomer is represented by X:1 and a reaction temperature is represented by Y° C.;
(b) subjecting the mixture (C) to a solid-liquid separation (I) in a temperature range not higher than a boiling point of water at an operation pressure; and
(c) washing a filter residue containing the fibrous filling material (D) obtained by the solid-liquid separation (I) with water having a temperature not higher than the boiling point of water at normal pressure to collect the fibrous filling material (D).

2 . The method according to claim 1 , wherein the polyamide 6 resin composition (A) containing at least the fibrous filling material (D) and the water (B) heated to 290° C. or higher and 350° C. or lower, or, the water (B) heated to 290° C. or higher and 350° C. or lower and the polyamide 6 oligomer aqueous solution (B1) heated to 290° C. or higher and 350° C. or lower are added to make contact with each other to obtain the mixture (C) containing at least the fibrous filling material (D), the ε-caprolactam, the polyamide 6 oligomer, and the water (B), and then the fibrous filling material (D) and the ε-caprolactam are collected from the mixture (C), and steps (a) to (c) are performed in this order:
(a) preparing the mixture (C) by adding the polyamide 6 resin composition (A) containing the fibrous filling material (D) and the water (B), or by adding the polyamide 6 resin composition (A) containing the fibrous filling material (D), the water (B), and the polyamide 6 oligomer aqueous solution (B1), to make contact with each other under a condition that a product of X and Y is 2,000 or less when a mass ratio of water to polyamide 6 or a mass ratio of water to a sum of polyamide 6 and the polyamide 6 oligomer is represented by X:1 and a reaction temperature is represented by Y° C.;
(b) subjecting the mixture (C) to solid-liquid separation (I) in a temperature range not higher than a boiling point of water at an operation pressure; and
(c) washing a filter residue containing the fibrous filling material (D) obtained by the solid-liquid separation (I) with water having a temperature not higher than the boiling point of water at normal pressure to collect the fibrous filling material (D).

3 . The method according to claim 1 , wherein a mass loss of the fibrous filling material (D) when the fibrous filling material (D) collected is subjected to a heating treatment in an air atmosphere at 600° C. for 3 hours is 3.0 mass % or less.

4 . The method according to claim 1 , wherein the solid-liquid separation (I) is performed in a temperature range not higher than the boiling point of water at normal pressure.

5 . The method according to claim 1 , wherein the mixture (C) containing at least the fibrous filling material (D), the ε-caprolactam, the polyamide 6 oligomer, and water is prepared, and then subsequently subjected to the solid-liquid separation (I).

6 . The method according to claim 1 , wherein the polyamide 6 oligomer aqueous solution (B1) is an extract liquid obtained in a step of extracting a polyamide 6 oligomer with hot water from polyamide 6 which is a product at a time of production of polyamide 6.

7 . The method according to claim 1 , wherein the polyamide 6 resin composition (A) containing at least the fibrous filling material (D) is a waste of a resin molded body containing polyamide 6 including at least the fibrous filling material (D).

8 . A method of producing polyamide 6, comprising obtaining ε-caprolactam by the method according to claim 1 , and polymerizing the obtained ε-caprolactam.

Assignees

• Toray Industries

Inventors

• Yamashita Kohei
• Takahashi Akihiro
• Kato Masashi
• Nishimura Mihoko
• Kato Koya

Classifications

• C07D223/10

  attached in position 2 · CPC title

• C07D201/16

  Separation or purification · CPC title

• B09B2101/75

  Plastic waste · CPC title

• B09B3/40

  involving thermal treatment, e.g. evaporation (processes using mineral binders involving a melting or softening step B09B3/29; involving radiation B09B3/50) · CPC title

• C08J2377/02

  Polyamides derived from omega-amino carboxylic acids or from lactams thereof (C08J2377/10 takes precedence) · CPC title