Aluminum-oxide-based-composition-containing zirconium nitride powder and method for producing same

Patent metadata

Field	Value
Publication number	US-2024343927-A1
Application number	US-202218683262-A
Country	US
Kind code	A1
Filing date	Aug 26, 2022
Priority date	Sep 28, 2021
Publication date	Oct 17, 2024
Grant date	—

Abstract

This aluminum-oxide-based-composition-containing zirconium nitride powder contains particles each of which is mainly composed of zirconium nitride and has a surface to which an aluminum oxide-based composition partially adheres, in which the aluminum-oxide-based-composition-containing zirconium nitride powder contains aluminum in a proportion of greater than 1% by mass and 15% by mass or less in terms of a total content of 100% by mass, and has a specific surface area of 30 m 2 /g to 90 m 2 /g measured by a BET method. This powder has relatively high light shielding properties in a near infrared region with a wavelength of 1,000 nm, has excellent patterning and visible light shielding properties, and has favorable moisture resistance, when the powder is used to form a black patterned film as a black pigment.

First claim

1 . An aluminum-oxide-based-composition-containing zirconium nitride powder comprising:
particles each of which is mainly composed of zirconium nitride and has a surface to which an aluminum oxide-based composition partially adheres, wherein the aluminum-oxide-based-composition-containing zirconium nitride powder contains aluminum in a proportion of greater than 1% by mass and 15% by mass or less in terms of a total content of 100% by mass, and has a specific surface area of 30 m 2 /g to 90 m 2 /g measured by a BET method.

2 . The aluminum-oxide-based-composition-containing zirconium nitride powder according to claim 1 ,
wherein in a case where a dispersion is prepared so that a concentration of the aluminum-oxide-based-composition-containing zirconium nitride powder is 50 ppm, and a transmission spectrum of the dispersion is measured, a light transmittance X at 370 nm is 20% or greater, a light transmittance Y at 1,000 nm is 35% or less, and a ratio (X/Y) of the light transmittance X at 370 nm to the light transmittance Y at 1,000 nm is 1.2 or greater.

3 . A method for producing the aluminum-oxide-based-composition-containing zirconium nitride powder according to claim 1 , the method comprising:
mixing a zirconium oxide powder with an aluminum-containing powder at a molar ratio of the aluminum-containing powder of 0.05 to 0.8 per mole of the zirconium oxide powder, a metallic magnesium powder at a molar ratio of the metallic magnesium powder of 2.0 to 6.0 per mole of the zirconium oxide powder, and a magnesium oxide powder at a molar ratio of the magnesium oxide powder of 0.3 to 5.0 per mole of the zirconium oxide powder to obtain a mixture; and firing the mixture at a temperature of higher than 900° C. and 1,100° C. or less for 60 minutes to 180 minutes in a nitrogen gas atmosphere to reduce the zirconium oxide powder.

4 . The method for producing the aluminum-oxide-based-composition-containing zirconium nitride powder according to claim 3 ,
wherein the aluminum-containing powder is a powder composed of any one or more of metallic aluminum, alumina, an aluminate compound, or aluminum hydroxide.

5 . A black dispersion that is formed by dispersing the aluminum-oxide-based-composition-containing zirconium nitride powder according to claim 1 in a solvent or a monomer compound.

6 . A black photosensitive composition comprising the aluminum-oxide-based-composition-containing zirconium nitride powder according to claim 1 as a black pigment.

7 . A black patterned film that is obtained by using the black photosensitive composition according to claim 6 .

8 . A black matrix that is obtained by using the black patterned film according to claim 7 .

9 . A light shielding material that is obtained by using the black patterned film according to claim 7 .

10 . A light shielding filter that is obtained by using the black patterned film according to claim 7 .

11 . A black film comprising a support film and the black patterned film according to claim 7 on the support film.

Assignees

• Mitsubishi Mat Electronic Chemicals Co Ltd
• Mitsubishi Materials Corp

Inventors

• Kageyama Kensuke
• SHIYAMA Takuya
• Aiba Naoyuki
• TAGUCHI Riho
• Akaike Hiroto
• Chitose Norihisa

Classifications

• C01P2004/04

  obtained by TEM, STEM, STM or AFM · CPC title

• C01P2002/84

  by UV- or VIS- data · CPC title

• G02B5/208

  for use with infrared or ultraviolet radiation, e.g. for separating visible light from infrared and/or ultraviolet radiation · CPC title

• G02B5/003

  Light absorbing elements · CPC title

• C09D133/04

  Homopolymers or copolymers of esters {(C09D143/04 takes precedence)} · CPC title