Electrolytic polishing treatment method for nickel-based alloy workpiece

Patent metadata

Field	Value
Publication number	US-2024191388-A1
Application number	US-202318531721-A
Country	US
Kind code	A1
Filing date	Dec 7, 2023
Priority date	Dec 7, 2022
Publication date	Jun 13, 2024
Grant date	—

Abstract

An electrolytic polishing treatment method for a nickel-based alloy workpiece made by lamination manufacturing comprises the following steps. Step (A) comprises performing a sandblasting treatment on the nickel-based alloy workpiece, followed by ultrasonic oscillation of the sandblasted nickel-based alloy workpiece in an oxalic acid solution. Step (B) comprises placing the nickel-based alloy workpiece in an electrolyte solution containing methanol, sulfuric acid, and perchloric acid and performing electrolytic polishing on the nickel-based alloy workpiece at a constant voltage after step (A). The processes of oxalic acid activation and electrolytic polishing are used to avoid the problems of residual stress and processing directionality caused by conventional mechanical processing and make the surface properties of the entire workpiece uniform.

First claim

What is claimed is:

1 . An electrolytic polishing treatment method of a nickel-based alloy workpiece made by lamination manufacturing comprises:
(A) performing a sandblasting treatment on the nickel-based alloy workpiece, followed by ultrasonic oscillation of the nickel-based alloy workpiece in an oxalic acid solution; and (B) placing the nickel-based alloy workpiece in an electrolyte solution containing methanol, sulfuric acid, and perchloric acid and performing electrolytic polishing on the nickel-based alloy workpiece at a constant voltage after step (A).

2 . The electrolytic polishing treatment method of a nickel-based alloy workpiece of claim 1 , wherein the sandblasting treatment in step (A) uses emery.

3 . The electrolytic polishing treatment method of a nickel-based alloy workpiece of claim 1 , wherein the oxalic acid solution in step (A) has a concentration of 5 to 15 vol %.

4 . The electrolytic polishing treatment method of a nickel-based alloy workpiece of claim 1 , wherein the ultrasonic oscillation in step (A) has an operation time of 5 to 10 minutes, an operation temperature of 20 to 30° C., and an oscillation frequency of 30 to 50 kHz.

5 . The electrolytic polishing treatment method of a nickel-based alloy workpiece of claim 1 , wherein the electrolyte solution of step (B) comprises 80 vol % or more of methanol, 4.5 vol % or more of sulfuric acid, and 12 vol % or more of perchloric acid.

6 . The electrolytic polishing treatment method of a nickel-based alloy workpiece of claim 1 , wherein in the electrolyte solution of step (B), a volume ratio of methanol:sulfuric acid:perchloric acid is 18:1:3.

7 . The electrolytic polishing treatment method of a nickel-based alloy workpiece of claim 1 , wherein the constant voltage of step (B) has a range of 10 to 15V.

8 . The electrolytic polishing treatment method of a nickel-based alloy workpiece of claim 1 , wherein the electrolytic polishing of step (B) has a reaction time of 15 to 20 minutes and an operation temperature of 0 to 30° C.

9 . The electrolytic polishing treatment method of a nickel-based alloy workpiece of claim 1 , wherein materials of the nickel-based alloy workpiece comprise a nickel-based powder and modified powder thereof.

10 . The electrolytic polishing treatment method of a nickel-based alloy workpiece of claim 1 , wherein the nickel-based alloy workpiece is in a heat-treated state or a rough blank state resulting from lamination manufacturing.

Assignees

• Nat Chung Shan Inst Science & Tech

Inventors

• Kao Chun-Hsiang
• Ferng Yi-Cherng
• Huang Ying-Sun
• Jen Kuo-Kuang
• Jian Shun-Yi
• Lee Chia-Yu
• Hung Jung-Chou
• Yang Po-Jen

Classifications

• C25F3/02

  Etching · CPC title

• B01J19/10

  employing sonic or ultrasonic vibrations · CPC title

• C25F3/22 Primary

  of heavy metals · CPC title

• B24C1/08 Primary

  for polishing surfaces, e.g. {smoothing a surface} by making use of liquid-borne abrasives · CPC title