Cathode active material, method for its manufacture, and use

Patent metadata

Field	Value
Publication number	US-2024006601-A1
Application number	US-202118036828-A
Country	US
Kind code	A1
Filing date	Nov 5, 2021
Priority date	Nov 13, 2020
Publication date	Jan 4, 2024
Grant date	—

Abstract

Process for making a composite oxide according to the formula x·Li 2 Ni 1-y1-y2 Mn y1 M 1 y2 O 3 ·(1−x)·LiNi 1-z M 2 z O 2 wherein x is in the range of from 0.01 to 0.5, z is in the range of from zero to 0.5,
M 1 is selected from Ti, Zr, Sn, Ge, Ta, Nb, Sb, W, and Mo, and combinations of at least two of the foregoing, M 2 is at least one of Co, Al, Mg, Fe, or Mn, or a combination of at least two of the foregoing,

0.1≤ y 1≤0.75, zero≤ y 2≤0.05,

said process comprising the following steps:
(a) providing a particulate hydroxide, oxide or oxyhydroxide of TM where TM has the general formula x·Ni 1-y1-y2 Mn y1 M 1 y ·(1−x)Ni 1-z M 2 z , or the respective species without M 1 and/or M 2 , (b) adding a source of lithium, (c) treating the mixture obtained from step (b) thermally under an atmosphere comprising oxygen in two steps:
(c) heating the mixture obtained from step (b) to 680 to 800° C. in an atmosphere containing in the range of from 10 to 100 vol-% oxygen, and, (e) heating the intermediate from step (c) to 450 to 580° C. in an atmosphere containing at least 90 vol-% oxygen.

First claim

1 .- 14 . (canceled)

15 . Process for making a cobalt-free composite oxide according to the formula x·Li 2 Ni 1-y Mn y O 3 ·(1−x)·LiNiO 2 wherein x is in the range of from 0.1 to 0.5, 0.1≤y≤0.75, said process comprising the following steps:
(a) providing a particulate hydroxide, oxide or oxyhydroxide of TM where TM has the general formula x·Ni 1-y Mn y ·(1−x)Ni,
(b) adding a source of lithium and, optionally, at least one oxide, hydroxide, or oxyhydroxide of Mn, in a molar ratio of Li:(Ni+Mn) of from 0.9:1 to 1.1:1,
(c) heating the mixture obtained from step (b) to 680 to 800° C. in an atmosphere containing oxygen,
(d) adding source of lithium, and
(e) heating the mixture obtained from step (d) to 450 to 580° C. in an atmosphere containing at least 90 vol % oxygen.

16 . Process according to claim 15 wherein 0.15≤y≤0.6.

17 . Process according to claim 15 wherein steps (c) (and (e) are performed under a forced flow of gas.

18 . Process according to claim 15 wherein the source of lithium is selected from lithium hydroxide, lithium carbonate, lithium nitrate, and lithium oxide.

19 . Process according to claim 15 wherein x is in the range of from 0.1 to 0.3.

20 . Process according to claim 15 wherein said process comprises an additional step (f) subsequent to step (e), and wherein said step (f) is selected from coating steps and wet treatment steps.

21 . Particulate cobalt-free composite oxide of the composition x·Li 2 Ni 1-y Mn y O3·(1−x)·LiNiO 2 wherein x is in the range of from 0.01 to 0.5, 0.1≤y≤0.75.

22 . Particulate composite oxide according to claim 21 wherein 0.15≤y≤0.6.

23 . Particulate composite oxide according to claim 21 wherein x is in the range of from 0.1 to 0.3.

24 . Particulate composite oxide according to claim 21 wherein cations in both the Li 2 Ni 1-y Mn y O 3 and the LiNiO 2 domains exhibit a substantially layered ordering, where the Li 2 Ni 1-y Mn y O 3 domains display alternating Li and Li 1/3 [Ni 1-y Mn y ]⅔ cation layers, and the LiNiO 2 domains display alternating Ni and Li cation layers, and wherein Li 1/3 [Ni 1-y Mn y ]⅔ cation layers in the Li 2 Ni 1-y Mn y O 3 domains exhibit substantially a honeycomb-type cation ordering wherein the Li cations have no other Li cations as their nearest cation neighbors within the same cation layer.

25 . Cathode comprising
(A) at least one particulate composite oxide according to claim 21 , (B) carbon in electrically conductive form, (C) at least one binder.

26 . Electrochemical cell comprising a cathode according to claim 25 .

Assignees

• Basf Se
• Univ Leland Stanford Junior

Inventors

• Teufl Tobias Maximilian
• Lampert Jordan K
• Sommer Heino
• Chueh William C
• Gent William E

Classifications

• H01M4/505 Primary

  of mixed oxides or hydroxides containing manganese for inserting or intercalating light metals, e.g. LiMn2O4 or LiMn2OxFy · CPC title

• H01M4/525

  of mixed oxides or hydroxides containing iron, cobalt or nickel for inserting or intercalating light metals, e.g. LiNiO2, LiCoO2 or LiCoOxFy · CPC title

• H01M4/131 Primary

  Electrodes based on mixed oxides or hydroxides, or on mixtures of oxides or hydroxides, e.g. LiCoOx · CPC title

• C01G53/56 Primary

  of the type (MnO3)2-, e.g. Li2(NixMn1-x)O3 or Li2(MyNixMn1-x-y)O3 · CPC title

• H01M2004/028

  Positive electrodes · CPC title