Abstract

A method for producing a carbon dioxide-containing hydrogel article including (1) to (3). (1) Preparing an article including a hydrogel that contains a water-soluble polymer, a cross-linking agent for the water-soluble polymer, and water, wherein a loss tangent of the hydrogel at 1 Hz in dynamic viscoelasticity measurement is 0.46 or greater. (2) Adjusting a composition of an ambient atmosphere of the article including the hydrogel such that a carbon dioxide gas concentration in the ambient atmosphere becomes 10 vol% or greater, and sealing the article including the hydrogel inside a package. (3) Making cross-linking of the hydrogel proceed until the loss tangent, at 1 Hz in dynamic viscoelasticity measurement, of the hydrogel in the article including the hydrogel becomes less than 0.46, and thereby obtaining a carbon dioxide-containing hydrogel article sealed inside the package.

First claim

1 . A method for producing a carbon dioxide-containing hydrogel article, the method comprising (1) to (3) below:
(1) preparing an article including a hydrogel that contains (A) a water-soluble polymer, (B) a cross-linking agent for the water-soluble polymer, and (C) water, a loss tangent of the hydrogel at 1 Hz in dynamic viscoelasticity measurement being 0.46 or greater; (2) while the loss tangent, at 1 Hz in dynamic viscoelasticity measurement, of the hydrogel in the article including the hydrogel is 0.46 or greater,
adjusting a composition of an ambient atmosphere of the article including the hydrogel such that a carbon dioxide gas concentration in the ambient atmosphere becomes 10 vol% or greater,
sealing the article including the hydrogel inside a package; and
(3) making cross-linking of the hydrogel proceed until the loss tangent, at 1 Hz in dynamic viscoelasticity measurement, of the hydrogel in the article including the hydrogel becomes less than 0.46, and thereby obtaining a carbon dioxide-containing hydrogel article sealed inside the package.

2 . The method for producing a carbon dioxide-containing hydrogel article according to claim 1 , wherein (2) is performed at atmospheric temperature and atmospheric pressure.

3 . The method for producing a carbon dioxide-containing hydrogel article according to claim 1 , wherein:
the water-soluble polymer contains an anionic polymer; and the cross-linking agent contains an aluminum ion-supplying cross-linking agent.

4 . The method for producing a carbon dioxide-wherein (2) further comprises:
arranging the article including the hydrogel between an air-impermeable first original sheet and an air-impermeable second original sheet and supplying a carbon dioxide-containing gas between the first and second original sheets, and in this state, first joining both lateral sides of the first and second original sheets which are being transported in a single direction, the lateral sides extending along the transporting direction; second joining the first and second original sheets together in a direction intersecting with the transporting direction at a position where the article including the hydrogel is not present, to thereby form a continuous package in which the article including the hydrogel and the carbon dioxide-containing gas are enclosed; and cutting the continuous package in a direction intersecting with the transporting direction at a region joined by the second joining, to thereby form the package.

5 . The method for producing a carbon dioxide-wherein, in (2), the loss tangent of the hydrogel is 0.48 or greater and 0.90 or less.

6 . The method for producing a carbon dioxide-containing hydrogel article according to claim 1 , wherein (1) further comprises mixing the water-soluble polymer, the cross-linking agent, and the water at atmospheric pressure, to thereby prepare the hydrogel including bubbles.

7 . The method for producing a carbon dioxide-containing hydrogel article according to claim 1 , wherein, in (2), while the loss tangent is 0.46 or greater, the composition of the ambient atmosphere is adjusted such that the carbon dioxide gas concentration in the ambient atmosphere of the article including the hydrogel becomes 10 vol% or greater.

8 . The method for producing a carbon dioxide-containing hydrogel article according to claim 1 , wherein, in (2), an operation of housing the article including the hydrogel inside the package and an operation of supplying a carbon dioxide-containing gas into the package are performed in this order, or performed in reverse order, or performed simultaneously, and then the package is sealed.

9 . The method for producing a carbon dioxide-containing hydrogel article according to claim 1 , wherein, in (3), the carbon dioxide-containing hydrogel article sealed inside the package is obtained by making cross-linking of the hydrogel proceed until the loss tangent becomes less than 0.40.

10 . The method for producing a carbon dioxide-containing hydrogel article according to claim 1 , wherein:
(3) is performed at atmospheric temperature; and in (3), the time required until the loss tangent becomes less than 0.46 is from 24 to 366 hours from when the hydrogel article is sealed inside the package.

11 . The method for producing a carbon dioxide-containing hydrogel article according to claim 1 , wherein, in (3), cross-linking of the hydrogel is allowed to proceed until the loss tangent is from 0.20 to 0.45.

12 . The method for producing a carbon dioxide-containing hydrogel article according to claim 1 , wherein (1) further comprises applying a prepared hydrogel onto a support, and forming, on the support, the article including the hydrogel.

13 . The method for producing a carbon dioxide-containing hydrogel article according to claim 6 , wherein a time for mixing the water-soluble polymer, the cross-linking agent, and the water is from 1 to 60 minutes.

14 . The method for producing a carbon dioxide-containing hydrogel article according to claim 6 , wherein a stirring speed for mixing the water-soluble polymer, the cross-linking agent, and the water is from 10 to 80 rpm.

15 . The method for producing a carbon dioxide-containing hydrogel article according to claim 1 , wherein the water-soluble polymer is an anionic polymer.

16 . The method for producing a carbon dioxide-containing hydrogel article according to claim 15 , wherein the anionic polymer includes a carboxyl group, a sulfuric acid group, or a phosphoric acid group.

17 . The method for producing a carbon dioxide-containing hydrogel article according to claim 1 , wherein the cross-linking agent is a metal ion compound, a cationic polymer, or a polyfunctional epoxy compound.

18 . The method for producing a carbon dioxide-containing hydrogel article according to claim 17 , wherein:
the cross-linking agent is a metal ion compound; and the metal ion compound is an oxide, a hydroxide, or a salt including aluminum, magnesium, calcium, or potassium.

19 . The method for producing a carbon dioxide-containing hydrogel article according to claim 1 , wherein a charging amount of the water in the hydrogel is from 20 to 95 mass%.

Assignees

• Kao Corp

Inventors

• Kimura Shohei

Classifications

• B65B61/06

  by cutting · CPC title

• A61K33/00 Primary

  Medicinal preparations containing inorganic active ingredients · CPC title

• B65B31/021

  the containers or wrappers being interconnected · CPC title

• B65B9/042 Primary

  for fluent material · CPC title

• A61K9/06

  Ointments; Bases therefor; {Other semi-solid forms, e.g. creams, sticks, gels (composition of ointments, creams or gels A61K47/00)} · CPC title