Preparation method for metal material

Patent metadata

Field	Value
Publication number	US-2022402012-A1
Application number	US-202217894124-A
Country	US
Kind code	A1
Filing date	Aug 23, 2022
Priority date	Dec 11, 2020
Publication date	Dec 22, 2022
Grant date	—

Abstract

The present invention discloses a preparation method for a metal material, including: horizontally placing a to-be-prepared metal material between wavy surfaces of a female die and a male die; connecting a press machine with the male die; pressing the metal material through the male die, so that the metal material makes complete contact with the male die and the female die; ejecting the pressed metal material; horizontally overturning the metal material, and then placing the metal material between the wavy surfaces of the female die and the male die; repeatedly performing the pressing and overturning processes until accumulated strain of the metal material meets a requirement; and taking out the metal material after the deformed metal material is flattened by a plane die. According to the present invention, a large-size nano grained material can be manufactured.

First claim

What is claimed is:

1 . A preparation method for a metal material, comprising:
horizontally placing a to-be-prepared metal material between wavy surfaces of a female die and a male die; starting a press machine which is connected to the male die, and pressing the metal material through the male die, so that the metal material makes complete contact with the male die and the female die; ejecting the pressed metal material, horizontally overturning the metal material, and then placing the metal material between the wavy surfaces of the female die and the male die; repeatedly performing the pressing process, ejecting a re-pressed metal material, horizontally overturning the re-pressed metal material again, then, placing the re-pressed metal material between the wavy surfaces of the female die and the male die, and repeatedly performing the pressing and overturning processes until accumulated strain of the metal material meets a requirement; and taking out the metal material after the deformed metal material is flattened by a plane die.

2 . The preparation method for the metal material according to claim 1 , wherein the male die and the female die are made of die steel, and the metal material includes pure metal or an alloy.

3 . The preparation method for the metal material according to claim 1 , wherein wavy surface features of the male die and the female die are staggered from each other, and the male die is completely attached to the female die.

4 . The preparation method for the metal material according to claim 3 , wherein the wavy surface features comprise a wave form height (h), a wave form width (w) and a feature radian.

5 . The preparation method for the metal material according to claim 4 , wherein strain accumulated after one-time pressing is in positive correlation with the feature radian.

6 . The preparation method for the metal material according to claim 5 , wherein an upper limit of a thickness of the to-be-prepared metal material is in positive correlation with the wave form height (h) and the wave form width (w).

7 . The preparation method for the metal material according to claim 1 , wherein the male die and the female die can be exchanged for use; and during repeated pressing, peak parts of the metal material make contact with peak parts of the male die and the female die.

8 . The preparation method for the metal material according to claim 2 , wherein the male die and the female die can be exchanged for use; and during repeated pressing, peak parts of the metal material make contact with peak parts of the male die and the female die.

9 . The preparation method for the metal material according to claim 3 , wherein the male die and the female die can be exchanged for use; and during repeated pressing, peak parts of the metal material make contact with peak parts of the male die and the female die.

10 . The preparation method for the metal material according to claim 4 , wherein the male die and the female die can be exchanged for use; and during repeated pressing, peak parts of the metal material make contact with peak parts of the male die and the female die.

11 . The preparation method for the metal material according to claim 5 , wherein the male die and the female die can be exchanged for use; and during repeated pressing, peak parts of the metal material make contact with peak parts of the male die and the female die.

12 . The preparation method for the metal material according to claim 6 , wherein the male die and the female die can be exchanged for use; and during repeated pressing, peak parts of the metal material make contact with peak parts of the male die and the female die.

Assignees

• Univ Shanghai Jiaotong

Inventors

• Chen Fei
• Wu Guangshan
• Cui Zhenshan
• Zhang Jiao
• Sun Baode

Classifications

• B21D13/10 Primary

  into a peculiar profiling shape · CPC title

• B21C23/001 Primary

  to improve the material properties, e.g. lateral extrusion · CPC title

• B21C25/02

  Dies · CPC title

• B21D13/02

  by pressing · CPC title