Tool part suitable to be used in humid environment

Patent metadata

Field	Value
Publication number	US-2022347828-A1
Application number	US-202017638936-A
Country	US
Kind code	A1
Filing date	Aug 27, 2020
Priority date	Aug 30, 2019
Publication date	Nov 3, 2022
Grant date	—

Abstract

The present invention relates to a tool part comprising a polymer composition. The tool part is suitable to be used in direct contact with water and/or in an environment with relative humidity equal to or higher than 55%. The present invention further relates to a process for the preparation of the tool part. The present invention also relates to a process for the preparation of the tool part. The present invention further relates to the use of the polymer composition for the preparation of the tool part.

First claim

1 . A tool part comprising a polymer composition, wherein the polymer composition comprises a polymer and reinforcing fiber, wherein the number average length of the reinforcing fiber is in the range of 0.80 to 11.1 mm, wherein the polymer in the polymer composition is a polypropylene, wherein the melt flow index (MFI) of the polypropylene is in the range of 30 to 100 dg/min according to ISO 1133:2011 at 230° C. with 2.16 kg load, wherein the density of the tool part is in the range from 1.08 to 2.51 g/cm 3 as measured according to ISO 1183-1:2019.

2 . The tool part according to claim 1 , wherein the amount of the reinforcing fiber is in the range from 10 wt % to 50 wt % based on the total amount of the polymer composition.

3 . The tool part according to claim 1 , wherein the number average length of the reinforcing fiber in the polymer composition is in the range of 2.0 to 10.5 mm.

4 . The tool part according to claim 1 , wherein the reinforcing fiber is an inorganic fiber.

5 . The tool part according to claim 1 , wherein the amount of the polymer composition in the tool part is at least 50 wt % based on the total amount of the tool part.

6 . The tool part according to claim 1 , wherein the retention of tensile strength of the polymer composition is at least 0.70, wherein the retention of tensile strength is the ratio between tensile strength tested on specimen conditioned for 48 hrs at 23° C. at 50% relative humidity and tensile strength tested on specimen conditioned for 48 hrs at 40° C. at 85% relative humidity tested according to ISO 527-2:2012 at room temperature (23° C.).

7 . The tool part according to claim 1 , wherein the tensile modulus of the polymer composition is at least 5350 MPa tested at 23° C. according to ISO 527-2:2012, wherein the test specimens of the polymer composition is conditioned at 40° C. at 85% relative humidity for 48 hrs.

8 . The tool part according to claim 1 , wherein the impact resistance of the polymer composition is at least 20 KJ/m 2 tested at 23° C. according to ISO 179-1:2010, wherein the test specimens of the polymer composition is conditioned at 40° C. at 85% relative humidity for 48 hrs.

9 . The tool part according to claim 1 wherein the polymer composition characterizes in that it satisfies the following inequation:

Tensile
⁢

modulus

1000

+

20

Retention
⁢

of
⁢

tensile
⁢

strength

>

Impact
⁢

resistance

Average
⁢

fiber
⁢

length

wherein specimens used to determine the tensile modulus are conditioned at 40° C. at 85% relative humidity for 48 h prior to be tested according to ISO 527-2:2012 at 23° C.; specimens used to determine impact resistance are conditioned at 40° C. at 85% relative humidity for 48 h prior to be tested according to ISO 179-1:2010 at 23° C.; average fiber length refers to the number average length of the fiber in the polymer composition.

10 . The tool part according to claim 1 , wherein the amount of polar moiety of the polymer in the polymer composition is at most 40 wt % based on the total amount of the polymer.

11 . The tool part according to claim 1 , wherein the polymer in the polymer composition is a polypropylene homopolymer.

12 . The tool part according to claim 1 , wherein the tool is an electric drill, a hammer, a shovel, or a lawn mower.

13 . A process for the preparation of the tool part according to claim 1 , comprising the step of injection moulding the polymer composition to obtain the tool part.

14 . (canceled)

15 . A method of using the tool of claim 1 , comprising using the tool in direct contact with water or in an environment with relative humidity higher than 55%.

Assignees

• Sabic Global Technologies Bv

Inventors

• Wen Liang
• Kong Xin
• Chen Steve
• Gao Winson
• Jiang Chaodong

Classifications

• C08K7/14

  Glass · CPC title

• B25F5/02 Primary

  Construction of casings, bodies or handles {(B25F5/006, B25F5/008 take precedence)} · CPC title

• B29K2023/12

  PP, i.e. polypropylene · CPC title

• B25G1/10

  characterised by material or shape (B25G1/01, B25G1/02 take precedence {; for hand tools comprising coating rollers B05C17/0205}) · CPC title

• B29C45/0005

  using fibre reinforcements · CPC title