Lithium nickel manganese cobalt composite oxide as a positive electrode active material for rechargeable lithium ion batteries

Patent metadata

Field	Value
Publication number	US-2022271275-A1
Application number	US-202017623694-A
Country	US
Kind code	A1
Filing date	Jul 2, 2020
Priority date	Jul 3, 2019
Publication date	Aug 25, 2022
Grant date	—

Abstract

A positive electrode active material powder suitable for lithium-ion batteries, comprising lithium transition metal-based oxide particles, said particles comprising a core and a surface layer, said surface layer being on top of said core, said particles comprising the elements: Li, a metal M′ and oxygen, wherein the metal M′ has a formula: M′=(Ni z (Ni 0.5 Mn 0.5 ) y Co x ) 1-k A k , wherein A is a dopant, 0.60≤z≤0.86, 0.05≤y≤0.20, 0.05≤x≤0.20, x+y+z+k=1, and k≤0.01, said positive electrode active material powder having a median particle size D50 ranging from 5 μm to 15 μm and a surface layer thickness ranging from 10 nm to 200 nm,
said surface layer comprising:
sulfur in a content superior or equal to 0.150 wt % and inferior or equal to 0.375 wt % with respect to the total weight of the positive electrode active material powder, and aluminum in a content superior or equal to 0.05 wt % and inferior or equal to 0.15 wt % with respect to the total weight of the positive electrode active material powder,

said surface layer of lithium transition metal-based oxide particles comprising a LiAlO 2 phase and an LiM″ 1-a Al a O 2 phase with M″ comprising: Ni, Mn, and Co, said LiAlO 2 phase being present in the surface layer in a content superior or equal to 0.10 at % and inferior or equal to 0.30 at % with respect to the total atomic content of M′ in the positive electrode active material powder, said LiM″ 1-a Al a O 2 phase being present in the surface layer in a content inferior to 0.14 at % with respect to the total atomic content of M′ in the positive electrode active material powder.

First claim

1 - 16 . (canceled)

17 . A positive electrode active material powder suitable for lithium-ion batteries, comprising lithium transition metal-based oxide particles, said particles comprising a core and a surface layer, said surface layer being on top of said core, said particles comprising the elements: Li, a metal M′ and oxygen, wherein the metal M′ has a formula: M′=(Ni z Mn y Co x ) 1-k A k , wherein A is a dopant, 0.60≤z<0.86, 0.05≤x≤0.20, x+y+z+k=1, and k≤0.01, said positive electrode active material powder having a median particle size D50 ranging from 5 μm to 15 μm and a surface layer thickness ranging from 10 nm to 200 nm,
said surface layer comprising:
sulfur in a content superior or equal to 0.150 wt % and inferior or equal to 0.375 wt % with respect to the total weight of the positive electrode active material powder, and
aluminum in a content superior or equal to 0.05 wt % and inferior or equal to 0.15 wt % with respect to the total weight of the positive electrode active material powder,

said surface layer of lithium transition metal-based oxide particles comprising a LiAlO 2 phase and an LiM″ 1-a Al a O 2 phase with M″ comprising: Ni, Mn, and Co, said LiAlO 2 phase being present in the surface layer in a content superior or equal to 0.10 at % and inferior or equal to 0.30 at % with respect to the total atomic content of M′ in the positive electrode active material powder, said LiM″ 1-a Al a O 2 phase being present in the surface layer in a content inferior to 0.14 at % with respect to the total atomic content of M′ in the positive electrode active material powder.

18 . The positive electrode active material powder according to claim 17 , wherein said particles comprises the elements: Li, M′ and oxygen, wherein M′ has a formula:
M′=Ni z Mn y Co x A k , wherein A is a dopant, 0.70≤z≤0.86, 0.05≤y≤0.20, 0.05≤x≤0.20, x+y+z+k=1, and k≤0.01.

19 . The positive electrode active material powder according to claim 17 , wherein said lithium transition metal-based oxide particles have an Al surface coverage A1/A2 that is superior or equal to 100, wherein A1 is an atomic ratio Al/(Ni+Mn+Co+Al+S) of the elements Al, Ni, Mn, Co, and S contained in the surface layer, said atomic ratio Al being obtained by XPS spectrum analysis and wherein A2 is an atomic ratio Al/(Ni+Mn+Co+Al+S) obtained by ICP.

20 . The positive electrode active material powder according to claim 17 , having a carbon content of less than 200 ppm.

21 . The positive electrode active material powder according to claim 17 , having a Li/(Ni+Mn+Co+A) atomic ratio or a Li/(Ni+Mn+Co+A+Al) atomic ratio superior or equal to 0.96 and inferior or equal to 1.05.

22 . The positive electrode active material powder according to claim 19 , wherein said surface layer exhibits an Al2p peak with a maximum peak intensity in the binding energies range from 73.0±0.2 eV to 74.5±0.2 eV, said intensity being obtained by XPS spectrum analysis.

23 . The positive electrode active material powder according to claim 17 , wherein said surface layer of lithium transition metal-based oxide particles have sulfate ion (SO 4 2− ) in a content superior or equal to 4500 ppm and inferior or equal to 11250 ppm.

24 . The positive electrode active material powder according to claim 17 , wherein said lithium transition metal-based oxide particles have a sulfate ion surface coverage S1/S2 that is superior to 0.85 and inferior or equal to 1.00, wherein S1 is an amount of sulfate ion contained in the surface layer, and wherein S2 is a total amount of sulfate ion in the particles.

25 . The positive electrode active material powder according to claim 17 , having a general formula: Li 1+a′ ((Ni z′ M y′ Co x′ Al v S w ) 1-k A k ) 1-a O 2 , wherein only A is a dopant, 0.60≤z′<0.86, 0.05≤y′≤0.20, 0.05≤x′≤0.20, and x′+y′+z′+v+w+k=1, 0.0018≤v≤0.0053, 0.006≤w≤0.012, −0.05≤a′≤0.05, and k≤0.01.

26 . The positive electrode active material powder according to claim 17 , wherein A comprises one or more of Al, B, S, Mg, Zr, Nb, W, Si, Ba, Sr, Ca, Zn, Cr, V, Y, or Ti, and wherein the amount of each of the elements of A is superior to 100 ppm with respect to the total weight of the positive electrode active material powder.

27 . The positive electrode active material powder according to claim 17 , wherein the thickness of the surface layer corresponds to a minimal distance D defined either as:
D (in nm)= L S1 −L S2 , wherein L S1 is a first point location at the center of a particle, L S2 is a second point location in a line defined between said first point location and a geometric center of said particle, wherein a content of S is measured by TEM-EDS at the second point location L S2 is superior or equal to 0 at % and inferior or equal to 5.0 at % of a content of S measured at the first point location, said second content of S (S 2 ) being defined as:
S 2 (in at %)= S 3 ±0.1 at %,

S 3 being a content of S (in at %) at a third point location (LS 3 ) in said line, said third point being located at any location between the geometric center of said particle and the second point location L S2 .

28 . The positive electrode active material powder according to claim 27 , wherein:
S 1 −S 2 ≥10.0 at %

29 . The positive electrode active material powder according to claim 27 , wherein Al is present in the surface layer in a content 1 defined as:

l
⁢

(

mol
⁢

%

)

=

(

Al

M
*

)

ICP

×

(

A
⁢

l
surface

/
A

⁢

l
total

)

with:

(

Al

M
*

)

ICP

is the atomic ratio of Al content on M* content in the powder measured by ICP, and

Al
surface

/

Al
total

=

4
3

⁢

Assignees

• Umicore Nv
• Umicore Korea Ltd

Inventors

• Blangero Maxime
• Jung Kyungsub
• Yun Bin-Na
• Karakulina Olesia

Classifications

• C01P2006/40

  Electric properties · CPC title

• H01M4/362 Primary

  Composites · CPC title

• H01M4/364

  as mixtures · CPC title

• C01P2004/51

  Particles with a specific particle size distribution · CPC title

• H01M4/525 Primary

  of mixed oxides or hydroxides containing iron, cobalt or nickel for inserting or intercalating light metals, e.g. LiNiO2, LiCoO2 or LiCoOxFy · CPC title