Autoclaved cement compositions

Patent metadata

Field	Value
Publication number	US-2022220035-A1
Application number	US-202017607356-A
Country	US
Kind code	A1
Filing date	Apr 29, 2020
Priority date	Apr 29, 2019
Publication date	Jul 14, 2022
Grant date	—

Abstract

The use of calcium aluminate cement in autoclaved cement products, cementitious compositions suitable for forming the autoclaved cement products, and methods for making the cementitious compositions and autoclaved cement products.

First claim

1 . A cementitious composition comprising, based on the total dry weight of the cementitious composition:
from about 0.25 wt % to less than about 50 wt % of a calcium aluminate cement; and from about 20 wt % to about 60 wt % of one or more other hydraulic binders.

2 . The cementitious composition of claim 1 , wherein the cementitious composition further comprises:
from about about 15 wt % to about 80 wt % of one or more granular materials; and/or from about 0.5 wt % to about 10 wt % of one or more reinforcing fibres; and/or from about 0.01 wt % to about 2 wt % of one or more blowing agents; and/or from about 0.5 wt % to about 8 wt % of one or more tobermorite modifiers.

3 . The cementitious composition of claim 1 , wherein the calcium aluminate cement comprises CA 2 , wherein C is CaO and A is Al 2 O 3 .

4 . The cementitious composition of claim 1 , wherein the calcium aluminate cement comprises C 2 AS, wherein C is CaO, A is Al 2 O 3 , and S is SiO 2 .

5 . The cementitious composition of claim 1 , wherein the calcium aluminate cement comprises equal to or greater than about 80 wt % total CA 2 and C 2 AS, based on the total dry weight of the calcium aluminate cement, wherein C is CaO, A is Al 2 O 3 , and S is SiO 2 .

6 . The cementitious composition of claim 1 , wherein the calcium aluminate cement comprises one or more of C, CA, CA 6 , C 3 A, C 4 A 3 $, C 12 A 7 , CAS 2 , CS, C 2 S, C 3 S, C 3 S 2 , A 3 S 2 , C 4 AF, and C 2 A 1-y F y , wherein C is CaO, A is Al 2 O 3 , S is SiO 2 , $ is SO 3 , F is Fe 2 O 3 , and y is 0 to 1.

7 . The cementitious composition of claim 1 , wherein the one or more other hydraulic binders is selected from Portland cement, fly ash, pozzolanic ash, blast furnace slag, silica flour, silica fume, metakaolin, lime (including, for example, slaked lime), basalt, alumino silicate, pozzolan, or a combination thereof.

8 . The cementitious composition of claim 2 , wherein the granular materials are selected from quartz, sand, limestone, gypsum, siliceous sand, or a combination thereof.

9 . The cementitious composition of claim 2 , wherein the one or more reinforcing fibres are selected from cellulose fibres, cellulose pulp, glass fibres, carbon fibres, polymeric fibres, and combinations thereof.

10 . The cementitious composition of any claim 2 , wherein the one or more blowing agents is aluminium.

11 . A method for making a product, the method comprising autoclaving the cementitious composition of claim 1 , wherein the product is a fibre cement board, an autoclaved aerated concrete (AAC), or another autoclaved cement product.

12 . The method of claim 11 , wherein the method comprises curing the cementitious composition prior to autoclaving and/or wherein the method comprises mixing the cementitious composition with water prior to autoclaving and/or prior to curing.

13 . An autoclaved cement product, obtained by and/or obtainable by the method of claim 11 .

14 . (canceled)

15 . (canceled)

16 . The cementitious composition of claim 1 , wherein the cementitious composition further comprises:
from about 15 wt % to about 70 wt % of one or more granular materials; from about 0.5 wt % to about 10 wt % of one or more reinforcing fibres; from about 0.01 wt % to about 2 wt % of one or more blowing agents; and from about 0.5 wt % to about 8 wt % of one or more tobermorite modifiers.

17 . The cementitious composition of claim 16 , wherein the calcium aluminate cement comprises from about 40 wt % to about 70 wt % CA 2 , wherein C is CaO and A is Al 2 O 3 .

18 . The cementitious composition of claim 17 , wherein the calcium aluminate cement comprises from about 15 wt % to about 45 wt % of C 2 AS, wherein C is CaO, A is Al 2 O 3 , and S is SiO 2 .

19 . The cementitious composition of claim 18 wherein the calcium aluminate cement comprises equal to or greater than about 80 wt % total CA 2 and C 2 AS, based on the total dry weight of the calcium aluminate cement.

20 . The cementitious composition of claim 16 any preceding claim,
wherein the calcium aluminate cement comprises one or more of C, CA, CA6, C3A, C4A3$, C12A7, CAS2, CS, C2S, C3S, C3S2, A3S2, C4AF, and C2A1-yFy,
wherein C is CaO, A is Al2O3, S is SiO2, $ is SO3, F is Fe2O3, and y is 0 to 1, for example 0 to 0.7,
wherein the one or more other hydraulic binders is selected from Portland cement, fly ash, pozzolanic ash, blast furnace slag, silica flour, silica fume, metakaolin, lime, basalt, alumino silicate, pozzolan, or a combination thereof,
wherein the granular materials are selected from quartz, sand, limestone, gypsum, siliceous sand, or a combination thereof
wherein the one or more reinforcing fibres are selected from cellulose fibres, cellulose pulp, glass fibres, carbon fibres, polymeric fibres, and combinations thereof. and
wherein the one or more blowing agents is aluminium, for example aluminium powder.

Assignees

• Imertech Sas

Inventors

• Espinosa Bruno
• Niepmann Dirk
• Grolleau Jerome
• Charpentier Eric
• Bousseau Jean-Noël

Classifications

• C04B14/365

  Gypsum (synthetic gypsum C04B18/0445, C04B18/064) · CPC title

• C04B18/24

  Vegetable refuse, e.g. rice husks, maize-ear refuse; Cellulosic materials, e.g. paper {, cork} · CPC title

• C04B24/2652

  Nitrogen containing polymers, e.g. polyacrylamides, polyacrylonitriles · CPC title

• C04B14/06

  Quartz; Sand · CPC title

• C04B2103/008

  Flocking or deflocking agents · CPC title