Conversion of gypsum waste into foamed construction material

Patent metadata

Field	Value
Publication number	US-2022162126-A1
Application number	US-202017440971-A
Country	US
Kind code	A1
Filing date	Mar 20, 2020
Priority date	Mar 27, 2019
Publication date	May 26, 2022
Grant date	—

Abstract

Techniques of forming a foamed insulation material from gypsum waste are disclosed herein. One example technique includes mechanically comminuting the gypsum waste from an original size into particles of gypsum at a target size smaller than the original size and mixing the particles of the gypsum with a binder to form a mixture of particles and binder. The binder is configured to bind the particles of gypsum upon hydration. The example technique can further include performing air entrainment on the mixture until a foam is formed from the mixture having the particles of gypsum and binder. The foam has water that causes the binder to bind the particles of gypsum. The example technique can then include removing moisture from the mixture with the formed foam to form a foamed insulation material from the particles of gypsum.

First claim

I/we claim:

1 . A method of forming a foamed insulation material from gypsum waste having gypsum sandwiched between facing and backing papers, the method comprising:
mechanically comminuting the gypsum waste from an original size into particles of gypsum at a target size smaller than the original size; mixing the particles of the gypsum from the mechanically comminuted gypsum waste with a binder to form a mixture of particles and binder, the binder being configured to bind the particles of gypsum upon hydration; performing air entrainment on the mixture until a foam is formed from the mixture having the particles of gypsum and binder, the foam having water that causes the binder to bind the particles of gypsum; and removing moisture from the mixture with the formed foam to form a foamed insulation material from the particles of gypsum.

2 . The method of claim 1 , further comprising:
separating the facing and backing papers from the gypsum core of the gypsum waste, wherein
mechanically comminuting the gypsum waste includes separately comminuting the gypsum into the particles of gypsum and comminuting the facing and backing papers into particles of paper; and
mixing the particles includes mixing the particles of gypsum with the particles of paper from comminuting the facing and backing papers.

3 . The method of claim 1 wherein:
mechanically comminuting the gypsum waste includes comminuting the gypsum in the gypsum waste along with the facing and backing papers into the particles of gypsum and particles of paper; and
mixing the particles of the gypsum includes mixing the particles of the gypsum and the particles of paper with the binder.

4 . The method of claim 1 wherein performing air entrainment on the mixture includes one of:
mixing the particles of the gypsum includes adding a surfactant and water into the mixture and applying mechanical agitation to the mixture until the foam is formed from the mixture;
applying a pre-made foam to the mixture; or
forming the foam using chemical admixtures that react to form the foam upon hydration

5 . The method of claim 1 wherein mixing the particles of the gypsum core with the binder includes adding a paper waste to the mixture in a range from about 2% up to 15% of dry weight.

6 . The method of claim 1 wherein mixing the particles of the gypsum core with the binder includes adding a plurality of aggregates of sand, stone, gravel, slag, fly ash, glass, silica, expanded slate, clay, pumice, perlite, diatomaceous earth, shale, crushed rock, straw, glass fiber, cellulose fiber, or plastic fiber.

7 . The method of claim 1 wherein mixing the particles of the gypsum core with the binder includes one of:
mixing the particles of the gypsum core with a cementitious binder from about 10% up to about 20% dry weight; or
mixing the particles of the gypsum core with a non-cementitious binder from about 1% up to about 10% dry weight

8 . The method of claim 1 wherein mixing the particles of the gypsum core with the binder includes one of:
mixing the particles of the gypsum core with an agar agar binder of about 1% to about 5% dry weight;
mixing the particles of the gypsum core with a sodium alginate binder from about 1% up to about 10%; or
mixing the particles of the gypsum core with a sodium alginate binder from about 1% up to about 10%.

9 . A foamed insulation material produced from a gypsum waste, the foamed insulation material comprising:
about 30% to about 90% by dry weight of gypsum particles from a gypsum waste; about 2% to about 15% by dry weight of a paper waste; and a binder configured to bind the gypsum particles upon hydration, wherein the foamed insulation material has:
a dry density range of about 0.2 to about 0.4 g/cm 3 ;
a thermal conductivity ranging from 0.036 W/mK to 0.053 W/mK; and
a resistance to heat transfer from RSI 0.189/cm to RSI 0.916/cm; and
wherein the foamed insulation material having a microstructure that includes a scaffold structure formed by a plurality of fibers, the scaffold structure having interstitial voids and carrying the gypsum particles bound to one another and to the scaffold material via the binder.

10 . The foamed insulation material of claim 9 wherein the gypsum waste includes gypsum sandwiched between facing and backing papers, and wherein the paper waste includes the facing and backing papers not removed from the gypsum waste.

11 . The foamed insulation material of claim 9 wherein the gypsum waste includes gypsum sandwiched between facing and backing papers, and wherein the paper waste includes the facing and backing papers not removed from the gypsum waste and an additional paper waste different than the facing and backing papers of the gypsum waste.

12 . The foamed insulation material of claim 9 , further comprising a plurality of aggregates of up to 20% dry weight, the plurality of aggregates include one or more of sand, stone, gravel, slag, fly ash, glass, silica, expanded slate, clay, pumice, perlite, diatomaceous earth, shale, crushed rock, straw, glass fiber, cellulose fiber, or plastic fiber.

13 . The foamed insulation material of claim 9 wherein the binder includes a cementitious binder of up to about 20% dry weight.

14 . The foamed insulation material of claim 9 wherein the binder includes a cementitious binder of up to about 20% dry weight, and wherein the cementitious binder includes at least one of Portland cement, a synthetic pozzolan, or a natural pozzolan.

15 . The foamed insulation material of claim 9 wherein the binder includes a cementitious binder that contains at least one of fly ash, ground granulated blast furnace slag, silica fume, volcanic ash, wood ash, or lime.

16 . The foamed insulation material of claim 9 wherein the binder includes a combination of Portland cement and pozzolans, and wherein a percentage ratio of pozzolans to Portland cement is about 1 percent (%) up to about 100 percent (%).

17 . The foamed insulation material of claim 9 wherein the binder includes a plant-based or algae-based biopolymer.

18 . The foamed insulation material of claim 9 wherein the binder includes sodium alginate or agar agar.

19 . The foamed insulation material of claim 9 wherein the foamed insulation material has a fire protective burn-through time of greater than about one hour and forty minutes per inch of thickness.

20 . The foamed insulation material of claim 9 wherein the foamed insulation material is configured as at least one of a rigid insulation panel; a pourable, blown, or sprayed insulation material; the insulating component of a composite structural panel; an insulating component of an exterior insulation finishing system; hollow insulating formwork for concrete; a pourable, blown, or sprayed material for excavation backfill.

Assignees

• Univ Washington State

Inventors

• Miyasaka Taiji
• Drake David Ronald

Classifications

• B09B3/24

  Binders with plastic · CPC title

• B09B3/23

  Binders with asphalt · CPC title

• B09B3/25

  using mineral binders or matrix · CPC title

• B09B3/21

  using organic binders or matrix · CPC title

• B32B2607/00

  Walls, panels · CPC title