Perovskite precursor composition, method of preparing perovskite film, perovskite film and perovskite solar cell

Patent metadata

Field	Value
Publication number	US-2022158104-A1
Application number	US-202117525216-A
Country	US
Kind code	A1
Filing date	Nov 12, 2021
Priority date	Nov 13, 2020
Publication date	May 19, 2022
Grant date	—

Abstract

An ionic liquid (IL)-containing perovskite precursor composition includes perovskite precursors; and a salt of a cationic imidazole derivative in which at least one of the two nitrogen atoms in the imidazole ring is linked to a carbon chain bearing a cyano (—C≡N) group. A perovskite solar cell with high stability includes a layer constituted by a perovskite film formed using the perovskite precursor composition.

First claim

What is claimed is:

1 . A perovskite precursor composition comprising:
perovskite precursors; and a salt of a cationic imidazole derivative in which at least one of two nitrogen atoms in imidazole ring is linked to a carbon chain bearing a cyano (—C≡N) group, wherein the cationic imidazole derivative has formula (1) or formula (2):

wherein, in the formula (1):
R 1 is C1-C4 alkyl; and
R 2 is —(CH 2 ) n — wherein n is 2 to 6; and
in the formula (2):
R 2a is —(CH 2 ) a — wherein a is 1 to 6; and
R 2b is —(CH 2 ) b — wherein b is 1 to 6.

2 . The perovskite precursor composition according to claim 1 , wherein anionic counterion for the cationic imidazole derivative of the formula (1) or the formula (2) is a halide anion which is one or more among Cl − , Br − and I − .

3 . The perovskite precursor composition according to claim 1 , wherein the salt of the cationic imidazole derivative is one of the following:

4 . The perovskite precursor composition according to claim 1 , wherein the perovskite precursors are ABX 3 materials wherein:
A are organic cations and/or Group 1 metal cations; B being at least one metal selected from the group consisting of: Pb, Sn, Bi, Cu, Ag and their mixtures; and X being halides such as Cl, Br, I and their mixtures.

5 . The perovskite precursor composition according to claim 1 , further containing a solvent which is one or more of: DMSO or DMF or gamma-butyrolactone.

6 . A perovskite precursor composition comprising:
perovskite precursors; and a salt of a cationic imidazole derivative having formula (1):

wherein, in the formula (1):

R 1 is C1-C6 alkyl; and
R 2 is —(CH 2 ) n — wherein n is 1; and
wherein anionic counterion for the cationic imidazole derivative of the formula (1) is chloride (Cl − ).

7 . The perovskite precursor composition according to claim 6 , wherein the salt of the cationic imidazole derivative is

8 . The perovskite precursor composition according to claim 6 , wherein the perovskite precursors are ABX 3 materials wherein:
A are organic cations and/or Group 1 metal cations; B being at least one metal selected from the group consisting of: Pb, Sn, Bi, Cu, Ag and their mixtures; and X being halides such as Cl, Br, I and their mixtures.

9 . The perovskite precursor composition according to claim 6 , further containing a solvent which is one or more of: DMSO or DMF or gamma-butyrolactone.

10 . Method of preparing a perovskite film comprising the steps of:
(A) preparation of the perovskite precursor composition according to claim 1 ; (B) providing a substrate; and (C) formation of a perovskite film on a surface of the substrate.

11 . The method of preparing the perovskite film according to claim 10 , wherein step (C) is carried out through a process selected from the group consisting of: printing, slot-die coating, meniscus-coating, and spin-coating.

12 . The method according to claim 10 , wherein the substrates are flexible or rigid conductive substrates.

13 . The method according to claim 10 , wherein after the formation of the perovskite film, the perovskite film is coated with a layer containing phenyl ethyl-ammonium iodide (PEAI).

14 . Method of preparing a perovskite film comprising steps of:
(A) preparation of the perovskite precursor composition according to claim 6 ; (B) providing a substrate; and (C) formation of a perovskite film on a surface of the substrate.

15 . The method of preparing the perovskite film according to claim 14 , wherein step (C) is carried out through a process selected from the group consisting of: printing, slot-die coating, meniscus-coating, and spin-coating.

16 . The method according to claim 14 , wherein the substrates are flexible or rigid conductive substrates.

17 . The method according to claim 14 , wherein after the formation of the perovskite film, the perovskite film is coated with a layer containing phenyl ethyl-ammonium iodide (PEAI).

18 . A perovskite film prepared by the method according to claim 10 .

19 . A perovskite film prepared by the method according to claim 14 .

20 . A perovskite solar cell comprising:
(a) a transparent conductive layer; (c) a perovskite film comprising the perovskite precursor composition according to claim 1 ; and (e) an electrode, optionally further comprising one or more of: (b) an electron transport layer; (b′) an electron-blocking layer; (d) a hole transport layer; and (d′) a hole-blocking layer.

21 . The perovskite solar cell according to claim 20 wherein the transparent conductive layer (a) comprises one or more of: fluorine-doped tin oxide (FTO), indium tin oxide (ITO), doped zinc oxide, carbon nanotube networks and graphene.

22 . The perovskite solar cell according to claim 20 wherein the electron transport layer (b) comprises one or more of: TiO 2 , SnO 2 , Nb-doped SnO 2 , Sb-doped SnO 2 , C60 and C60 derivatives, bathocuproine (BCP), a combination of C60/BCP, and a combination of TiO 2 /SnO 2 bilayer.

23 . The perovskite solar cell according to claim 20 , wherein the hole transport layer (d) comprises one or more of: spiro-OMeTAD (2,2′,7,7′-tetrakis-(N,N′-di-p-methoxyphenylamine)-9,9′-spirobifluorene), pyrene-based materials (such as PY-1, PY-2, PY-3), Truxene-core based materials, phenothiazine-based materials, acridine-, thiophene-, biphenyl-, bithiophene-, tetrathiophene-, difluorobenzene and phenyl-based materials, triazine-based materials, benzotrithiophene- and squaraine-based materials, fluorene- and spiro-fluorene-based materials and carbazole-based materials, phthalocyanines, carbon, metal complexes, and CuNCS, NiO x .

24 . The perovskite solar cell according to claim 20 , wherein electrode (e) comprises one or more of: Au, C, Ag, Cu or Al.

25 . The perovskite solar cell according to claim 20 , wherein the perovskite solar cell further comprises mesoporous scaffold, either in n-i-p or p-i-n configuration.

26 . The perovskite solar cell according to claim 20 , wherein the perovskite film (c) is coated with a layer containing phenyl ethyl-ammonium iodide (PEAI), the layer containing PEAI being situated between the perovskite film (c) and the hole transport layer (d) and also between the perovskite film (c) and the electrode (e).

27 . A perovskite solar cell comprising:
(a) a transparent conductive layer; (c) a perovskite film comprising the perovskite precursor composition according to claim 6 ; and (e) an electrode, optionally further comprising one or more of: (b) an electron transport layer; (b′) an electron-blocking layer; (d) a hole transport layer; and (d′) a hole-blocking layer.

28 . The perovskite solar cell according to claim 27 wherein the transparent conductive layer (a) comprises one or more of: fluorine-doped tin oxide (FTO), indium tin oxide (ITO), doped zinc oxide, carbon nanotube networks and graphene.

29 .

Assignees

• Toyota Motor Co Ltd

Inventors

• Kinge Sachin
• Fei Zhaofu
• Dyson Paul J
• Khaja Nazeeruddin Mohammad
• Gao Xiao-Xin
• Ding Bin

Classifications

• H01G9/2027

  comprising an oxide semiconductor electrode · CPC title

• H10K85/50

  Organic perovskites; Hybrid organic-inorganic perovskites [HOIP], e.g. CH3NH3PbI3 · CPC title

• H10K30/151

  the wide bandgap semiconductor comprising titanium oxide, e.g. TiO2 · CPC title

• H10K30/50

  Photovoltaic [PV] devices · CPC title

• H10K30/10

  comprising heterojunctions between organic semiconductors and inorganic semiconductors · CPC title