Nickel manganese cobalt composite hydroxide, method for producing nickel manganese cobalt composite hydroxide, lithium nickel manganese cobalt composite oxide, and lithium ion secondary battery

Patent metadata

Field	Value
Publication number	US-2022131144-A1
Application number	US-201917425031-A
Country	US
Kind code	A1
Filing date	Dec 26, 2019
Priority date	Jan 22, 2019
Publication date	Apr 28, 2022
Grant date	—

Abstract

A nickel manganese cobalt composite hydroxide, which is a precursor of a positive electrode active material and is composed of secondary particles to which primary particles containing a nickel, manganese, and cobalt are aggregated, or composed of the primary and secondary particles, wherein a sodium content contained in the nickel manganese cobalt composite hydroxide is less than 0.0005% by mass, and a void ratio of particles is more than 50% to 80%. Also, a ratio of an average particle size of a lithium nickel manganese cobalt composite oxide divided by an average particle size of the nickel manganese cobalt composite hydroxide, which is a precursor, is 0.95 to 1.05, and further, when observing 100 or more particles selected randomly by a scanning electron microscope, a number that an aggregation of secondary particles is observed is 5% or less with respect to a total number of observed secondary particles.

First claim

1 . A nickel manganese cobalt composite hydroxide, which is a precursor of a positive electrode active material, and which is composed of secondary particles to which primary particles containing a nickel, a manganese, and a cobalt are aggregated, or composed of the primary particles and the secondary particles,
wherein a sodium content contained in the nickel manganese cobalt composite hydroxide is less than 0.0005% by mass, and a void ratio of particles of the nickel manganese cobalt composite hydroxide is more than 50% to 80%.

2 . The nickel manganese cobalt composite hydroxide according to claim 1 , wherein a specific surface area of the nickel manganese cobalt composite hydroxide is 50 to 60 m 2 /g.

3 . The nickel manganese cobalt composite hydroxide according to claim 1 , wherein a sulfate radical content contained in the nickel manganese cobalt composite hydroxide is 0.2% by mass or less, and also, a chloride radical content is 0.01% by mass or less.

4 . The nickel manganese cobalt composite hydroxide according to claim 1 , wherein a value of [(d90−d10)/average particle size], which is an index indicating a spread of a particle size distribution of the nickel manganese cobalt composite hydroxide, is 0.55 or less.

5 . The nickel manganese cobalt composite hydroxide according to claim 1 , wherein the nickel manganese cobalt composite hydroxide is represented by a general formula: Ni x Mn y Co z M t (OH) 2+a wherein x+y+z+t=1, 0.20≤x≤0.80, 0.10≤y≤0.90, 0.10≤z≤0.50, 0≤t≤0.10, 0≤a≤0.5, and M is at least one selected from Mg, Ca, Al, Ti, V, Cr, Zr, Nb, Mo, and W.

6 . The nickel manganese cobalt composite hydroxide according to claim 1 , wherein a content of at least one of a potassium, a calcium, and a magnesium contained in the nickel manganese cobalt composite hydroxide is less than 0.0005% by mass.

7 . A method for producing a nickel manganese cobalt composite hydroxide, which is a precursor of a positive electrode active material, and which is composed of secondary particles to which primary particles containing a nickel, a manganese, and a cobalt are aggregated, or composed of the primary particles and the secondary particles, comprising:
a crystallization process for obtaining a transition metal composite hydroxide by crystallizing in a reaction solution obtained by adding a raw material solution containing a nickel, a manganese, and a cobalt, a solution containing an ammonium ion supplier, and an alkaline solution; and a washing process for washing the transition metal composite hydroxide obtained in the crystallization process by a washing liquid, wherein the alkaline solution in the crystallization process is a mixed solution of an alkali metal hydroxide and a carbonate, a ratio [CO 3 2− ]/[OH − ] of the carbonate with respect to the alkali metal hydroxide in the mixed solution is 0.002 to 0.050, a crystallization is performed by switching an atmosphere multiple times in two stages of an oxidizing atmosphere and a non-oxidizing atmosphere in the crystallization process, and the washing liquid in the washing process is an ammonium hydrogen carbonate solution with a concentration of 0.05 mol/L or more.

8 . The method for producing the nickel manganese cobalt composite hydroxide according to claim 7 , wherein the crystallization process further comprises a nucleation process and a particle growth process, and
in the nucleation process, a nucleation is performed by adding the alkaline solution to the reaction solution such that a pH measured on the basis of a liquid temperature of 25 degrees Celsius will be 12.0 to 14.0, and in the particle growth process, the alkaline solution is added to the reaction solution containing nuclei formed in the nucleation process such that a pH measured on the basis of a liquid temperature of 25 degrees Celsius will be 10.5 to 12.0.

9 . The method for producing the nickel manganese cobalt composite hydroxide according to claim 7 , wherein the nickel manganese cobalt composite hydroxide obtained via the washing process is a nickel manganese cobalt composite hydroxide, which is a precursor of a positive electrode active material, and which is composed of secondary particles to which primary particles containing a nickel, a manganese, and a cobalt are aggregated, or composed of the primary particles and the secondary particles, and
a sodium content contained in the nickel manganese cobalt composite hydroxide is less than 0.0005% by mass, and a void ratio of particles of the nickel manganese cobalt composite hydroxide is more than 50% to 80%.

10 . A lithium nickel manganese cobalt composite oxide composed of secondary particles to which primary particles containing a lithium, a nickel, a manganese, and a cobalt are aggregated, or composed of the primary particles and the secondary particles,
wherein a sodium content contained in the lithium nickel manganese cobalt composite oxide is less than 0.0005% by mass, and a void ratio of particles of the lithium nickel manganese cobalt composite oxide is more than 50% to 80%.

11 . The lithium nickel manganese cobalt composite oxide according to claim 10 , wherein a sulfate radical content contained in the lithium nickel manganese cobalt composite oxide is 0.15% by mass or less, and a chloride radical content is 0.005% by mass or less, and also, a Me site occupancy factor is 93.0% or more.

12 . The lithium nickel manganese cobalt composite oxide according to claim 10 , wherein a ratio of an average particle size of the lithium nickel manganese cobalt composite oxide divided by an average particle size of a nickel manganese cobalt composite hydroxide, which is a precursor, is 0.95 to 1.05.

13 . The lithium nickel manganese cobalt composite oxide according to claim 10 , wherein, when observing 100 or more particles of the lithium nickel manganese cobalt composite oxide selected randomly by a scanning electron microscope, a number that an aggregation of secondary particles is observed is 5% or less with respect to a total number of observed secondary particles.

14 . The lithium nickel manganese cobalt composite oxide according to claim 10 , wherein a content of at least one of a potassium, a calcium, and a magnesium contained in the lithium nickel manganese cobalt composite oxide is less than 0.0005% by mass.

15 . A lithium ion secondary battery comprising a positive electrode at least containing the lithium nickel manganese cobalt composite oxide according to claim 10 .

Assignees

• Sumitomo Metal Mining Co

Inventors

• Oshita Hiroko
• Ryoshi Kazuomi

Classifications

• H01M10/0525 Primary

  Rocking-chair batteries, i.e. batteries with lithium insertion or intercalation in both electrodes; Lithium-ion batteries · CPC title

• H01M4/505

  of mixed oxides or hydroxides containing manganese for inserting or intercalating light metals, e.g. LiMn2O4 or LiMn2OxFy · CPC title

• H01M4/525 Primary

  of mixed oxides or hydroxides containing iron, cobalt or nickel for inserting or intercalating light metals, e.g. LiNiO2, LiCoO2 or LiCoOxFy · CPC title

• H01M2004/028

  Positive electrodes · CPC title

• H01M4/362

  Composites · CPC title