Abstract

The present disclosure provides a polymeric opal comprising a polymer and an additive. The additive comprises a two-dimensional (2D) material and/or a carbon nanotube and the weight ratio of the polymer to the additive is between 100:0.001 and 00:0.1.

First claim

1 . A polymeric opal comprising a polymer and an additive, wherein the additive comprises a two-dimensional (2D) material and/or a carbon nanotube and the weight ratio of the polymer to the additive is between 100:0.001 and 100:0.1.

2 . The polymeric opal of claim 1 , wherein the volumetric ratio of the polymer to the additive between 100:0.0005 and 100:0.05, between 100:0.001 and 100:0.01, between 100:0.0025 and 100:0.0075 or between 100:0.004 and 100:0.006.

3 . The polymeric opal of claim 1 , wherein the additive consists of a 2D material.

4 . The polymeric opal of claim 1 , wherein the 2D material comprises a plurality of particles having a mean thickness of less than 50 nm and a largest lateral dimension with a mean size of less than 30 μm and/or wherein the 2D material is selected from the group consisting of graphene, hexagonal boron nitride (h-BN) and a transition metal dichalcogenide.

5 . (canceled)

6 . The polymeric opal of claim 1 , wherein the polymeric opal comprises a surfactant.

7 . The polymeric opal of claim 6 , wherein the surfactant comprises a non-ionic surfactant.

8 . The polymeric opal of claim 7 , wherein the non-ionic surfactant comprises

wherein n is an integer between 1 and 50, and/or a polysorbate, optionally wherein the non-ionic surfactant comprises triton X-100 and/or polysorbate 80.

9 . (canceled)

10 . The polymeric opal of claim 7 , wherein the volumetric ratio of the polymer to the non-ionic surfactant is between 100:0.0001 and 100:2, between 100:0.001 and 100:1, between 100:0.01 and 100:0.75, or between 100:0.4 and 100:06.

11 . The polymeric opal of claim 1 , wherein the polymer has a dry glass transition temperature (T g ) between 0° C. and 100° C.

12 . The polymeric opal of claim 1 , wherein the polymer comprises a plurality of particles having an average particle size of between 50 nm and 1,000 nm.

13 . The polymeric opal of claim 1 , wherein the polymer comprises a carboxylic acid group.

14 . The polymeric opal of claim 1 , wherein the polymeric opal comprises an interstitial liquid, optionally wherein the interstitial liquid comprises water, an alcohol or an amine and/or between 0.5 wt % and 30 wt % of the polymeric opal.

15 . (canceled)

16 . (canceled)

17 . The polymeric opal of claim 1 , wherein the polymeric opal comprises a polymer coating, optionally wherein the polymer coating is configured to modify the rate of evaporation of the interstitial liquid.

18 . (canceled)

19 . The polymeric opal of claim 1 , wherein the polymeric opal exhibits a stopband at a wavelength between 200 nm and 1000 nm.

20 . A method of producing a polymeric opal, the method comprising:
providing a dispersion comprising a polymer and an additive in a solvent, wherein the additive comprises a two-dimensional (2D) material and/or a carbon nanotube and the volumetric ratio of the polymer to the additive is between 100:0.0001 and 100:0.1; evaporating the solvent at a rate whereby evaporation of the solvent dominates over diffusion and sedimentation of the polymer and the additive to thereby form a polymeric opal.

21 . A method according to claim 20 , wherein evaporating the solvent at a rate whereby evaporation of the solvent dominates over diffusion and sedimentation of the polymer and the additive comprises controlling the conditions that the dispersion is exposed to such that the Peclet number (Pe) is at least 0.25 and the sedimentation number (Ns) is less than 10.

22 . A method according to claim 20 , wherein the dispersion is maintained at a temperature between 1° C. and 80° C. and a humidity between 5% and 99%.

23 . A method according to claim 20 , wherein the dispersion comprises a surfactant.

24 . A photonic paper, an item of jewellery, a time-temperature indicator, a mechano-chromic sensor, a waveguide, a scaffold for tissue engineering or a sensor comprising a polymeric opal as defined in claim 1 .

25 . An anti-counterfeiting kit comprising a photonic paper, as defined by claim 24 , and a pen comprising a solvent.

26 . (canceled)

Assignees

• Univ Surrey

Inventors

• Jurewicz Izabela
• Dalton Alan

Classifications

• C08K3/042 Primary

  Graphene or derivatives, e.g. graphene oxides · CPC title

• B82Y20/00

  Nanooptics, e.g. quantum optics or photonic crystals · CPC title

• C08F2/22

  Emulsion polymerisation · CPC title

• B82Y40/00

  Manufacture or treatment of nanostructures · CPC title

• C08K3/38

  Boron-containing compounds · CPC title