Polyethylene laminates for use in flexible packaging materials

Patent metadata

Field	Value
Publication number	US-2021331845-A1
Application number	US-201816625101-A
Country	US
Kind code	A1
Filing date	Jun 27, 2018
Priority date	Jun 30, 2017
Publication date	Oct 28, 2021
Grant date	—

Abstract

Embodiments of laminate structures for flexible packaging comprise a print film comprising ethylene-based polymer, a sealant film laminated to the print film, wherein the sealant film comprising at least 3 layers and has an overall thickness from 15 to 30 μm. The sealant film comprises a middle layer, an outer layer, and an inner layer disposed between the print film and the middle layer. The inner layer comprises an ethylene interpolymer having a density from 0.910 to 0.925 g/cc and a melt index (I2) from 0.5 to 5 g/10 min, and at least one of the inner layer, the middle layer, and the outer layer comprise a first composition comprising at least one ethylene based polymer, wherein the first composition comprises a Molecular Weighted Comonomer Distribution Index (MWCDI) value greater than 0.9, and a melt index ratio (I10/I2) that meets the equation: I10I2≥7.0-log (I2).

First claim

1 . A laminate structure comprising:
a print film comprising ethylene-based polymer; a sealant film laminated to the print film, the sealant film comprising at least 3 layers and having an overall thickness from 15 to 30 μm, where the sealant film comprises a middle layer, an outer layer, and an inner layer disposed between the print film and the middle layer, wherein
the inner layer comprises an ethylene interpolymer having a density from 0.900 to 0.925 g/cc and a melt index (12) from 0.5 to 5 g/10 min, wherein 12 is measured according to ASTM D1238 at 190° C. and 2.16 kg load; and
at least one of the inner layer, the middle layer, and the outer layer comprise a first composition comprising at least one ethylene based polymer, wherein the first composition comprises a Molecular Weighted Comonomer Distribution Index (MWCDI) value greater than 0.9, and a melt index ratio (I 10 /I 2 ) that meets the following equation: I 10 /I 2 ≥7.0−1.2×log (I 2 ).

2 . The laminate structure of claim 1 , wherein the middle layer and the outer layer each comprise the first composition.

3 . The laminate structure of claim 1 , wherein the inner layer comprises at least 50% by weight of the ethylene interpolymer.

4 . The laminate structure of claim 1 , wherein the inner layer further comprises low density polyethylene (LDPE) having a density from 0.915 to 0.930 g/cc, melt index (I 2 ) from 0.5 to 5 g/10 min, and a Molecular Weight Distribution (MWD) from 3 to 10, wherein the MWD is defined as M w /M n , wherein M w is a weight average molecular weight and M n is a number average molecular weight as measured by Gel Permeation Chromatography (GPC).

5 . The laminate structure of claim 1 , wherein the inner layer comprises from 60 to 90% by weight of the ethylene interpolymer, and from 10 to 40% by weight of the LDPE.

6 . The laminate structure of claim 1 , wherein the first composition has a MWCDI value less than, or equal to, 10.0.

7 . The laminate structure of claim 1 , wherein the first composition has a Zero-Shear Viscosity Ratio (ZSVR) value from 1.2 to 3.0.

8 . The laminate structure of claim 1 , wherein the first composition has a melt index ratio I 10 /I 2 less than, or equal to, 9.2.

9 . The laminate structure of claim 1 , wherein the first composition has a vinyl unsaturation level greater than 10 vinyls per 1,000,000 total carbons.

10 . The laminate structure of claim 1 , wherein the print film comprises at least 3 layers, where the print film comprises a middle layer, an outer layer, and an inner layer disposed adjacent the inner layer of the sealant film, wherein
the middle layer comprises at least 90% by weight high density polyethylene (HDPE) having a density from 0.950 to 0.965 g/cc and a melt index (I 2 ) from 0.1 to 20 g/10 min, wherein 12 is measured according to ASTM D1238 at 190° C. and 2.16 kg load; and
the inner layer, the outer layer, or both comprises linear low density polyethylene (LLDPE) having a density from 0.925 to 0.965 g/cc and a melt index (I 2 ) from 0.1 to 20 g/10 min.

11 . The laminate structure of claim 10 , wherein the middle layer of the print film comprises 100% by wt. HDPE.

12 . The laminate structure of claim 10 , wherein the inner layer, the outer layer, or both of the print film further comprise low density polyethylene (LDPE) having an MWD from 3 to 10 and a melt index (I 2 ) from 0.5 to 5 g/10 min, wherein the MWD is defined as Mw/Mn, wherein Mw is weight average molecular weight and Mn is number average molecular weight.

13 . The laminate structure of claim 10 , wherein the inner layer, the outer layer, or both of the print film comprises at least 50 wt. % LLDPE, wherein the density of the LLDPE in the inner layer, the outer layer, or both of the print film is from 0.930 to 0.940 g/cc and the melt index (12) from 0.5 to 1.5 g/10 min.

14 . The laminate structure of claim 1 , wherein the laminate structure has an overall thickness less than 50 μm.

15 . An article comprising the laminate structure of claim 1 , wherein the article is a flexible packaging material.

Assignees

• Dow Global Technologies Llc

Inventors

• Laddha Sachin
• Mishra Shashibhushan
• Wang Jian

Classifications

• B32B2307/412

  Transparent · CPC title

• B32B27/327

  comprising polyolefins obtained by a metallocene or single-site catalyst · CPC title

• B32B2439/06

  Bags, sacks, sachets · CPC title

• B32B27/08

  of synthetic resin · CPC title

• B32B2553/00

  Packaging equipment or accessories not otherwise provided for · CPC title