Roll-to-roll sofc manufacturing method and system

Patent metadata

Field	Value
Publication number	US-2021175517-A1
Application number	US-202017118261-A
Country	US
Kind code	A1
Filing date	Dec 10, 2020
Priority date	Dec 10, 2019
Publication date	Jun 10, 2021
Grant date	—

Abstract

A method of making a solid oxide fuel cell (SOFC) includes the steps of providing a first SOFC layer laminate tape comprising a first SOFC layer composition attached to a flexible carrier film layer, providing a second SOFC laminate tape comprising a second SOFC layer composition attached to a flexible carrier film layer, and providing a third SOFC layer laminate tape comprising a third SOFC layer composition attached to a flexible carrier film layer. The first SOFC layer laminate tape, the second SOFC layer laminate tape, and the third SOFC layer laminate tape are assembled on rolls positioned along a roll-to-roll assembly line. The laminate tapes are sequentially laminated and calendered and the flexible carrier films removed to provide a composite SOFC precursor laminate that can be sintered and combined with a cathode to provide a completed SOFC. An assembly for making composite SOFC precursor laminates is also disclosed.

First claim

We claim:

1 . A method of making a solid oxide fuel cell (SOFC), comprising the steps of:
providing a first SOFC layer laminate tape comprising a first SOFC layer composition attached to a flexible carrier film layer; providing a second SOFC laminate tape comprising a second SOFC layer composition attached to a flexible carrier film layer; providing a third SOFC layer laminate tape comprising a third SOFC layer composition attached to a flexible carrier film layer; assembling the first SOFC layer laminate tape, the second SOFC layer laminate tape, and the third SOFC layer laminate tape on rolls positioned along a roll-to-roll assembly line; continuously positioning adjacent to one another and moving the first SOFC layer laminate tape, and the second SOFC layer laminate tape, with the respective flexible carrier film layers facing outward, to create a SOFC precursor laminate having a first thickness; passing the SOFC precursor laminate through a calender to reduce the thickness of the SOFC precursor laminate to a second thickness less than the first thickness; continuously removing one of the respective tape layers from the SOFC precursor laminate, the other of the tape layers of the SOFC precursor laminate remaining; continuously moving and positioning adjacent to one another the SOFC precursor laminate and the third SOFC layer laminate tape, with the respective tape layers facing outward, to create a composite SOFC precursor laminate comprising the SOFC precursor laminate and the third SOFC layer laminate tape, the composite SOFC precursor laminate having a first thickness; and, calendering the composite SOFC precursor laminate to reduce the first thickness to a second thickness less that the first thickness.

2 . The method of claim 1 , wherein the first SOFC layer composition, the second SOFC layer composition, and the third SOFC layer composition comprise, interchangeably, an anode support layer composition, an anode functional layer composition, and an electrolyte layer composition.

3 . The method of claim 1 , wherein:
providing the first SOFC layer laminate tape comprises providing an anode support layer laminate tape comprising an anode support layer attached to a flexible support tape layer; providing the second SOFC layer laminate tape comprises providing an anode functional layer laminate tape comprising an anode functional layer attached to a flexible anode tape layer; providing the third SOFC layer laminate tape comprises providing an electrolyte layer laminate tape comprising an electrolyte layer attached to a flexible electrolyte tape layer; assembling the anode support layer laminate tape, the anode functional layer laminate tape, and the electrolyte layer laminate tape on rolls positioned along a roll-to-roll assembly line; continuously positioning adjacent to one another and moving the anode functional layer laminate tape, and one of the electrolyte layer laminate tape and the support layer laminate tape, with the respective tape layers facing outward, to create an anode precursor laminate having a first thickness; passing the anode precursor laminate through a calender to reduce the thickness of the anode precursor laminate to a second thickness less than the first thickness; continuously removing one of the respective tape layers from the anode precursor laminate, the other of the tape layers of the anode precursor laminate remaining; continuously moving and positioning adjacent to one another the anode precursor laminate, and the other of the electrolyte layer laminate tape and the support layer laminate tape, with the respective tape layers facing outward, to create a composite fuel cell precursor laminate comprising the support layer, the anode layer, and the electrolyte layer, the composite fuel cell precursor layer having a first thickness; and, calendering the composite fuel cell precursor laminate to reduce the first thickness to a second thickness less that the first thickness.

4 . The method of claim 1 , further comprising the step of removing the flexible carrier film from the composite SOFC precursor laminate.

5 . The method of claim 4 , further comprising the step of applying a cathode layer to the composite SOFC precursor laminate to form a solid oxide fuel cell assembly.

6 . The method of claim 5 , further comprising the step of constructing a solid oxide fuel cell with the solid oxide fuel cell assembly.

7 . The method of claim 4 , further comprising the step of sintering the composite SOFC precursor laminate.

8 . The method of claim 3 , wherein
the step of providing an anode support layer laminate tape comprises the step of providing an anode support layer slurry, depositing the anode support layer slurry on a flexible support tape; and drying the anode support layer slurry to form the anode support layer precursor tape; and, the step of providing an anode functional layer laminate tape comprises the steps of providing an anode functional layer slurry, depositing the anode functional layer slurry on a flexible anode tape, and drying the anode functional layer slurry to form the anode functional layer precursor tape; and, the step of providing an electrolyte layer laminate tape comprises the steps of providing an electrolyte layer slurry, depositing the electrolyte layer slurry onto a flexible electrolyte tape, and drying the electrolyte layer slurry to form the electrolyte layer precursor tape.

9 . The method of claim 1 , wherein at least one of the first, second and third SOFC layer compositions are deposited onto the flexible carrier film by at least on selected from the group consisting of slot die coating, dip coating, tape casting, and screen printing.

10 . The method of claim 1 , wherein at least one of the first, second and third SOFC layer compositions comprises a binder.

11 . The method of claim 10 , wherein the binder is at least one selected from the group consisting of polyvinyl butyral (PVB) and polyvinyl alcohol (PVA), polyethyl methacrylate, cellulose acetate, and polyvinyl alcohol.

12 . The method of claim 1 , wherein the flexible carrier film layer from one of the first SOFC layer laminate tape, the second SOFC layer laminate tape, and the third SOFC layer laminate tape is performed by at least one selected from the group consisting of scraping and peeling.

13 . The method of claim 1 , wherein the roll-to-roll assembly line has a line speed of between 0.1 to 20 m/min.

14 . The method of claim 1 , wherein the method is performed at temperatures of between 0 to 250° C.

15 . The method of claim 1 , wherein after each lamination step the laminated layers are calendered to reduce the thickness between 0.1-40%.

16 . The method of claim 1 , further comprising cutting the rolls of the SOFC precursor laminate into SOFC coupons, and sintering the SOFC coupons for a predetermined sintering-time interval over a predetermined sintering-temperature range.

17 . The method of claim 1 , wherein the SOFC precursor laminate has a porosity of from 1% to 50%.

18 . The method of claim 1 , wherein the SOFC precursor laminate has a porosity of from 1% to 40%.

19 . The method of claim 1 , wherein the SOFC precursor laminate has a porosity of from 1% to 30%.

20 . The method of claim 1 , wherein the SOFC precursor laminate has a porosity of from 1% to 20%.

21 . A method for fabricating rolls of a solid oxide fuel cell (SOFC) structure, wherein the SOFC structure comprises a stack of N≥3 layers arranged in a particu

Assignees

• Ut Battelle Llc
• Redox Power Systems Llc

Inventors

• Li Jianlin
• Parikh Dhrupadkumar P
• Langdo Thomas
• Bishop Sean R
• Blackburn Bryan M

Classifications

• H01M8/1213

  characterised by the electrode/electrolyte combination or the supporting material · CPC title

• H01M4/8857

  Casting, e.g. tape casting, vacuum slip casting · CPC title

• H01M4/8889

  Cosintering or cofiring of a catalytic active layer with another type of layer · CPC title

• H01M4/8621

  containing only metallic or ceramic material, e.g. made by sintering or sputtering · CPC title

• H01M2008/1293

  Fuel cells with solid oxide electrolytes · CPC title