Catalyst for solid polymer fuel cells and method for producing the same

Patent metadata

Field	Value
Publication number	US-2021143444-A1
Application number	US-201816492734-A
Country	US
Kind code	A1
Filing date	Apr 16, 2018
Priority date	Apr 18, 2017
Publication date	May 13, 2021
Grant date	—

Abstract

The present invention relates to a catalyst for solid polymer fuel cells in which catalyst particles including platinum are supported on a carbon powder carrier. The invention provides a catalyst for solid polymer fuel cells in which the ratio of zerovalent platinum to platinum present on the surfaces of the catalyst particles is 80% or more and 100% or less. In the platinum catalyst, excellent durability is exhibited in an environment of operating a solid polymer fuel cell, and the amount of platinum eluted at the time of immersing the catalyst in a predetermined sulfuric acid solution is lower as compared to conventional platinum catalysts. The invention provides a catalyst for solid polymer fuel cells excellent in both initial activity and durability.

First claim

1 . A catalyst for solid polymer fuel cells in which catalyst particles comprising platinum are supported on a carbon powder carrier, wherein p 1 a ratio of zerovalent platinum to platinum present on surfaces of the catalyst particles is 80% or more and 100% or less.

2 . The catalyst for solid polymer fuel cells according to claim 1 , wherein an amount of platinum eluted at a time of immersing the catalyst in 0.5 M sulfuric acid at 60° C. for 48 hours is 0.1 ppm or more and 5.0 ppm or less per 2 g of the catalyst.

3 . The catalyst for solid polymer fuel cells according to claim 1 , wherein the catalyst particles have a particle size of 2 nm or more and 20 nm or less.

4 . The catalyst for solid polymer fuel cells according to claim 1 , wherein a catalyst ratio to the whole catalyst is 25 to 70% on a mass basis.

5 . A method for producing the catalyst for solid polymer fuel cells defined in claim 1 , comprising the steps of:
preparing a mixed solution by mixing a carbon powder carrier with a platinum compound solution; adding a reducing agent to the mixed solution to support catalyst particles including platinum on the carbon powder carrier; and performing a heat treatment on the carbon powder carrier supporting the catalyst particles, wherein the step of preparing a mixed solution preparing step is for mixing the carbon powder carrier with the platinum compound solution while grinding the carbon powder carrier, and the heat treatment is for heating the carbon powder carrier at a temperature of 1000° C. or higher and 1200° C. or lower.

6 . The method for producing the catalyst for solid polymer fuel cells according to claim 5 , comprising a step of bringing the catalyst after heat treatment into contact with an oxidizing solution at least once.

7 . The method for producing the catalyst for solid polymer fuel cells according to claim 6 , wherein the step of bringing the catalyst into contact with at least one oxidizing solution selected from a group including solutions of sulfuric acid, nitric acid, phosphorous acid, potassium permanganate, hydrogen peroxide, hydrochloric acid, chloric acid, hypochlorous acid and chromic acid.

8 . The catalyst for solid polymer fuel cells according to claim 2 , wherein the catalyst particles have a particle size of 2 nm or more and 20 nm or less.

9 . The catalyst for solid polymer fuel cells according to claim 2 , wherein a catalyst ratio to the whole catalyst is 25 to 70% on a mass basis.

10 . The catalyst for solid polymer fuel cells according to claim 3 , wherein a catalyst ratio to the whole catalyst is 25 to 70% on a mass basis.

11 . A method for producing the catalyst for solid polymer fuel cells defined in claim 2 , comprising the steps of:
preparing a mixed solution by mixing a carbon powder carrier with a platinum compound solution; adding a reducing agent to the mixed solution to support catalyst particles including platinum on the carbon powder carrier; and performing a heat treatment on the carbon powder carrier supporting the catalyst particles, wherein the step of preparing a mixed solution preparing step is for mixing the carbon powder carrier with the platinum compound solution while grinding the carbon powder carrier, and the heat treatment is for heating the carbon powder carrier at a temperature of 1000° C. or higher and 1200° C. or lower.

12 . The method for producing the catalyst for solid polymer fuel cells according to claim 11 , comprising a step of bringing the catalyst after heat treatment into contact with an oxidizing solution at least once.

13 . The method for producing the catalyst for solid polymer fuel cells according to claim 12 , wherein the step of bringing the catalyst into contact with at least one oxidizing solution selected from a group including solutions of sulfuric acid, nitric acid, phosphorous acid, potassium permanganate, hydrogen peroxide, hydrochloric acid, chloric acid, hypochlorous acid and chromic acid.

14 . A method for producing the catalyst for solid polymer fuel cells defined in claim 3 , comprising the steps of:
preparing a mixed solution by mixing a carbon powder carrier with a platinum compound solution; adding a reducing agent to the mixed solution to support catalyst particles including platinum on the carbon powder carrier; and performing a heat treatment on the carbon powder carrier supporting the catalyst particles, wherein the step of preparing a mixed solution preparing step is for mixing the carbon powder carrier with the platinum compound solution while grinding the carbon powder carrier, and the heat treatment is for heating the carbon powder carrier at a temperature of 1000° C. or higher and 1200° C. or lower.

15 . The method for producing the catalyst for solid polymer fuel cells according to claim 14 , comprising a step of bringing the catalyst after heat treatment into contact with an oxidizing solution at least once.

16 . The method for producing the catalyst for solid polymer fuel cells according to claim 15 , wherein the step of bringing the catalyst into contact with at least one oxidizing solution selected from a group including solutions of sulfuric acid, nitric acid, phosphorous acid, potassium permanganate, hydrogen peroxide, hydrochloric acid, chloric acid, hypochlorous acid and chromic acid.

17 . A method for producing the catalyst for solid polymer fuel cells defined in claim 4 , comprising the steps of:
preparing a mixed solution by mixing a carbon powder carrier with a platinum compound solution; adding a reducing agent to the mixed solution to support catalyst particles including platinum on the carbon powder carrier; and performing a heat treatment on the carbon powder carrier supporting the catalyst particles, wherein the step of preparing a mixed solution preparing step is for mixing the carbon powder carrier with the platinum compound solution while grinding the carbon powder carrier, and the heat treatment is for heating the carbon powder carrier at a temperature of 1000° C. or higher and 1200° C. or lower.

18 . The method for producing the catalyst for solid polymer fuel cells according to claim 17 , comprising a step of bringing the catalyst after heat treatment into contact with an oxidizing solution at least once.

19 . The method for producing the catalyst for solid polymer fuel cells according to claim 17 , wherein the step of bringing the catalyst into contact with at least one oxidizing solution selected from a group including solutions of sulfuric acid, nitric acid, phosphorous acid, potassium permanganate, hydrogen peroxide, hydrochloric acid, chloric acid, hypochlorous acid and chromic acid.

Assignees

• Tanaka Precious Metal Ind

Inventors

• Matsutani Koichi

Classifications

• H01M4/926 Primary

  on carbon or graphite · CPC title

• H01M2008/1095

  Fuel cells with polymeric electrolytes · CPC title

• H01M4/88 Primary

  Processes of manufacture · CPC title

• H01M2300/0082

  Organic polymers · CPC title

• H01M8/10

  Fuel cells with solid electrolytes · CPC title