Positive electrode active material for non-aqueous electrolyte secondary batteries, production method therefor, and non-aqueous electrolyte secondary batteries using said positive electrode active material

Patent metadata

Field	Value
Publication number	US-2020343547-A1
Application number	US-201816642912-A
Country	US
Kind code	A1
Filing date	Jul 31, 2018
Priority date	Aug 29, 2017
Publication date	Oct 29, 2020
Grant date	—

Abstract

Provided is a positive electrode active material for non-aqueous electrolyte secondary batteries for making high capacity and high output compatible, non-aqueous electrolyte secondary batteries, having the positive electrode active material adopted thereto, and a production method for a positive electrode active material in which the positive electrode active material can be easily produced in an industrial scale. A positive electrode active material for non-aqueous electrolyte secondary batteries, contains: primary particles of a lithium nickel composite oxide represented by at least General Formula: LizNi1-x-yCoxMyO2 (0.95≤z≤1.03, 0<x≤0.20, 0<y≤0.10, x+y≤0.20, and M is at least one type of element selected from Mg, Al, Ca, Ti, V, Cr, Mn, Nb, Zr, and Mo); and secondary particles configured by flocculating the primary particles, wherein an LiAl compound and an LiW compound are provided on surfaces of the primary particles.

First claim

1 . A positive electrode active material for non-aqueous electrolyte secondary batteries, comprising: primary particles of a lithium nickel composite oxide represented by at least General Formula: Li z Ni 1-x-y Co x M y O 2 (0.95≤z≤1.03, 0<x≤0.20, 0<y≤0.10, x+y≤0.20, and M is at least one type of element selected from Mg, Al, Ca, Ti, V, Cr, Mn, Nb, Zr, and Mo); and secondary particles configured by aggregating the primary particles, wherein an LiAl compound and an LiW compound are provided on surfaces of the primary particles.

2 . The positive electrode active material for non-aqueous electrolyte secondary batteries, according to claim 1 , wherein an amount of Al contained in the LiAl compound is 0.01 atom % to 0.50 atom % with respect to total number of atoms of Ni, Co, and M contained in the lithium nickel composite oxide of the primary particles.

3 . The positive electrode active material for non-aqueous electrolyte secondary batteries, according to claim 1 , wherein an amount of W contained in the LiW compound is 0.05 atom % to 0.30 atom % with respect to total number of atoms of Ni, Co, and M contained in the lithium nickel composite oxide of the primary particles.

4 . The positive electrode active material for non-aqueous electrolyte secondary batteries, according to claim 1 , wherein the LiAl compound is at least one type selected from a group consisting of LiAl 2 (OH) 7 .xH 2 O, LiH(AlO 2 ) 2 .5H 2 O, and LiAlO 2 .

5 . The positive electrode active material for non-aqueous electrolyte secondary batteries, according to claim 1 , wherein the LiW compound is at least one type selected from a group consisting of (Li 2 WO 4 ) 7 (H 2 O) 4 , Li 2 WO 4 , and Li 4 WO 5 .

6 . The positive electrode active material for non-aqueous electrolyte secondary batteries, according to claim 1 , wherein a crystallite diameter that is calculated from a peak of a (003) surface in X-ray diffraction (XRD) of the lithium nickel composite oxide is 1350 ∈ to 1500 ∈.

7 . A production method for a positive electrode active material for non-aqueous electrolyte secondary batteries containing a lithium nickel composite oxide,
the method comprising processes of (A) to (D) described below in order of the processes of (A) to (D): (A) a process of mixing a nickel compound containing nickel, cobalt, and at least one type selected from Mg, Al, Ca, Ti, V, Cr, Mn, Nb, Zr, and Mo, and a lithium compound, and then, of firing the compounds in a temperature range of 720° C. to 770° C. in an oxidizing atmosphere, and thus, of preparing a fired powder of a lithium nickel composite oxide that is represented by at least General Formula: Li z Ni 1-x-y Co x M y O 2 (here, 0.98≤z≤1.05, 0<x≤0.20, 0<y≤0.10, x+y≤0.20, and M is at least one type of element selected from Mg, Al, Ca, Ti, V, Cr, Mn, Nb, Zr, and Mo) and contains primary particles and secondary particles configured by aggregating the primary particles; (B) a process of forming a slurry such that an amount of the fired powder of the lithium nickel composite oxide is 1000 g to 2000 g with respect to 1 L of water, and of obtaining a cleaned cake by performing a water washing treatment with respect to the fired powder of the lithium nickel composite oxide that is prepared in the process of (A); (C) a process of adding an aluminum compound and a tungsten compound to the cleaned cake of the process of (B), and of mixing the compounds and the cake; and (D) a process of performing a thermal treatment with respect to the mixture of the fired powder of the lithium nickel composite oxide, the aluminum compound, and the tungsten compound that is prepared in the process of (C), and of forming an LiAl compound and an LiW compound on surfaces of the primary particles of the fired powder of the lithium nickel composite oxide.

8 . The production method for a positive electrode active material for non-aqueous electrolyte secondary batteries, according to claim 7 , wherein an amount of Al contained in the aluminum compound is 0.01 atom % to 0.50 atom % with respect to total number of atoms of Ni, Co, and M contained in the lithium nickel composite oxide.

9 . The production method for a positive electrode active material for non-aqueous electrolyte secondary batteries, according to claim 7 , wherein an amount of W contained in the tungsten compound is 0.05 atom % to 0.30 atom % with respect to the total number of atoms of Ni, Co, and M contained in the lithium nickel composite oxide.

10 . The production method for a positive electrode active material for non-aqueous electrolyte secondary batteries, according to claim 7 , wherein the thermal treatment of the process of (D) is performed at 100° C. to 600° C. in an oxygen atmosphere or a vacuum atmosphere.

11 . The production method for a positive electrode active material for non-aqueous electrolyte secondary batteries, according to claim 7 ,
wherein the nickel compound is any one of
a nickel composite hydroxide,
a nickel oxy composite hydroxide obtained by performing oxidation with respect to the nickel composite hydroxide with an oxidant,
a nickel composite oxide obtained by performing oxidation roasting with respect to the nickel oxy composite hydroxide at a temperature of 500° C. to 750° C.,
a nickel composite oxide obtained by performing oxidation roasting with respect to the nickel composite hydroxide at a temperature of 500° C. to 750° C., and
a nickel composite oxide obtained by performing oxidation roasting with respect to a mixture of the nickel composite hydroxide and the nickel oxy composite hydroxide at a temperature of 500° C. to 750° C.

12 . The production method for a positive electrode active material for non-aqueous electrolyte secondary batteries, according to claim 7 , wherein the lithium compound is at least one type selected from a group consisting of a hydroxide, an oxyhydroxide, an oxide, a carbonate, a nitrate, and a halide of lithium.

13 . The production method for a positive electrode active material for non-aqueous electrolyte secondary batteries, according to claim 7 , wherein in the process of (A), a mixing ratio of the nickel compound and the lithium compound is adjusted such that a lithium amount in the lithium compound with respect to a total amount of all metal elements in the nickel compound is at a molar ratio of 0.98 to 1.05.

14 . The production method for a positive electrode active material for non-aqueous electrolyte secondary batteries, according to claim 7 , wherein in the process of (B), a water washing temperature during the water washing treatment is adjusted to 10° C. to 40° C.

15 . The production method for a positive electrode active material for non-aqueous electrolyte secondary batteries, according to claim 7 , wherein the aluminum compound is aluminum hydroxide or aluminum oxide.

16 . The production method for a positive electrode active material for non-aqueous electrolyte secondary batteries, according to claim 7 , wherein the tungsten compound is tungsten oxide or a tungstic acid.

17 . A non-aqueous electrolyte secondary battery, comprising a positive electrode containing the positive electrode active material for a non-aqueous electrolyte secondary battery according to claim 1 .

18 . The positive electrode active material for non-aqueous electrolyte secondary batteries, according to claim 2 , wherein an amount of W contained in the LiW compound is 0.05 atom % to 0.30 atom % with respect to total number of atoms of Ni, Co, and M contained in the lithium nickel composite oxide of the primary particles.

19 . The positive el

Assignees

• Sumitomo Metal Mining Co

Inventors

• Yokoyama Jun
• Ryoshi Kazuomi

Classifications

• C01G53/82

  Compounds containing nickel, with or without oxygen or hydrogen, and containing two or more other elements · CPC title

• Y02E60/10

  Energy storage using batteries · CPC title

• C01P2004/80

  Particles consisting of a mixture of two or more inorganic phases · CPC title

• H01M10/052

  Li-accumulators · CPC title

• H01M4/366 Primary

  as layered products · CPC title