Separator for secondary battery

Patent metadata

Field	Value
Publication number	US-2019288257-A1
Application number	US-201916425977-A
Country	US
Kind code	A1
Filing date	May 30, 2019
Priority date	May 25, 2016
Publication date	Sep 19, 2019
Grant date	—

Abstract

Provided herein is a separator used for an electrochemical device such as a lithium-ion battery. The separator disclosed herein comprises a porous base material, and a protective porous layer coated on one or both surfaces of the porous base material disclosed herein, wherein the protective porous layer comprises an organic binder and an inorganic filler, and wherein the inorganic filler comprises a whisker-type material selected from the group consisting of Al 2 O 3 , SiO 2 , TiO 2 , ZrO 2 , BaO x , ZnO, CaCO 3 , TiN, AlN, MTiO 3 , K 2 O.nTiO 2 , Na 2 O.mTiO 2 , and combinations thereof, wherein x is 1 or 2; M is Ba, Sr or Ca; n is 1, 2, 4, 6 or 8; and m is 3 or 6. Also provided herein is a lithium-ion battery including the separator disclosed herein. The separator disclosed herein is excellent in terms of safety, ion permeability, and cycle characteristics.

First claim

What is claimed is:

1 . A secondary-battery separator comprising, a porous base material and a protective porous layer coated on one or both surfaces of the porous base material, wherein the protective porous layer comprises an organic binder and an inorganic filler, and wherein the inorganic filler comprises a whisker-type material selected from the group consisting of Al 2 O 3 , SiO 2 , TiO 2 , ZrO 2 , BaO x , ZnO, CaCO 3 , TiN, AlN, MTiO 3 , K 2 O.nTiO 2 , Na 2 O.mTiO 2 , and combinations thereof, wherein x is 1 or 2; M is Ba, Sr or Ca; n is 1, 2, 4, 6 or 8; and m is 3 or 6,
wherein the inorganic filler further comprises a particulate-type material selected from the group consisting of Al 2 O 3 , SiO 2 , TiO 2 , ZrO 2 , BaO x , ZnO, CaCO 3 , TiN, AlN, and combinations thereof, wherein x is 1 or 2; and wherein the protective porous layer is a two-layered structure comprising a first layer and a second layer, wherein the first layer is adjacent to the porous base material, and the second layer is on and in contact with the first layer, and wherein the particulate-type material resides in the first layer and the whisker-type material resides in the second layer.

2 . The secondary-battery separator of claim 1 , wherein the whisker-type material has a diameter from about 0.05 μm to about 3 μm, and a ratio of length to diameter from about 5 to about 300.

3 . The secondary-battery separator of claim 1 , wherein the whisker-type material is unidirectionally oriented in the TD direction.

4 . The secondary-battery separator of claim 1 , wherein the whisker-type material tends to align along the TD direction, and wherein at least 50% of the whisker-type material are lying within an angle of ±30° about an axis in the TD direction.

5 . The secondary-battery separator of claim 1 , wherein the particulate-type material has an average diameter from about 100 nm to about 10 μm.

6 . The secondary-battery separator of claim 1 , wherein the particulate-type material has an average diameter from about 1 μm to about 10 μm.

7 . The secondary-battery separator of claim 1 , wherein the protective porous layer has a thickness from 4 μm to about 20 μm.

8 . The secondary-battery separator of claim 1 , wherein the porous base material has a thickness from about 10 μm to about 30 μm.

9 . The secondary-battery separator of claim 1 , wherein the average thickness ratio of the second layer to the first layer is from about 1:3 to about 3:1.

10 . The secondary-battery separator of claim 1 , wherein the porous base material is a non-woven fabric consisting of natural or polymeric fibers, and wherein the polymeric fibers has a melting point of 200° C. or higher.

11 . The secondary-battery separator of claim 10 , wherein the polymeric fibers of the porous base material are selected from the group consisting of polyester, polyacetal, polyamide, polycarbonate, polyimide, polyetherether ketone, polyether sulfone, polyphenylene oxide, polyphenylene sulfide, polyethylene naphthalene, and combinations thereof.

12 . The secondary-battery separator of claim 11 , wherein the polyester is polyethylene terephthalate, polybutylene terephthalate or a combination thereof.

13 . The secondary-battery separator of claim 1 , wherein the organic binder is selected from the group consisting of a polyester, polyamide, polyether, polyimide, polycarboxylate, polycarboxylic acid, polyvinyl compound, polyolefin, rubber, polyvinyl pyrrolidone, polyacrylic acid, polyacrylate, polymethacrylic acid, polymethacrylate, polystyrene, polyvinyl alcohol, polyvinyl acetate, polyacrylamide, cellulose, cellulose acetate, cellulose acetate butyrate, cellulose acetate propionate, carboxymethyl cellulose, cyanoethylcellulose, cyanoethylsucrose, polyurethane, nitrile butadiene rubber (NBR), styrene butadiene rubber (SBR), latex, acrylonitrile-styrene-butadiene copolymer, fluorinated polymer, chlorinated polymer, and combinations thereof.

14 . The secondary-battery separator of claim 1 , wherein the weight ratio of the inorganic filler to the organic binder is from about 99:1 to about 1:1.

15 . The secondary-battery separator of claim 1 , wherein the difference in tensile strength of the separator along the TD direction and MD direction is about 5% or less.

16 . The secondary-battery separator of claim 1 , wherein the separator has a thickness from about 1 μm to about 80 μm.

17 . The secondary-battery separator of claim 1 , wherein the separator has a porosity from about 40% to about 97%.

18 . The secondary-battery separator of claim 1 , wherein the separator has an average pore size from about 1 μm to about 10 μm.

19 . A method for producing a battery, comprising, inserting the separator as claimed in claim 1 into the battery.

20 . A lithium battery comprising the separator as claimed in claim 1 .

Assignees

• Grst Int Ltd

Inventors

• Wong Sing Ming Tony
• Wong Sing Hung Eric
• Shen Peihua
• Hung Yuen
• Ho Kam Piu
• Wang Ranshi

Classifications

• H01M50/457

  comprising three or more layers · CPC title

• H01M50/451

  comprising layers of only organic material and layers containing inorganic material · CPC title

• H01M50/494

  Tensile strength · CPC title

• H01M50/454

  comprising a non-fibrous layer and a fibrous layer superimposed on one another · CPC title

• H01M50/423

  Polyamide resins · CPC title