Process for depositing a metal or metal alloy on a surface of a substrate including its activation

Patent metadata

Field	Value
Publication number	US-2019169751-A1
Application number	US-201716092459-A
Country	US
Kind code	A1
Filing date	May 4, 2017
Priority date	May 4, 2016
Publication date	Jun 6, 2019
Grant date	—

Abstract

A process for depositing metal or metal alloy on a substrate including treating the substrate surface with an activation solution comprising a source of metal ions so the metal ions are adsorbed on the substrate surface, treating the obtained substrate surface with a treatment solution containing an additive selected from thiols, thioethers, disulphides and sulphur containing heterocycles, and a reducing agent suitable to reduce the metal ions adsorbed on the substrate surface selected from boron based reducing agents, hypophosphite ions, hydrazine and hydrazine derivatives, ascorbic acid, iso-ascorbic acid, sources of formaldehyde, glyoxylic acid, sources of glyoxylic acid, glycolic acid, formic acid, sugars, and salts of aforementioned acids; and subsequently treating the substrate surface with a metallizing solution comprising a source of metal ions to be deposited such that a metal or metal alloy is deposited thereon.

First claim

1 . A process for depositing a metal or metal alloy on at least one surface of a substrate comprising the steps of
(a) providing a substrate; (b) treating the surface of said substrate with an activation solution comprising at least one source of metal ions selected from the group consisting of sources of ruthenium ions, sources of rhodium ions, sources of palladium ions, sources of osmium ions, sources of iridium ions, sources of platinum ions, sources of copper ions, sources of silver ions, sources of nickel ions, sources of cobalt ions, sources of gold ions and mixtures thereof such that at least one portion of said metal ions is being adsorbed on the surface of said substrate; (c) treating the surface of said substrate obtained from step (b) with a treatment solution comprising
i) at least one additive independently selected from the group consisting of thiols, thioethers, disulphides and sulphur containing heterocycles, and
ii) at least one reducing agent suitable to reduce the metal ions adsorbed on the surface of said substrate selected from the group consisting of boron based reducing agents, sources of hypophosphite ions, hydrazine and hydrazine derivatives, ascorbic acid, iso-ascorbic acid, sources of formaldehyde, glyoxylic acid, sources of glyoxylic acid, glycolic acid, formic acid, sugars, and salts of aforementioned acids; and
(d) treating the surface obtained from step (c) of said substrate with a metallizing solution comprising a solvent and at least one source of metal ions to be deposited such that a metal or metal alloy is deposited thereon.

2 . The process according to claim 1 characterised in that the at least one reducing agent is a boron based reducing agent selected from the group consisting of amino boranes, ammonia borane, borohydrides, borane and homologues thereof.

3 . The process according to claim 1 characterised in that the concentration of the at least one reducing agent ranges from 0.1 to 500 mmol/L.

4 . The process according to claim 1 characterised in that the metallizing solution is an electroless metallizing solution comprising said at least one source of metal ions, at least one complexing agents and at least one reducing agent.

5 . The process according to claim 4 characterised in that the at least one source of metal ions in the metallizing solution is selected from the group consisting of sources of copper ions, of sources of nickel ions, of sources of cobalt ions and mixtures thereof.

6 . (canceled)

7 . The process according to claim 1 characterised in that the at least one surface of the substrate is selected from the group consisting of metallic surfaces, non-metallic surfaces and combinations thereof.

8 . The process according to claim 1 characterised in that the substrate is selected from the group consisting of printed circuit boards, printed circuit foils, interposers, chip carriers, IC substrates, semiconductor wafers, circuit carriers, interconnect devices and precursors for any of the aforementioned.

9 . The process according to claim 1 characterised in that the additives selected from the group consisting of thiols, thioethers, disulphides and sulphur containing heterocycles are contained in the treatment solution in a total concentration of 0.1 μg/L to 1 g/L.

10 . (canceled)

11 . (canceled)

12 . (canceled)

13 . The process according to claim 1 characterised in that the thiols are represented by the following formula (I)
R1-SH   (I)

wherein R1 is independently selected from the group consisting of substituted and unsubstituted aliphatic groups, substituted and unsubstituted aryl groups and substituted and unsubstituted heteroaryl groups.

14 . The process according to claim 13 characterised in that the thiols are selected from the group consisting of ethylthiol, 1-propylthiol, 2-propylthiol, 1-butylthiol, 2-butylthiol, 2-methylpropane-1-thiol, ethane-1,2-dithiol, propane-1,2-dithiol, propane-1,3-dithiol, butane-1,2-dithiol, butane-1,3-dithiol, butane-1,4-dithiol, butane-2,3-dithiol, 2-methylpropane-1,2-dithiol, 1H-benzo[d]imidazole-2-thiol, 1-methyl-1H-benzimidazole-2-thiol, 2-mercaptophenol, 4-mercaptophenol, thiosalicylic acid and 6-mercaptopyridine-3-carboxylic acid and the respective hydroxy and/or amino and/or carboxyl derivatives of the aforementioned.

15 . The process according to claim 1 characterised in that the thioethers are represented by the following formula (II)
R2-S—R3   (II)

wherein R2 and R3 are independently from each other selected from the group consisting of substituted and unsubstituted aliphatic groups, substituted and unsubstituted aryl groups and substituted and unsubstituted heteroaryl groups.

16 . The process according to claim 15 characterised in that the thioethers are selected from the group consisting of diethylsulphane, dipropylsulphane, dibutylsulphane, ethylproylsulphane, ethylbutylsulphane, propylbutylsulphane, 2(methylthio)benzoic acid, 4,4′-thiodiphenol, and the respective the respective hydroxy and/or amino and/or carboxyl derivatives of the aforementioned.

17 . The process according to claim 1 characterised in that the disulphides are represented by the following formula (III)
R4-S—S—R5   (III)

wherein R4 and R5 are independently from each other selected from the group consisting of substituted and unsubstituted aliphatic groups, substituted and unsubstituted aryl groups and, substituted and unsubstituted heteroaryl groups.

18 . The process according to claim 17 characterised in that the disulphides are selected from the group consisting of cystamine, 2-hydroxyethyl disulphide, 3-hydroxypropyldisulphide, 4-hydroxybutyldisulphide, dithiodiglycolic acid, 3,3′-dithiodipropionic acid, 4,4′-dithiodibutyric acid, bis(2-aminophenyl) disulphide, bis(4-aminophenyl) disulphide, 2,2′-dithiodibenzoic acid, difurfuryl disulphide, D-penicillamine disulphide, 3,3′-dihydroxydiphenyl disulphide, methyl furfuryl disulphide, 1,2-bis(2,2-diethoxyethyl)disulphide, 2,2′-dithiodipyridine and 6,6′-dithiodinicotinic acid.

19 . The process according to claim 1 characterised in that the sulphur containing heterocycles comprise
at least one ring-system which comprises carbon atoms, at least one sulphur atom and optionally at least one nitrogen atom,
wherein the total amount of said carbon, sulphur and nitrogen atoms in the at least one ring-system ranges from 3 to 13 atoms, preferably from 4 to 12, more preferably from 5 to 9;

and wherein
the sulphur containing heterocycles are substituted or unsubstituted; and
the sulphur containing heterocycles are saturated or unsaturated, preferably aromatic.

20 . The process according to claim 19 characterised in that the sulphur containing heterocycles are selected from the group consisting of unsubstituted and substituted thiophene, unsubstituted and substituted thiazole, unsubstituted and substituted thiopyran, unsubstituted and substituted benzothiazole, unsubstituted and substituted thiabendazole, unsubstituted and substituted benzothiazole, unsubstituted and substituted thiazole, unsubstituted and substituted thiophene, unsubstituted and substituted tetrahydrothiophene, unsubstituted and substituted thiazolidine, unsubstituted and substituted 1,3-Dithiolane, unsubstituted and substituted 1,4-dithiane, unsubstituted and substituted 1,3-dithiane, unsubstituted and substituted thiomorpholine, unsubstituted and substituted tetrahydrothiopyran.

21 . The process according to claim 1 characterised in that the trea

Assignees

• Atotech Deutschland Gmbh

Inventors

• Wendeln Christian
• Stamp Lutz
• Dosse Bexy
• Wurdinger Kay
• Krilles Gerson
• Nguyen Tang Cam Lai

Classifications

• C23C18/40 Primary

  using reducing agents · CPC title

• C23C18/2066 Primary

  Use of organic or inorganic compounds other than metals, e.g. activation, sensitisation with polymers · CPC title

• C23C18/30

  Activating {or accelerating or sensitising with palladium or other noble metal} · CPC title

• C23C18/1692

  Heat-treatment · CPC title

• C23C18/1844

  with use of organic or inorganic compounds other than metals, first · CPC title