Steel for Induction Hardening

Patent metadata

Field	Value
Publication number	US-2019153574-A1
Application number	US-201716316695-A
Country	US
Kind code	A1
Filing date	Jul 19, 2017
Priority date	Jul 19, 2016
Publication date	May 23, 2019
Grant date	—

Abstract

A steel for induction hardening according to the present invention includes a chemical composition consisting of, in mass percent: C: 0.58 to 0.68%, Si: 0.70 to 1.40%, Mn: 0.20 to 1.40%, P: less than 0.020%, S: less than 0.020%, Al: 0.005 to 0.060%, N: 0.0020 to 0.0080%, 0: 0.0015% or less, V: 0.01 to 0.25%, B: 0.0003 to 0.0040%, Ti: 0.010 to 0.050%, and Ca: 0.0005 to 0.005%, with the balance being Fe and impurities, and satisfies Formulae (1) to (3). The steel microstructure is made up of ferrite and pearlite. A ratio of a number of composite inclusions is 20% or more.
C+Si/7+Mn/5+Cr/9+Mo/2.5≤1.05   (1)

C+Si/10+Mn/20+Cr/25≥0.70   (2)

Cr/Si≤0.20   (3)

First claim

1 . A steel for induction hardening comprising a chemical composition consisting of, in mass percent:
C: 0.58 to 0.68%; Si: 0.70 to 1.40%; Mn: 0.20 to 1.40%; P: less than 0.020%; S: less than 0.020%; Al: 0.005 to 0.060%; N: 0.0020 to 0.0080%; 0: 0.0015% or less; V: 0.01 to 0.25%; B: 0.0003 to 0.0040%; Ti: 0.010 to 0.050%; Ca: 0.0005 to 0.005%; Cr: 0 to 0.15%; Cu: 0 to 0.50%; Ni: 0 to 0.30%; Mo: 0 to 0.20%; and Nb: 0 to 0.05%, with the balance being Fe and impurities, and satisfying Formulae (1) to (3), wherein a steel microstructure is made up of ferrite and pearlite, where an area fraction of the pearlite is 85% or more, and in the steel, a ratio of a number of composite inclusions to a total number of Al 2 O 3 inclusions and the composite inclusions is 20% or more, and the composite inclusions contain, in mass percent, 2.0% or more of SiO 2 and 2.0% or more of CaO, with the 99% or more of the balance being Al 2 O 3 ;
C+Si/7+Mn/5+Cr/9+Mo/2.5≤1.05   (1)

C+Si/10+Mn/20+Cr/25≥0.70   (2)

Cr/Si≤0.20   (3)

where, symbols of elements in Formulae (1) to (3) are to be substituted by contents of corresponding elements (mass percent).

2 . The steel for induction hardening according to claim 1 , wherein the chemical composition contains one or more types selected from the group consisting of:
Cr: 0.05 to 0.15%; Cu: 0.03 to 0.50%; Ni: 0.03 to 0.30%; and Mo: 0.01 to 0.20%.

3 . The steel for induction hardening according to claim 1 , wherein the chemical composition contains Nb: 0.01 to 0.05%.

4 . The steel for induction hardening according to claim 2 , wherein the chemical composition contains Nb: 0.01 to 0.05%.

Assignees

• Nippon Steel & Sumitomo Metal Corp

Inventors

• Shiga Akira
• Neishi Yutaka
• Miyanishi Kei

Classifications

• C22C38/002

  containing In, Mg, or other elements not provided for in one single group C22C38/001 - C22C38/60 · CPC title

• C22C38/54 Primary

  with boron · CPC title

• C22C38/50

  with titanium or zirconium · CPC title

• C22C38/26

  with niobium or tantalum · CPC title

• C21D2211/005

  Ferrite · CPC title