Polyethylene based laminated film structure with barrier properties

Patent metadata

Field	Value
Publication number	US-2018370202-A1
Application number	US-201616061920-A
Country	US
Kind code	A1
Filing date	Dec 13, 2016
Priority date	Dec 15, 2015
Publication date	Dec 27, 2018
Grant date	—

Abstract

Laminated film structure comprising at least one first film having a thin ceramic or metal coating, being laminated to a second film and whereby the laminated film structure is based on polyethylene only, i.e. polymers other than polyethylene are substantially absent and whereby the laminated film structure has good barrier properties

First claim

1 . A laminated polyethylene based film structure having barrier properties, the laminated polyethylene based film structure comprising
(1) one oriented first film comprising:
a) at least one layer A based on a polyethylene polymer having a density of from 890 to 980 kg/m 3 , and
b) optionally at least one layer B, wherein layer B comprises: a high density polyethylene (HDPE) having a density of from 940 to 970 kg/m 3 , a medium density polyethylene (MDPE) having a density of from 925 to 940 kg/m 3 , or a linear low density polyethylene (LLDPE) having a density of 910 up to 950 kg/m 3 ,
wherein the oriented first film:
is at least oriented in machine direction (MDO film) in a draw ratio of from 1:1.5 to 1:12 and
has a film thickness after orientation of from 10 to 50 μm, and
has one surface that is coated by a thin vapor deposited barrier ceramic or metal layer, such that the oriented first film as a coated surface;

and (2) a second film laminated onto the coated surface of the oriented first film, wherein the second film comprises
c) at least one sealant layer C based on a polyethylene polymer, and
d) optionally a high density polyethylene (HDPE) barrier layer D,
and wherein polymers other than ethylene based polymers are substantially absent from the laminated polyethylene based film structure.

2 . The laminated polyethylene based film structure according to claim 1 , wherein the polyethylene polymer of layer A is selected from the group consisting of a high density polyethylene (HDPE), a medium density polyethylene (MDPE), a linear low density polyethylene (LLDPE), a blend of a linear low density polyethylene (LLDPE) with a high pressure low density polyethylene (LDPE), and a blend of an ethylene based plastomer with a high pressure low density polyethylene (LDPE).

3 . The laminated polyethylene based film structure according to claim 1 , wherein the polyethylene polymer of layer A is a linear low density polyethylene (LLDPE) with an MFR 2 (190° C., 2.16 kg, ISO 1133) in the range of from 0.01 to 20 g/10 min and a density in the range of from 910 to 950 kg/m 3 .

4 . The laminated polyethylene based film structure according to claim 3 , wherein the linear low density polyethylene (LLDPE) contains at least one or two C 3 -C 10 alpha-olefin comonomer(s), wherein the LLDPE is produced using a Ziegler-Natta catalyst.

5 . The laminated polyethylene based film structure according to claim 1 , wherein the oriented first film includes at least one layer B, and wherein the at least one layer B comprises a layer of a high density polyethylene (HDPE) having a density of from 940 to 970 kg/m 3 .

6 . The laminated polyethylene based film structure according to claim 1 , wherein the oriented first film further comprises an additional layer E, wherein layer E comprises a high density polyethylene (HDPE) having a density of from 940 to 970 kg/m 3 , a medium density polyethylene (MDPE) having a density of from 925 to 940 kg/m 3 , or a linear low density polyethylene (LLDPE) having a density of from 910 to 950 kg/m 3 .

7 . The laminated polyethylene based film structure according to claim 6 , wherein the oriented first film:
is an unblocked film having the structure E/A/B, or is a blocked film having the structure E/A/BL/BL/A/B or E/A/A/A/BL/BL/A/A/A/B, wherein BL is a blocking layer comprising a blend of a LLDPE as used in layer A and an ethylene based plastomer with a density below 915 kg/m 3 .

8 . The laminated polyethylene based film structure according to claim 1 , wherein the oriented first film is only oriented in machine direction.

9 . The laminated polyethylene based film structure according to claim 8 , wherein the machine direction oriented first film has
i) a tensile modulus (according to ISO 527-3) in machine direction measured on a 25 μm MDO film at room temperature of at least 800 MPa, ii) a tensile modulus (according to ISO 527-1 and 527-3) in machine direction measured on a 25 μm MDO film at 70° C. of at least 100 MPa, iii) a ratio of i) to ii) of below 10, iv) a gloss (20°) according to ASTM D2457 for a film thickness of 25 μm of at least 30%, and v) a haze according to ASTM D1003 for a film thickness of 25 μm of below 30%.

10 . The laminated polyethylene based film structure according to claim 1 , wherein the coated surface of the oriented first film is coated with an aluminum coating, an AlOx coating, or a SiOx coating.

11 . The laminated polyethylene based film structure according to claim 1 , wherein the laminated polyethylene based film structure shows an oxygen transmission rate (OTR; ASTM F-1927; 23° C., 50% RH) of lower than 50 cm 3 /m 2 /1 day and a water vapor transmission rate (WVTR, ASTM F-1249; 37.8° C., 90% humidity) of below 5 g/m 2 /1 day.

12 . A laminated article comprising the laminated polyethylene based film structure of claim 1 .

13 . A method of se of the laminated polyethylene based film structure of claim 1 , the method comprising using the laminated polyethylene based film for producing vertical or horizontal form fill seal packaging, pouches, sacks, or bags.

14 . The laminated polyethylene based film structure according to claim 6 , wherein layer E is the same as layer B.

15 . The laminated polyethylene based film structure according to claim 6 , wherein layer E is different than layer B.

Assignees

• Borealis Ag

Inventors

• Niedersüss Peter
• Ackermans Nina
• Cavacas Paulo
• De Wever Willem
• Defoer Johan

Classifications

• B32B2307/514

  Oriented · CPC title

• B32B27/08 Primary

  of synthetic resin · CPC title

• B32B2255/205

  Metallic coating · CPC title

• B32B2307/7246

  Water vapor barrier · CPC title

• B32B2255/10

  on synthetic resin layer or on natural or synthetic rubber layer · CPC title