Method of Preparing Lithium Ion Battery Cathode Materials

Patent metadata

Field	Value
Publication number	US-2018366723-A1
Application number	US-201615780238-A
Country	US
Kind code	A1
Filing date	Nov 25, 2016
Priority date	Jan 4, 2016
Publication date	Dec 20, 2018
Grant date	—

Abstract

Provided herein is a method for preparing a surface modified cathode material for lithium-ion battery, wherein the cathode material comprises lithium multi-metal composite oxide particles capped with a thin film of an oxide of the metal, wherein the lithium multi-metal composite oxide is represented by Li 1+z Ni x Mn y Co 1-x-y O 2 ; and wherein z is from 0 to 0.2; x is from 0.35 to 0.8; y is from 0.1 to 0.45; and the metal is one or more elements selected from the group consisting of Fe, Mn, Al, Mg, Zn, Ti, La, Ce, Sn, Zr, Ru and combination thereof. The cathode material disclosed herein exhibits a high initial specific capacity from 150 mAh/g to 200 mAh/g, possesses good safety characteristics and shows impressive energy retention of about 91% after 1000 cycles.

First claim

What is claimed is:

1 . A method of preparing a cathode material for a lithium-ion battery cell, comprising the steps of:
1) dissolving a salt of nickel, a salt of manganese, and a salt of cobalt in de-ionized water to obtain an aqueous solution, wherein a molar ratio of the metal elements Ni to Mn to Co is 1.2-7.2 to 1.5-3.1 to 1-2.2; 2) adding the aqueous solution into an alkaline solution to form a suspension of multi-element metal hydroxide particles; 3) adding a solution of a salt of a metal into the suspension to form a solid product comprising a precipitate of a hydroxide of the metal on the surface of the multi-element metal hydroxide particles; 4) drying the suspension containing the solid product to obtain a multi-element precursor; 5) mixing the multi-element precursor with one or more lithium salts to obtain a first mixture, wherein a molar ratio of the metal element Li to a total amount of the metal elements Ni, Mn, Co and the metal is 1.02-1.2 to 1; 6) dispersing the first mixture in an aqueous solvent to form a slurry; 7) homogenizing the slurry by a homogenizer; 8) drying the slurry to obtain a solid mixture; 9) calcinating the solid mixture under an atmosphere with an oxygen content higher than 21% at a temperature from about 600° C. to about 900° C. for a time period from about 4 hours to about 12 hours to obtain a calcinated product; and 10) cooling the calcinated product to room temperature, crushing the calcinated product, and isolating particles of the calcinated product having a particle size D50 in the range from about 5 μm to about 15 μm to obtain the cathode material; wherein the cathode material comprises lithium multi-metal composite oxide particles capped with a thin film of an oxide of the metal, wherein the lithium multi-metal composite oxide is represented by Li 1+z Ni x Mn y Co 1-x-y O 2 ; and wherein z is from 0 to 0.2; x is from 0.35 to 0.8; y is from 0.1 to 0.45; and the metal is one or more elements selected from the group consisting of Fe, Mn, Al, Mg, Zn, Ti, La, Ce, Sn, Zr, Ru and combinations thereof.

2 . The method of claim 1 , wherein a total molar concentration of the metal elements in the aqueous solution is from about 0.9 mol/L to about 1.6 mol/L.

3 . The method of claim 1 , wherein the alkaline solution comprises a base selected from the group consisting of LiOH, NaOH, KOH, NH 3 .H 2 O, Be(OH) 2 , Mg(OH) 2 , Ca(OH) 2 , Li 2 CO 3 , Na 2 CO 3 , NaHCO 3 , K 2 CO 3 , KHCO 3 , (CH 3 ) 4 NOH and combinations thereof.

4 . The method of claim 1 , wherein a pH value in step 2) is maintained at a range from about 10 to about 12 by addition of the alkaline solution and the solution is stirred for a time period from about 15 minutes to about 2 hours.

5 . The method of claim 1 , wherein the salt of nickel, the salt of manganese, the salt of cobalt, and the salt of the metal comprise an anion selected from the group consisting of sulfate, nitrate, acetate, chloride and combinations thereof.

6 . The method of claim 1 , wherein a molar concentration in the solution of the salt of the metal is from about 0.1 mol/L to about 0.5 mol/L and the solution is stirred for a time period from about 15 minutes to about 2 hours.

7 . The method of claim 1 , wherein the drying process in step 4) is performed by a spray dryer.

8 . The method of claim 1 , wherein the solid product is separated from the suspension before drying and the solid product is dried by a microwave dryer or a microwave vacuum dryer.

9 . The method of claim 1 , wherein the lithium salt is LiOH, Li 2 CO 3 , LiF or a combination thereof.

10 . The method of claim 1 , wherein the aqueous solvent for dispersing the first mixture is water, ethanol, isopropanol, butanol or a combination thereof.

11 . The method of claim 1 , wherein the homogenizer is a blender, a mill, an ultrasonicator, a rotor-stator homogenizer, or a high pressure homogenizer.

12 . The method of claim 10 , wherein the ultrasonicator is a probe-type ultrasonicator or an ultrasonic flow cell.

13 . The method of claim 1 , wherein the slurry is homogenized for a time period from about 1 hour to about 10 hours, or a time period from about 2 hours to about 4 hours.

14 . The method of claim 11 , wherein the ultrasonicator is operated at a power density from about 10 W/L to about 100 W/L, or from about 40 W/L to about 60 W/L.

15 . The method of claim 1 , wherein the drying process in step 8) is performed by a double-cone vacuum dryer, a microwave dryer, or a microwave vacuum dryer.

16 . The method of claim 1 , wherein the solid mixture has a particle size D50 in the range from about 1 μm to about 10 μm.

17 . The method of claim 1 , wherein the calcination process is performed by a push-plate tunnel furnace, or a rotary furnace.

18 . The method of claim 1 , wherein the crushing process is performed by a ball mill, hammer mill, a jet mill, or a high pressure dispersion mill.

19 . The method of claim 1 , wherein the isolating step is performed by passing through a mesh sieve having a range from about 200 to about 400.

20 . The method of claim 1 , wherein the thin film of the oxide of the metal capped on the surface of the lithium multi-metal composite oxide particles has a thickness from about 500 nm to about 1 μm.

Assignees

• Grst Int Ltd

Inventors

• Shen Peihua
• Wong Sing Hung Eric

Classifications

• H01M4/366 Primary

  as layered products · CPC title

• C01P2006/12

  Surface area · CPC title

• H01M4/525

  of mixed oxides or hydroxides containing iron, cobalt or nickel for inserting or intercalating light metals, e.g. LiNiO2, LiCoO2 or LiCoOxFy · CPC title

• H01M4/505

  of mixed oxides or hydroxides containing manganese for inserting or intercalating light metals, e.g. LiMn2O4 or LiMn2OxFy · CPC title

• C01P2004/61

  Micrometer sized, i.e. from 1-100 micrometer · CPC title