Seawater-resistant stainless clad steel

Patent metadata

Field	Value
Publication number	US-2018298477-A1
Application number	US-201816013302-A
Country	US
Kind code	A1
Filing date	Jun 20, 2018
Priority date	Mar 8, 2012
Publication date	Oct 18, 2018
Grant date	—

Abstract

Disclosed is a manufacturing method for a seawater-resistant stainless clad steel including a cladding material made of stainless steel having a pitting index represented by Cr[mas %]+3.3Mo[mass %]+16N[mass %], of 35.0 or more and a microstructure in a surface portion thereof including, by area ratio, less than 2.0% of a σ phase. The method including the steps of performing a mechanical treatment from at least one of grindstone polishing and belt polishing and performing at least one of an electrolytic treatment in acid solutions or in neutral salt solutions, and a pickling treatment, to manufacture the stainless clad steel having dynamic friction coefficients in the rolling direction and in a direction at a right angle to the rolling direction, determined in accordance with JIS K 7125, both of 0.05 or less.

First claim

1 .- 5 . (canceled)

6 . A manufacturing method for a seawater-resistant stainless clad steel comprising a cladding material made of stainless steel having a pitting index represented by Cr[mass %]+3.3Mo[mass %]+16N[mass %], of 35.0 or more and a microstructure in a surface portion thereof including, by area ratio, less than 2.0% of a σ phase,
the method comprising the steps of:
performing a mechanical treatment from at least one of grindstone polishing and belt polishing; and
performing at least one of an electrolytic treatment in acid solutions or in neutral salt solutions, and a pickling treatment, to manufacture the stainless clad steel having dynamic friction coefficients in the rolling direction and in a direction at a right angle to the rolling direction, determined in accordance with JIS K 7125, both of 0.05 or less.

7 . The method according to claim 6 , wherein a crystal grain size of the cladding material determined in accordance with JIS G 0551 is 6.0 or more.

8 . The method according to claim 6 , wherein the cladding material has a chemical composition including, by mass %, B:0.0010% to 0.0050%.

9 . The method according to claim 6 , further comprising the steps of:
bonding the cladding material and a base material to form a bonded material as a slab; reheating the slab at a temperature of 900° C. to 1100° C.; hot-rolling the reheated slab to form a hot-rolled plate; cooling the hot-rolled plate at a cooling rate of 0.2° C./s to 20° C./s without performing a normalizing treatment; and subsequently performing the mechanical treatment and performing at least one of the electrolytic treatment and the pickling treatment.

10 . The method according to claim 6 , further comprising the steps of:
bonding the cladding material and a base material to form a bonded material as a slab; reheating the slab at a temperature of 950° C. to 1150° C.; hot-rolling the reheated slab to form a hot-rolled plate; performing a normalizing treatment on the hot-rolled plate under the conditions of a heating temperature of 800° C. to 1000° C.; cooling the treated plate at a cooling rate of 1.0° C./s to 20° C./s; and subsequently performing the mechanical treatment and performing at least one of the electrolytic treatment and the pickling treatment.

11 . The method according to claim 6 , wherein the stainless clad steel has a ratio of the dynamic friction coefficients (L/C) in the rolling direction (L) and in a direction (C) at a right angle to the rolling direction of 0.50 or more and 2.0 or less.

12 . The method according to claim 6 , wherein the cladding material has a chemical composition including, by mass %, C: 0.03% or less, Si: 1.50% or less, Mn: 2.0% or less, P: 0.04% or less, S: 0.03% or less, Cu: 2.0% or less, Ni: 17.0% to 25.0%, Cr: 19.0% to 26.0%, Mo: 3.0% to 6.0%, and N: 0.10% to 0.35%.

Assignees

• Jfe Steel Corp

Inventors

• Yazawa Yoshihiro
• Kishi Keiichiro
• Tachibana Shunichi
• Hoshino Toshiyuki

Classifications

• C21D8/0226 Primary

  Hot rolling · CPC title

• C22C38/54 Primary

  with boron · CPC title

• C25F3/06

  of iron or steel · CPC title

• C22C38/04

  containing manganese · CPC title

• C21D6/002

  containing Cr (C21D6/004 takes precedence) · CPC title