Method for preparing styrene-butadiene rubber and styrene-butadiene rubber

Patent metadata

Field	Value
Publication number	US-2018215902-A1
Application number	US-201615741538-A
Country	US
Kind code	A1
Filing date	Dec 28, 2016
Priority date	Dec 28, 2015
Publication date	Aug 2, 2018
Grant date	—

Abstract

The present invention relates to a method for preparing styrene-butadiene rubber in which a molecular weight modifier containing two or more components is used in a polymerization reaction and each of the two or more components is added at a optimal time, and the method is capable of improving physical properties of the prepared styrene-butadiene rubber, and styrene-butadiene rubber prepared thereby. The styrene-butadiene rubber prepared according to the preparation method of the present invention has improvement in characteristics such as tensile strength, elongation, etc., and thus may be usefully used in the production of a tire having environmental friendliness, abrasion resistance, and the like.

First claim

1 . A method for preparing styrene-butadiene rubber (SBR), the method comprising a polymerization in an emulsion state by using a composition including 1) a styrene-based monomer; 2) a butadiene-based monomer; and 3) a molecular weight modifier comprising t-dodecylmercaptan and pentamethylheptanethiol (PMHT),
wherein the t-dodecylmercaptan and the pentamethylheptanethiol are included in a weight ratio of 70:30 to 95:5, and the pentamethylheptanethiol is added at the time when the polymerization exhibits a conversion rate of 10% to 55%.

2 . The method of claim 1 , wherein the pentamethylheptanethiol comprises at least one selected from the group consisting of 2,2,4,4,6-pentamethylheptane-4-thiol, 2,4,4,6,6-pentamethylheptane-2-thiol, 2,3,4,6,6-pentamethylheptane-2-thiol, and 2,3,4,6,6-pentamethylheptane-3-thiol.

3 . The method of claim 1 , wherein the pentamethylheptanethiol comprises the 2,2,4,4,6-pentamethylheptane-4-thiol in an amount of 65 mol % or more based on a total mole number of the pentamethylheptanethiol.

4 . The method of claim 1 , wherein the t-dodecylmercaptan and the pentamethylheptanethiol are included in a weight ratio of 80:20 to 95:5.

5 . The method of claim 1 , wherein the molecular weight modifier comprises the 2,2,4,4,6-pentamethylheptane-4-thiol in an amount of 5 mol % or more based on a total mole number of the molecular weight modifier.

6 . The method of claim 1 , wherein the composition comprises the molecular weight modifier in an amount of 0.05 to 2 parts by weight based on 100 parts by weight of the composition.

7 . Styrene-butadiene rubber which is prepared by the method of claim 1 and has a tensile strength (TS) ranging from 250 kg·f/cm 2 to 300 kg·f/cm 2 , and a tensile elongation (s) ranging from 370% to 400%.

8 . The styrene-butadiene rubber of claim 7 , wherein the 300% modulus value of the styrene-butadiene rubber is 190 to 200.

Assignees

• Lg Chemical Ltd

Inventors

• Lee Jae Min
• Lee Se Eun
• Kim Byoung Yun
• Jo In Sung
• Choi Woo Seok

Classifications

• C08F2/26

  anionic · CPC title

• C08L9/06 Primary

  Copolymers with styrene · CPC title

• C08F2/22

  Emulsion polymerisation · CPC title

• C08F236/10 Primary

  with vinyl-aromatic monomers · CPC title

• C08F2/38

  Polymerisation using regulators, e.g. chain terminating agents {, e.g. telomerisation} · CPC title