Thermoset foams and manufacturing process

Patent metadata

Field	Value
Publication number	US-2018201747-A1
Application number	US-201615569095-A
Country	US
Kind code	A1
Filing date	Apr 19, 2016
Priority date	Apr 27, 2015
Publication date	Jul 19, 2018
Grant date	—

Abstract

A process for the manufacture of a solid thermoset foam includes the following successive stages: (a) making available an expandable and thermosetting composition containing a sugar and an acid catalyst chosen from strong acids, phosphoric acid and acidic inorganic salts, (b) introducing the expandable and thermosetting composition into a mold or applying the expandable composition to a support as a film with a thickness at least equal to 1 mm, and (c) heating the expandable and thermosetting composition to a temperature at least equal to 140° C., so as to form a block of solid thermoset foam.

First claim

1 . A process for manufacturing a solid thermoset foam comprising the following successive stages:
(a) making available an expandable and thermosetting composition containing:
a sugar, and
an acid catalyst chosen from strong acids, phosphoric acid and acidic inorganic salts, a concentration of strong acids being at least equal to 0.1 N, a concentration of phosphoric acid being at least equal to 0.1 mol/l and a concentration of acidic inorganic salts being such that the pH of the composition is less than or equal to 3, the acidic inorganic salts being chosen from aluminum, gallium, copper, zinc, silver, nickel, iron and lead sulfates, nitrates, chlorides and bromides,
(b) introducing the expandable and thermosetting composition into a mold or applying the expandable composition to a support as a film with a thickness at least equal to 1 mm, and (c) heating the expandable and thermosetting composition to a temperature at least equal to 140° C., so as to form a block of solid thermoset foam.

2 . The process as claimed in claim 1 , wherein, when the acid catalyst is chosen from a group formed by strong acids and phosphoric acid, the acid/sugar molar ratio is less than ⅙.

3 . The process as claimed in claim 1 , wherein the thickness of the film is at least equal to 2 mm.

4 . The process as claimed in claim 1 , wherein the block of solid thermoset foam is a slab.

5 . The process as claimed in claim 1 , wherein the expandable composition contains at most 60% by weight of water.

6 . The process as claimed in claim 1 , wherein the sugar represents at least 70% of the dry weight of the expandable composition.

7 . The process as claimed in claim 1 , wherein the sugar is chosen from reducing sugars and nonreducing sugars.

8 . The process as claimed in claim 7 , wherein the sugar is a reducing sugar chosen from glucose and starch hydrolysates.

9 . The process as claimed in claim 1 , wherein the concentration of strong acid is between 0.1 and 1.5 N.

10 . The process as claimed in claim 1 , wherein the expandable composition additionally contains up to 20% by weight, with respect to the dry weight of the total expandable composition, of one or more inorganic or organic fillers.

11 . A solid foam produced by the process as claimed in claim 1 .

12 . The solid foam as claimed in claim 11 , wherein the solid foam exhibits a density of between 30 and 60 kg/m 3 .

13 . The solid foam as claimed in claim 11 , wherein the solid foam exhibits a closed porosity.

14 . The solid foam as claimed in claim 11 , wherein a mean diameter of pores of the solid foam, determined by X-ray tomography, is between 100 and 800 nm.

15 . A composition containing:
a sugar, and an acid catalyst chosen from strong acids, phosphoric acid and acidic inorganic salts, wherein the composition is an expandable and thermosetting composition for manufacturing an insulating product of foam type.

16 . The process as claimed in claim 1 , wherein, when the acid catalyst is chosen from a group formed by strong acids and phosphoric acid, the acid/sugar molar ratio is between 1/34 and 1/10.

17 . The process as claimed in claim 1 , wherein the thickness of the film is at least equal to 10 mm.

18 . The process as claimed in claim 1 , wherein the expandable composition contains at most 5% by weight of water.

19 . The process as claimed in claim 1 , wherein the sugar represents at least 90% of the dry weight of the expandable composition.

20 . The process as claimed in claim 1 , wherein the sugar is chosen from reducing sugars.

Assignees

• Saint Gobain Isover

Inventors

• Savonnet Marie
• Salomon Pierre
• Obert Edouard

Classifications

• C08J9/02 Primary

  using blowing gases generated by the reacting monomers or modifying agents during the preparation or modification of macromolecules · CPC title

• C08J2205/042

  Nanopores, i.e. the average diameter being smaller than 0,1 micrometer · CPC title

• C08J2205/052

  Closed cells, i.e. more than 50% of the pores are closed · CPC title

• C08J2361/02

  Condensation polymers of aldehydes or ketones only · CPC title

• C08J2203/10

  Water or water-releasing compounds · CPC title