Silicon oxide-coated iron oxide composition for coating comprising iron oxide particles coated with silicon oxide

Patent metadata

Field	Value
Publication number	US-2018200159-A1
Application number	US-201815923390-A
Country	US
Kind code	A1
Filing date	Mar 16, 2018
Priority date	Oct 5, 2015
Publication date	Jul 19, 2018
Grant date	—

Abstract

The present invention provides a composition for coating having high ultraviolet ray protection ability for a coating material, and properties required for a coating material such as texture, appearance, designability and weather resistance. The composition is a silicon oxide-coated iron oxide composition for coating comprising iron oxide particles, a primary particle diameter of which is 1 nm or more and 50 nm or less, wherein at least a part of the surface of said iron oxide particles is coated with silicon oxide, and wherein said composition comprises an iron oxide particle dispersion having the average molar absorption coefficient of 1500 LI(mol·cm) or more for the light of the wavelengths from 190 nm to 380 nm in a state that said coated iron oxide particles are dispersed in a dispersion medium. It is preferable that the transmittance of said iron oxide particle containing dispersion for the light of the wavelengths from 200 nm to 420 nm is 2.0% or less, and the transmittance of said iron oxide particle containing dispersion for the light of the wavelengths from 620 nm to 780 nm is 80% or more.

First claim

1 . A silicon oxide-coated iron oxide composition for coating comprising iron oxide particles, wherein a primary particle diameter of the iron oxide particles is 1 nm or more and 50 nm or less,
wherein at least a part of the surface of said iron oxide particles is coated with silicon oxide, wherein said iron oxide particles coated with silicon oxide are the particles wherein at least a part of the surface of one iron oxide particle or the surface of the aggregates of a plurality of iron oxide particles is coated with silicon oxide, and the particle diameter of said iron oxide particle or said aggregates of iron oxide particles is 50 nm or less, and wherein said composition comprises an iron oxide particle dispersion having the average molar absorption coefficient of 1500 L/(mol·cm) or more for the light having wavelengths from 190 nm to 380 nm in a state that said coated iron oxide particles are dispersed in a dispersion medium.

2 . The silicon oxide-coated iron oxide composition for coating according to claim 1 , wherein said dispersion medium of the iron oxide particle dispersion is pure water.

3 . The silicon oxide-coated iron oxide composition for coating according to claim 1 , wherein said coated iron oxide particles are provided with an ester group, and said dispersion medium is butyl acetate.

4 . The silicon oxide-coated iron oxide composition for coating according to claim 1 , wherein
the molar absorption coefficient of said iron oxide particle dispersion for the light having wavelength of 400 nm is 500 L/(mol·cm) or more, or the molar absorption coefficient of said iron oxide particle dispersion for the light having wavelength of 300 nm is 1500 L/(mol·cm) or more, or the molar absorption coefficient of said iron oxide particle dispersion for the light having wavelength of 250 nm is 1500 L/(mol·cm) or more.

5 . The silicon oxide-coated iron oxide composition for coating according to claim 1 , wherein the molar absorption coefficient of said iron oxide particle dispersion for the light having wavelength of 220 nm is 2000 L/(mol·cm) or more.

6 . The silicon oxide-coated iron oxide composition for coating according to claim 1 , wherein the transmittance of said iron oxide particle dispersion for the light having wavelengths from 200 nm to 420 nm is 2.0% or less, and wherein the transmittance of said iron oxide particle dispersion for the light having wavelengths from 620 nm to 780 nm is 80% or more.

7 . The silicon oxide-coated iron oxide composition for coating according to claim 1 , wherein the haze value of said iron oxide particle dispersion is 2.0% or less at the concentration of 2 wt % of silicon oxide-coated iron oxide.

8 . The silicon oxide-coated iron oxide composition for coating according to claim 1 , wherein said silicon oxide comprises amorphous silicon oxide.

9 . The silicon oxide-coated iron oxide composition for coating according to claim 1 , wherein said iron oxide particles coated with silicon oxide is core-shell type iron oxide particles wherein the surface of the core iron oxide particles is coated with the shell silicon oxide, and wherein the primary particle diameter of said core-shell type iron oxide particles is 100.5% or more and 190% or less relative to the primary particle diameter of said core iron oxide particles.

10 . The silicon oxide-coated iron oxide composition for coating according to claim 1 , wherein the particle diameter of said iron oxide particles coated with silicon oxide is 100.5% or more and 190% or less relative to said particle diameter of the iron oxide particle or said aggregates of the iron oxide particles.

11 . The silicon oxide-coated iron oxide composition for coating according to claim 1 , further comprising a perylene pigment.

12 . A paint comprising the silicon oxide-coated iron oxide composition for coating according to claim 1 .

13 . A coating film comprising the silicon oxide-coated iron oxide composition for coating according to claim 1 .

14 . A vehicle equipped with the coating film according to claim 13 .

Assignees

• M Technique Co Ltd

Inventors

• Enomura Masakazu
• Honda Daisuke

Classifications

• C01P2004/04

  obtained by TEM, STEM, STM or AFM · CPC title

• C01P2002/82

  by IR- or Raman-data · CPC title

• C09D1/00

  Coating compositions, e.g. paints, varnishes or lacquers, based on inorganic substances · CPC title

• A61K8/25

  Silicon; Compounds thereof · CPC title

• C09D7/67

  Particle size smaller than 100 nm · CPC title