Alkaline storage battery cathode, method for manufacturing alkaline storage battery cathode, alkaline storage battery, method for manufacturing alkaline storage battery, alkaline storage battery cathode active material, and method for manufacturing alkaline storage battery cathode active material

Patent metadata

Field	Value
Publication number	US-2017194635-A1
Application number	US-201715465579-A
Country	US
Kind code	A1
Filing date	Mar 21, 2017
Priority date	Apr 18, 2011
Publication date	Jul 6, 2017
Grant date	—

Abstract

This alkaline storage battery cathode is provided with: nickel hydroxide particles covered by a cobalt-compound coating layer; a zinc compound; and an yttrium compound and/or an ytterbium compound. The zinc compound and the yttrium compound and/or ytterbium compound are blended at a blend ratio that is in accordance with the ratio of the capacity characteristics of the alkaline storage battery and the output characteristics of the alkaline storage battery.

First claim

1 . An alkaline storage battery cathode comprising:
a cathode active material powder made of nickel hydroxide particles coated with a cobalt-compound coating layer; and an additive powder mixed with the cathode active material powder at a certain proportion, wherein the additive powder includes a zinc compound powder, and at least one of an yttrium compound powder and an ytterbium compound powder, mixed with the zinc compound powder, wherein the zinc compound powder and the at least one of the yttrium compound powder and the ytterbium compound powder have a mixing ratio that is determined based on an index indicating a ratio of a capacity characteristic at an upper limit temperature of an operating temperature range of an alkaline storage battery using the alkaline storage battery cathode and an output characteristic of the alkaline storage battery at a lower limit temperature of the operating temperature range.

2 . The alkaline storage battery cathode according to claim 1 , wherein the nickel hydroxide particles include magnesium/nickel hydroxide solid solution particles.

3 . The alkaline storage battery cathode according to claim 1 , wherein the cobalt-compound coating layer is made of cobalt oxyhydroxide having β-type crystal structure.

4 . The alkaline storage battery cathode according to claim 1 , wherein:
the capacity characteristic at the upper limit temperature of the operating temperature range of the alkaline storage battery is a discharge capacity of the alkaline storage battery at 60 degrees Celsius, and the output characteristic at the lower limit temperature of the operating temperature range of the alkaline storage battery is a DC internal resistance of the alkaline storage battery at −30 degrees Celsius.

5 . The alkaline storage battery cathode according to claim 1 , wherein a ratio of the weight of zinc in the zinc compound powder to total of the weight of the zinc in the zinc compound powder and the weight of yttrium in the yttrium compound powder is no less than 0.35 and no more than 0.85.

6 . The alkaline storage battery cathode according to claim 1 , comprising:
a porous substrate; and a dry mixture filling pores of the porous substrate, wherein the dry mixture contains the nickel hydroxide particles, the zinc compound powder, and the at least one of the yttrium compound powder and the ytterbium compound powder.

7 . An alkaline storage battery comprising:
a cathode including a cathode active material powder made of nickel hydroxide particles coated with a cobalt-compound coating layer, and an additive powder mixed with the cathode active material powder at a certain proportion, the additive powder including a zinc compound powder and at least one of an yttrium compound powder and an ytterbium compound powder, mixed with the zinc compound powder; and wherein the zinc compound powder and the at least one of the yttrium compound powder and the ytterbium compound powder have a mixing ratio determined based on an index indicating a ratio of a capacity characteristic at an upper limit temperature of an operating temperature range of the alkaline storage battery using the cathode and an output characteristic of the alkaline storage battery at a lower limit temperature of the operating temperature range.

8 . The alkaline storage battery cathode according to claim 1 , wherein the cathode active material powder and the additive powder are mixed at the certain proportion to form a dry mixture that fills a porous substrate, and
wherein the cathode active material powder is coated nickel hydroxide particles each made of a nickel hydroxide core and a cobalt-compound coating layer coating the nickel hydroxide core, and wherein the coated nickel hydroxide particles have a specific surface area that is greater by no less than 3 m2/g and no more than 8 m2/g with respect to a specific surface area of the nickel hydroxide core, and the specific surface area of the coated nickel hydroxide particles is 18 to 23 m2/g.

9 . An alkaline storage battery comprising the alkaline storage battery cathode according to claim 8 .

Assignees

• Primearth Ev Energy Co Ltd

Inventors

• Kudo So
• Maehara Kenichi
• Takeda Sachio
• Ookawa Kazuhiro
• Takehara Satoru
• Sakamoto Hiroyuki

Classifications

• H01M4/62

  Selection of inactive substances as ingredients for active masses, e.g. binders, fillers · CPC title

• H01M4/32 Primary

  Nickel oxide or hydroxide electrodes · CPC title

• H01M2004/028

  Positive electrodes · CPC title

• H01M10/30

  Nickel accumulators (H01M10/34 takes precedence) · CPC title

• H01M4/26

  Processes of manufacture · CPC title