Amphiphilic anisotropic powder and method for manufacturing same

Patent metadata

Field	Value
Publication number	US-2017190846-A1
Application number	US-201515314869-A
Country	US
Kind code	A1
Filing date	May 29, 2015
Priority date	May 30, 2014
Publication date	Jul 6, 2017
Grant date	—

Abstract

Disclosed are an amphiphilic anisotropic powder and a method for manufacturing the same. In an aspect, the technique disclosed in the present specification has an effect of providing an amphiphilic anisotropic powder which simultaneously maximizes chemical interface activity and physical interface activity by controlling amphiphilic property, which is the characteristic of an existing surfactant, and geometric property, which is the characteristic of powder macroparticles. In another aspect, the technique disclosed in the present specification has an effect of providing a method for manufacturing an amphiphilic anisotropic powder, which can be mass-produced due to a simple method and an excellent yield and of which the particle size can be controlled to about 100 to about 2500 nm.

First claim

1 . Amphiphilic anisotropic powder comprising a first hydrophilic polymer spheroid and a second hydrophobic polymer spheroid,
wherein the first polymer spheroid and the second polymer spheroid are bound with each other in such a manner that one polymer spheroid at least partially penetrates the other polymer spheroid, and the first polymer spheroid has a core-shell structure and the shell comprises a functional group.

2 . The amphiphilic anisotropic powder according to claim 1 , wherein the core of the first polymer spheroid and the second polymer spheroid comprise a vinyl polymer, and the shell of the first polymer spheroid comprises a copolymer of a vinyl monomer with a functional group.

3 . The amphiphilic anisotropic powder according to claim 2 , wherein the vinyl polymer is a vinyl aromatic polymer.

4 . The amphiphilic anisotropic powder according to claim 1 , wherein the functional group is a siloxane.

5 . The amphiphilic anisotropic powder according to claim 1 , wherein the shell of the first polymer spheroid further comprises a hydrophilic functional group introduced thereto.

6 . The amphiphilic anisotropic powder according to claim 5 , wherein the hydrophilic functional group is at least one selected from the group consisting of a carboxylic acid group, sulfone group, phosphate group, amino group, alkoxy group, ester group, acetate group, polyethylene glycol group and a hydroxyl group.

7 . The amphiphilic anisotropic powder according to claim 1 , which has a symmetric form, asymmetric snowman form or asymmetric reversed snowman form on the basis of the binding portion where the first polymer spheroid and the second polymer spheroid are bound with each other.

8 . The amphiphilic anisotropic powder according to claim 1 , which has a particle size of 100-2500 nm.

9 . The amphiphilic anisotropic powder according to claim 1 , which forms macroemulsion particles with a size of 2-200 μm.

10 . A method for preparing amphiphilic anisotropic powder as defined in claim 1 , comprising the steps of:
(1) agitating a first monomer with a polymerization initiator to form a core of a first polymer spheroid; (2) agitating the resultant core of the first polymer spheroid with a first monomer, polymerization initiator and a functional group-containing compound to form a coated first polymer spheroid having a core-shell structure; (3) agitating the resultant first polymer spheroid having a core-shell structure with a second monomer and polymerization initiator to provide anisotropic powder in which a second polymer spheroid is formed; and (4) introducing a hydrophilic functional group to the resultant anisotropic powder.

11 . The method for preparing amphiphilic anisotropic powder according to claim 10 , wherein the first monomer is mixed with the polymerization initiator at a weight ratio of 100-1000:1, in step (1).

12 . The method for preparing amphiphilic anisotropic powder according to claim 10 , wherein the functional group-containing compound is siloxane-containing (meth)acrylate, in step (2).

13 . The method for preparing amphiphilic anisotropic powder according to claim 10 , wherein the first monomer, polymerization initiator and the functional group-containing compound are mixed at a weight ratio of 80-98:0.2-1.0:1-20, in step (2).

14 . The method for preparing amphiphilic anisotropic powder according to claim 10 , wherein the second monomer and polymerization initiator are mixed at a weight ratio of 150-250:1, in step (3).

15 . The method for preparing amphiphilic anisotropic powder according to claim 10 , wherein the second monomer is mixed in an amount of 40-300 parts by weight based on 100 parts by weight of the first polymer spheroid having a core-shell structure, in step (3).

16 . The method for preparing amphiphilic anisotropic powder according to claim 10 , wherein the hydrophilic functional group is introduced by using a silane coupling agent and a reaction modifier, in step (4).

17 . The method for preparing amphiphilic anisotropic powder according to claim 16 , wherein the silane coupling agent is N-[3-(trimethoxysilyl) propyl]ethylenediamine.

18 . The method for preparing amphiphilic anisotropic powder according to claim 16 , wherein the reaction modifier is ammonium hydroxide.

Assignees

• Amorepacific Corp

Inventors

• Nam Jin
• Kim Youngsun
• An Soon Ae
• Kang Byung Young
• Han Sang Hoon

Classifications

• C08L101/02

  characterised by the presence of specified groups {, e.g. terminal or pendant functional groups} · CPC title

• C08J7/12

  Chemical modification · CPC title

• C08F10/00

  Homopolymers and copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond · CPC title

• C08F212/08 Primary

  Styrene · CPC title

• C08J3/12 Primary

  Powdering or granulating · CPC title