Method for Processing Packaging Material

Patent metadata

Field	Value
Publication number	US-2017073244-A1
Application number	US-201515310961-A
Country	US
Kind code	A1
Filing date	May 21, 2015
Priority date	May 28, 2014
Publication date	Mar 16, 2017
Grant date	—

Abstract

The subject of the present invention is a method for processing metallized packaging materials, especially beverage cartons, or blister packaging.
According to the invention, the aluminum is dissolved with the aid of acid and separated from the plastic. The metal-containing acid solution then undergoes pyrohydrolytic treatment and the acid is thus recovered. The aluminum can be recovered as valuable aluminum oxide.

First claim

1 .- 17 . (canceled)

18 . A method for processing packaging materials containing plastics, aluminum and other metals, comprising:
separating other metals that are soluble in hydrochloric acid from the packaging material, leaving a mix containing plastics and aluminum solids; subjecting the mix to acid that dissolves the aluminum, thereby forming a solution of aluminum in the acid, with dispersed plastic solids; separating the plastic solids from the solution of aluminum in acid; pyrohydrolytically treating the solution of aluminum in acid to form an aluminum oxide fraction and a gaseous acid fraction; and recovering the acid in the gaseous acid fraction by absorption or condensation.

19 . The method according to claim 18 , wherein the packaging material includes pulp and the pulp is detached from the packaging material to form a pulp suspension and the pulp suspension is separated from the plastics and aluminum before the aluminum is dissolved in acid.

20 . The method according to claim 18 , wherein the acid used to dissolve the aluminum is hydrochloric acid.

21 . The method according to claim 18 , wherein the pyrohydrolytic treatment is conducted in a spray roasting reactor.

22 . The method according to claim 18 , wherein the aluminum oxide formed undergoes thermal post-treatment.

23 . The method according to claim 22 , wherein the thermal post-treatment takes place at a temperature between 800° C. and 2400° C.

24 . The method according to claim 22 , wherein the thermal post-treatment is conducted in a lime kiln or a plasma reactor.

25 . The method according to claim 18 , wherein the aluminum oxide is ground.

26 . The method according to claim 18 , wherein the aluminum oxide is subjected to fractionation according to particle size.

27 . The method according to claim 18 , wherein the acid recovered in the pyrohydrolytic treatment is used again to dissolve the aluminum.

28 . The method according to claim 19 , wherein after the other metals are separated, pulp fibers still adhering to the plastics or aluminum are dynamically separated before the aluminum is dissolved in the acid.

29 . The method according to claim 19 , wherein the plastics are fed to an additional cleaning stage after separating the solution of aluminum in acid and any remaining pulp fibers and acid residues are removed from the plastics in this additional cleaning stage.

30 . The method according to claim 29 , wherein the plastics are washed and the wash water containing acid is used for absorption of the gaseous products formed.

31 . The method according to claim 18 , wherein the plastics and the aluminum are shredded in the acid before the aluminum is dissolved.

32 . The method according to claim 18 , wherein the solution of aluminum in acid is cleaned using wet chemical or physical methods before pyrohydrolitic treatment.

33 . The method according to claim 18 , wherein additives, such as metals, are added to the solution of aluminum in acid before the pyrohydrolitic treatment.

34 . A method for processing packaging materials containing plastics, metals including aluminum, and pulp, comprising:
separating the pulp from the packaging material; separating metals other than aluminum that are soluble in hydrochloric acid from the packaging material; after separating the pulp and the other metals to leave a remaining mix of plastics and aluminum solids, subjecting the mix to hydrochloric acid thereby dissolving the aluminum and forming a metal-containing solution of the acid with dispersed plastic solids; separating the metal-containing solution of the acid from the plastic solids; pyrohydrolytically treating the metal-containing solution in order to form an aluminum oxide fraction and a gaseous acid fraction; and recovering the acid in the gaseous acid fraction by absorption or condensation.

35 . The method according to claim 34 , wherein the separated pulp forms a pulp suspension and the pulp suspension is separated from the plastics and aluminum before the aluminum is dissolved in acid.

36 . The method according to claim 35 , wherein the plastics and the aluminum are shredded in the acid before the aluminum is dissolved.

37 . The method according to claim 36 , wherein the plastics are fed to an additional cleaning stage after separating the solution of aluminum in acid and any remaining fibers and acid residues are removed from the plastics in this additional cleaning stage.

Assignees

• Andritz Ag Maschf

Inventors

• Gabl Helmuth

Classifications

• C22B21/00

  Obtaining aluminium · CPC title

• C22B7/00

  Working up raw materials other than ores, e.g. scrap, to produce non-ferrous metals and compounds thereof; {Methods of a general interest or applied to the winning of more than two metals (briquetting of scrap C22B1/248; preliminary treatment of scrap C22B1/005)} · CPC title

• B29B17/02

  Separating plastics from other materials · CPC title

• B29B2017/0293

  Dissolving the materials in gases or liquids · CPC title

• B29L2031/7166

  Cartons of the fruit juice or milk type, i.e. containers of polygonal cross sections formed by folding blanks into a tubular body with end-closing or contents-supporting elements, e.g. gable type containers (in general B65D5/06) · CPC title