Galvanized steel sheet and method for producing the same (as amended)

Patent metadata

Field	Value
Publication number	US-2016369406-A1
Application number	US-201515121589-A
Country	US
Kind code	A1
Filing date	Feb 27, 2015
Priority date	Feb 27, 2014
Publication date	Dec 22, 2016
Grant date	—

Abstract

A method for producing a galvanized steel sheet includes an oxide layer forming step of bringing a galvanized steel sheet into contact with an acidic solution containing sulfate ions, then holding the galvanized steel sheet in contact for 1 to 60 seconds, and then washing the galvanized steel sheet with water; and a neutralization treatment step of holding a surface of an oxide layer, which has been formed in the oxide layer forming step, in contact with an alkaline aqueous solution for 0.5 seconds or longer, and then performing washing with water and drying. The alkaline aqueous solution contains P ions at a P concentration of 0.01 g/L or more and carbonate ions at a carbonate ion concentration of 0.1 g/L or more.

First claim

1 . A galvanized steel sheet comprising a steel sheet and a galvanized coating layer formed on the steel sheet,
wherein the coating layer includes an oxide layer in a surface layer, the oxide layer having an average thickness of 20 nm or more, and the oxide layer comprises Zn, O, H, S, C, P, and unavoidable impurities, and contains 50 mg/m 2 or more of Zn, 5 mg/m 2 or more of S, 0.2 mg/m 2 or more of C, and 0.2 mg/m 2 or more of P.

2 . The galvanized steel sheet according to claim 1 , wherein a sulfate group, a carbonate group, a hydroxyl group, and a phosphate group exist in the oxide layer.

3 . The galvanized steel sheet according to claim 1 , wherein the oxide layer contains a crystal structure represented by Zn 4 (SO 4 ) 1-X (CO 3 ) X (OH) 6 .nH 2 O,
where X is a real number in the range of 0<X<1 and n is a real number in the range of 0≦n≦10.

4 . The galvanized steel sheet according to claim 2 , wherein the oxide layer contains a crystal structure represented by Zn 4 (SO 4 ) 1-X (CO 3 ) X (OH) 6 .nH 2 O,
where X is a real number in the range of 0<X<1 and n is a real number in the range of 0≦n≦10.

5 . The galvanized steel sheet according to claim 1 , wherein the oxide layer contains at least one selected from PO 4 3− , P 2 O 7 4− , P 3 O 9 5− , and an inorganic acid or a metal compound of any of the foregoing, and
the metal compound contains at least one selected from sodium and zinc.

6 . The galvanized steel sheet according to claim 2 , wherein the oxide layer contains at least one selected from PO 4 3− , P 2 O 7 4− , P 3 O 9 5− , and an inorganic acid or a metal compound of any of the foregoing, and
the metal compound contains at least one selected from sodium and zinc.

7 . The galvanized steel sheet according to claim 3 , wherein the oxide layer contains at least one selected from PO 4 3− , P 2 O 7 4− , P 3 O 9 5− , and an inorganic acid or a metal compound of any of the foregoing, and
the metal compound contains at least one selected from sodium and zinc.

8 . The galvanized steel sheet according to claim 4 , wherein the oxide layer contains at least one selected from PO 4 3− , P 2 O 7 4− , P 3 O 9 5− , and an inorganic acid or a metal compound of any of the foregoing, and
the metal compound contains at least one selected from sodium and zinc.

9 . The galvanized steel sheet according to claim 1 , wherein the galvanized steel sheet is a hot-dip galvannealed steel sheet, a hot-dip galvanized steel sheet, or an electrogalvanized steel sheet.

10 . A method for producing the galvanized steel sheet according to claim 1 , the method comprising:
an oxide layer forming step of bringing a galvanized steel sheet into contact with an acidic solution containing sulfate ions, then holding the galvanized steel sheet in contact for 1 to 60 seconds, and then washing the galvanized steel sheet with water; and a neutralization treatment step of holding a surface of an oxide layer, which has been formed in the oxide layer forming step, in contact with an alkaline aqueous solution for 0.5 seconds or longer, and then performing washing with water and drying, wherein the alkaline aqueous solution contains P ions at a P concentration of 0.01 g/L or more and carbonate ions at a carbonate ion concentration of 0.1 g/L or more, and has a pH of 9 to 12.

11 . The method for producing a galvanized steel sheet according to claim 10 , wherein the alkaline aqueous solution contains a carbonate and at least one phosphorus compound selected from a phosphate, a pyrophosphate, and a triphosphate.

12 . The method for producing a galvanized steel sheet according to claim 10 , wherein the carbonate ions are contained at a carbonate ion concentration of 0.6 g/L or more.

13 . The method for producing a galvanized steel sheet according to claim 10 , wherein the carbonate ions are contained at a carbonate ion concentration of 1.2 g/L or more.

14 . The method for producing a galvanized steel sheet according to claim 10 , wherein the alkaline aqueous solution has a pH of 9 to 12 and a temperature of 20° C. to 70° C.

15 . The method for producing a galvanized steel sheet according to claim 10 , wherein the acidic solution has a pH buffering action and has a pH-increasing property in the range of 0.003 to 0.5, where the pH-increasing property is defined by an amount (L) of a 1.0 mol/L sodium hydroxide solution needed to increase a pH of 1 L of the acidic solution from 2.0 to 5.0.

16 . The method for producing a galvanized steel sheet according to claim 10 , wherein the acidic solution contains a total of 5 to 50 g/L of at least one salt selected from an acetate, a phthalate, a citrate, a succinate, a lactate, a tartrate, a borate, and a phosphate, and has a pH of 0.5 to 5.0 and a solution temperature of 20° C. to 70° C.

17 . The method for producing a galvanized steel sheet according to claim 10 , wherein, in the oxide layer forming step, an acidic solution coating weight on a steel sheet surface after contacting the acidic solution is 15 g/m 2 or less.

18 . The method for producing a galvanized steel sheet according to claim 10 , wherein the galvanized steel sheet is a hot-dip galvannealed steel sheet, a hot-dip galvanized steel sheet, or an electrogalvanized steel sheet.

19 . The method for producing a galvanized steel sheet according to claim 10 , wherein, after a steel sheet is galvanized and before the oxide layer forming step, a surface is activated by being brought into contact with an alkaline aqueous solution.

20 . The method for producing a galvanized steel sheet according to claim 10 , wherein, after a steel sheet is galvanized and before the oxide layer forming step, temper rolling is performed.

Assignees

• Jfe Steel Corp

Inventors

• Hoshino Katsuya
• Taira Shoichiro
• Nagoshi Masayasu
• Hanada Kazutoshi

Classifications

• C23C28/3225

  with at least one zinc-based layer · CPC title

• C23C22/50 Primary

  Treatment of iron or alloys based thereon · CPC title

• C23C22/62

  Treatment of iron or alloys based thereon · CPC title

• C23C2/40

  Plates; Strips · CPC title

• C23C22/53

  Treatment of zinc or alloys based thereon · CPC title