Alumina-Forming, High Temperature Creep Resistant Ni-Based Alloys
US2016369376A1 · US · A1
| Field | Value |
|---|---|
| Publication number | US-2016369376-A1 |
| Application number | US-201514745740-A |
| Country | US |
| Kind code | A1 |
| Filing date | Jun 22, 2015 |
| Priority date | Jun 22, 2015 |
| Publication date | Dec 22, 2016 |
| Grant date | — |
How to read this patent
A practical reading order for non-experts. Skip the full description unless you need deep technical detail.
- Title
What the patent document calls the invention.
- Abstract
A short plain-language summary of the technical disclosure.
- Assignees and inventors
Who owns or filed the patent and who is credited as inventor.
- Key dates
Filing, priority, publication, and grant dates set the timeline.
- First independent claim
The legal scope of protection — read this for what is actually claimed.
- CPC / IPC classifications
Technology tags used to group this patent with similar filings.
- Citations and related patents
Prior art links and similar publications in this corpus.
Abstract
Official abstract text for this publication.
An alumina-forming, high temperature creep resistant alloy is composed essentially of, in terms of weight percent: up to 10 Fe, 3.3 to 4.6 Al, 6 to 22 Cr, 0.68 to 0.74 Mn, 5.2 to 6.6 Mo, 0.4 to 1.2 Ti, up to 0.1 Hf, 0.005 to 0.05 La, 0.4 to 0.6 W, 0.1 to 0.35 C, up to 0.002 B, 0.001 to 0.02 N, balance Ni.
First claim
Opening claim text (preview).
What is claimed is: 1 . An alloy consisting essentially of, in terms of weight percent: Fe up to 10 Al 3.3 to 4.6 Cr 6 to 22 Mn 0.68 to 0.74 Mo 5.2 to 6.6 Ti 0.4 to 1.2 Hf up to 0.1 La 0.005 to 0.05 W 0.4 to 0.6 C 0.1 to 0.35 B up to 0.002 N 0.001 to 0.02 Ni balance 2 . An alloy in accordance with claim 1 wherein Fe is present in an amount of 1 to 6 weight percent. 3 . An alloy in accordance with claim 2 wherein Fe is present in an amount of 0.1 to 2 weight percent. 4 . An alloy in accordance with claim 1 wherein Cr is present in an amount of 16 to 20 weight percent. 5 . An alloy consisting essentially of, in terms of weight percent: Fe 9.4 to 10 Al 3.6 to 4.2 Cr 16 to 17 Mn 0.68 to 0.74 Mo 5.2 to 5.4 Ti 0.45 to 0.5 La 0.005 to 0.05 W 0.4 to 0.6 C 0.1 to 0.35 B up to 0.002 N 0.001 to 0.02 Ni balance 6 . An alloy consisting essentially of, in terms of weight percent: Fe 1.8 to 2.2 Al 3.3 to 4.0 Cr 17 to 20 Mn 0.68 to 0.74 Mo 6.0 to 6.6 Ti 0.4 to 0.6 Hf 0.06 to 0.1 La 0.005 to 0.05 W 0.4 to 0.6 C 0.1 to 0.35 B up to 0.002 N 0.001 to 0.02 Ni balance
Assignees
Inventors
Classifications
- C22C19/056Primary
with the maximum Cr content being at least 10% but less than 20% · CPC title
with the maximum Cr content being less 10% · CPC title
Patent family
Related publications grouped by family.
External sources
Frequently asked questions
Answers are generated from the same data shown on this page.
- What does patent US2016369376A1 cover?
- An alumina-forming, high temperature creep resistant alloy is composed essentially of, in terms of weight percent: up to 10 Fe, 3.3 to 4.6 Al, 6 to 22 Cr, 0.68 to 0.74 Mn, 5.2 to 6.6 Mo, 0.4 to 1.2 Ti, up to 0.1 Hf, 0.005 to 0.05 La, 0.4 to 0.6 W, 0.1 to 0.35 C, up to 0.002 B, 0.001 to 0.02 N, balance Ni.
- Who is the assignee on this patent?
- Ut Battelle Llc
- What technology area does this patent fall under?
- Primary CPC classification C22C19/056. Mapped technology areas include Chemistry & Metallurgy.
- When was this patent published?
- Publication date Thu Dec 22 2016 00:00:00 GMT+0000 (Coordinated Universal Time) (A1). Legal status and post-grant events are not shown on this page.
- What related patents are in patentsdb?
- We list 8 related publications on this page (citations in our corpus or others sharing the same primary CPC).