Binder composition for nonaqueous battery electrodes, slurry for nonaqueous battery electrodes, nonaqueous battery electrode, and nonaqueous battery

Patent metadata

Field	Value
Publication number	US-2016248095-A1
Application number	US-201415024444-A
Country	US
Kind code	A1
Filing date	Jun 20, 2014
Priority date	Sep 27, 2013
Publication date	Aug 25, 2016
Grant date	—

Abstract

A binder composition for nonaqueous battery electrodes is prepared by adding a small amount of an acetylene glycol compound to an aqueous polymer emulsion obtained by emulsion polymerization of a monomer mixture comprising from 15 to 70% by mass of styrene (a), from 20 to 80% by mass of an ethylenically unsaturated carboxylate (b), from 1 to 10% by mass of an ethylenically unsaturated carboxylic acid (c), from 0.1 to 5% by mass of a crosslinkable ethylenically unsaturated monomer (d), and from 0 to 20% by mass of another monoethylenically unsaturated monomer (e). When the above binder composition is used, an active material is not peeled off in the step of cutting a collector even when a small amount of the binder is used, and a nonaqueous battery excellent in a charge-discharge cycle property can be produced.

First claim

1 . A binder composition for nonaqueous battery electrodes, the composition being prepared by adding one or more acetylene glycol compounds selected from the group consisting of compounds represented by the following formula (1):

wherein R 1 to R 4 each independently represent a hydrogen atom or an alkyl group having from 1 to 8 carbon atoms and derivatives thereof, to an aqueous polymer emulsion,
wherein the aqueous polymer emulsion is obtained by emulsion polymerization of a monomer mixture comprising from 15 to 70% by mass of styrene (a), from 20 to 80% by mass of an ethylenically unsaturated carboxylate (b), from 1 to 10% by mass of an ethylenically unsaturated carboxylic acid (c), from 0.1 to 5% by mass of a crosslinkable ethylenically unsaturated monomer (d), and from 0 to 20% by mass of another monoethylenically unsaturated monomer (e), and
from 0.02 to 0.7 part by mass of the one or more acetylene glycol compounds is added to 100 parts by mass of non-volatile matter of the aqueous polymer emulsion.

2 . The binder composition for nonaqueous battery electrodes as claimed in claim 1 , wherein the compound represented by the formula (1) is a compound represented by the following formula (2):

3 . The binder composition for nonaqueous battery electrodes as claimed in claim 1 , wherein the acetylene glycol compound is a compound in which an alkylene oxide having from 2 to 4 carbon atoms or an oligomer thereof is added to the compound represented by the formula (1).

4 . The binder composition for nonaqueous battery electrodes as claimed in claim 3 , wherein the oligomer has a degree of polymerization of from 2 to 40.

5 . The binder composition for nonaqueous battery electrodes as claimed in claim 3 , wherein the alkylene oxide is ethylene oxide.

6 . The binder composition for nonaqueous battery electrodes as claimed in claim 1 , wherein the content of non-volatile matter of the binder composition is from 5 to 70% by mass.

7 . The binder composition for nonaqueous battery electrodes as claimed in claim 1 , wherein at least a part of the ethylenically unsaturated carboxylate (b) is an ethylenically unsaturated carboxylate having a polar group.

8 . The binder composition for nonaqueous battery electrodes as claimed in claim 7 , wherein the polar group is a hydroxy group or a glycidyl group.

9 . The binder composition for nonaqueous battery electrodes as claimed in claim 1 , wherein the electrode is a negative electrode.

10 . A slurry for nonaqueous battery electrodes comprising an electrode active material and a binder composition as claimed in claim 1 , wherein the electrode active material/the non-volatile matter of the binder composition (mass ratio) is from 100/0.1 to 100/1.8.

11 . The slurry for nonaqueous battery electrodes as claimed in claim 10 , wherein the electrode active material/the non-volatile matter of the binder composition (mass ratio) is from 100/0.3 to 100/1.6.

12 . The slurry for nonaqueous battery electrodes as claimed in claim 10 , wherein the content of the acetylene glycol compound is from 1 to 100 ppm by mass in the total amount of the slurry.

13 . The slurry for nonaqueous battery electrodes as claimed in claim 10 , wherein the content of the acetylene glycol compound is from 2 to 50 ppm by mass in the total amount of the slurry.

14 . The nonaqueous battery electrode formed by using the slurry for nonaqueous battery electrodes as claimed in claim 10 .

15 . A nonaqueous battery comprising the nonaqueous battery electrode as claimed in claim 14 .

Assignees

• Showa Denko Kk

Inventors

• Kurata Tomonori
• Hanasaki Mitsuru
• UCHIYASHIKI Junya

Classifications

• H01M4/13

  Electrodes for accumulators with non-aqueous electrolyte, e.g. for lithium-accumulators; Processes of manufacture thereof · CPC title

• H01M4/622 Primary

  being polymers · CPC title

• H01M4/137

  Electrodes based on electro-active polymers · CPC title

• C08L1/02

  Cellulose; Modified cellulose · CPC title

• H01M4/1399

  of electrodes based on electro-active polymers · CPC title