Process stabilization of polymer compositions comprising phosphorous containing flame retardants

Patent metadata

Field	Value
Publication number	US-2016200897-A1
Application number	US-201514717573-A
Country	US
Kind code	A1
Filing date	May 20, 2015
Priority date	Jan 9, 2015
Publication date	Jul 14, 2016
Grant date	—

Abstract

Flame retardant polymer compositions comprising certain polymers, a flame retardant material obtained by heating certain phosphonic acid salts at temperatures over 200° C. and certain clays or metal compounds such as select metal borates, oxides, hydroxides, oxide hydroxides etc., are readily processed at elevated temperatures and under high stress conditions whereas similar compositions without the clays or metal compounds of the invention are prone to decomposition. For example, polyamide compositions comprising the flame retardant material obtained by heating certain phosphonic acid salts at temperatures over 200° C., hydrotalcite clays, and/or borates, oxides, hydroxides, oxide hydroxides of zinc or calcium, are highly stable to thermal processing under strenuous conditions such as high temperature extrusion.

First claim

1 . A flame retardant polymer composition comprising:
a) a thermoset or thermoplastic polymer; b) from 1% to 50%, by weight based on the total weight of the flame retardant polymer composition, of a flame retardant material obtained by thermal conversion of salts of formula (I) before incorporation into the polymer composition by a process comprising heating at temperatures of about 200° C. or higher from about 0.01 hour to about 20 hours one or more than one compound of formula (I)

wherein
R is C 1-12 alkyl, C 6-10 aryl, C 7-18 alkylaryl, or C 7-18 arylalkyl, wherein said alkyl, aryl, alkylaryl, or arylalkyl are unsubstituted or are substituted by halogen, hydroxyl, amino, C 1-4 alkylamino, di-C 1-4 alkylamino, C 1-4 alkoxy, carboxy or C 2-5 alkoxycarbonyl;
M is a metal,
y is a number of from 1 to 4 so that M (+)y is a metal cation where (+)y represents the charge formally assigned to the cation, and p is a number of from 1 to 4; and

c) one or more compounds selected from the group consisting of hydrotalcite days, metal borates, metal oxides and metal hydroxides.

2 . The flame retardant polymer composition according to claim 1 wherein the metal of the metal borates, metal oxides and metal hydroxides is zinc or calcium.

3 . The flame retardant polymer composition according to claim 2 comprising one or more additional flame retardants, one or more synergists and/or one or more flame retardant adjuvants selected from the group consisting of halogenated flame retardants, alkyl phosphine oxide flame retardants, aryl phosphine oxide flame retardants, alkyl phosphate flame retardants, aryl phosphate flame retardants, alkyl aryl phosphonates, aryl phosphonates, alkyl phosphinates, aryl phosphinates, salts of alkyl phosphinic acid, salts of aryl phosphinic acid, carbon black, graphite, carbon nanotubes, silicones, polyphenylene ether, melamine, melamine derivatives, melamine condensation products, melamine salts, metal hydroxides, oxides, oxide hydrates and borates wherein the metal is other than zinc or calcium, carbonates, sulfates, sulfides, phosphates, phosphites, carboxylates, hypophosphites, silicates, and mixed metal salts.

4 . The flame retardant polymer composition according to claim 3 wherein the one or more additional flame retardants, one or more synergists and/or one or more flame retardant adjuvants is selected from the group consisting of benzylic phosphine oxides, poly benzylic phosphine oxides, melamine, melam, melem, melon, melamine cyanurate, melamine borate, melamine phosphates, melamine metal phosphates, talc, calcium silicate, aluminosilicate, aluminosilicate as hollow tubes, magnesium carbonate, barium sulfate, boron phosphate, exfoliated vermiculite, magnesium oxide, magnesium hydroxide, aluminum oxide, aluminum oxide hydroxide, aluminum trihydrate, aluminum hydrogen phosphite, silica, tin oxide, antimony oxide (III and V) and oxide hydrate, titanium oxide, zirconium oxide and zirconium hydroxide.

5 . The flame retardant polymer composition according to claim 4 wherein the one or more additional flame retardants, one or more synergists and/or one or more flame retardant adjuvants is selected from the group consisting of aluminum hydrogen phosphite, melem, melam, melon, a melamine metal phosphate wherein the metal comprises aluminum, magnesium or zinc, an aluminum tris(dialkylphosphinate), methylene-diphenylphosphine oxide-substituted polyaryl ether, xylylenebis(diphenylphosphine oxide), 4,4′-bis(diphenylphosphinylmethyl)-1,1′-biphenyl, ethylene bis-1,2-bis-(9,10-dihydro-9-oxy-10-phosphaphenanthrene-10-oxide)ethane and dimelamine zinc pyrophosphate.

6 . The flame retardant polymer composition according to claim 3 wherein the one or more additional flame retardants, one or more synergists and/or one or more flame retardant adjuvants comprises one or more halogenated flame retardants, alkyl or aryl phosphine oxide flame retardants, alkyl or aryl phosphate flame retardants, alkyl or aryl phosphonates, alkyl or aryl phosphinates, salts of alkyl or aryl phosphinic acid, carbon black, graphite, carbon nanotubes, silicones, polyphenylene ether, melamine, melamine derivatives, melamine condensation products or melamine salts.

7 . The flame retardant polymer composition according to claim 2 wherein the flame retardant material (b) is obtained by a process comprising:
i) preparing an intermediate salt complex by treating one or more phosphonic acid compound with one or more appropriate metal compound to give an intermediate salt complex corresponding to formula (I) comprising multiple values for R and/or M, and then heating the intermediate salt complex at temperatures of about 200° C. or higher for about 0.01 hour to about 20 hours;

or
ii) preparing an intimate salt mixture by combining two or more individual metal phosphonic acid salts of formula (I) which have differing values for R and/or M, and then heating the intimate salt mixture at temperatures of about 200° C. or higher for about 0.01 hour to about 20 hours;

or
(iii) heating at temperatures of about 200° C. or higher for about 0.01 hour to about 20 hours two or more separate metal phosphonic acid salts of formula (I), which differ by having different values for R and/or M to form individual flame retardant materials that are subsequently mixed together to form a blended flame retardant material.

8 . The flame retardant polymer composition according to claim 1 wherein M in formula (I) is Li, K, Na, Mg, Ca, Ba, Zn, Zr, B, AI, Si, Ti, Sn or Sb.

9 . The flame retardant polymer composition according to claim 1 wherein M in formula (I) is Al or Ca.

10 . The flame retardant polymer composition according to claim 1 wherein in formula (I) R is unsubstituted C 1-6 alkyl, C 6 aryl, C 7-10 alkylaryl, or C 7-12 arylalkyl.

11 . The flame retardant polymer composition according to claim 9 wherein R is methyl, ethyl, propyl, isopropyl, benzyl or phenyl.

12 . The flame retardant polymer composition according to claim 1 wherein the thermoset or thermoplastic polymer comprises one or more of a polyolefin homopolymer, polyolefin copolymer, rubber, epoxy resin, polyester, polyurethane, polysulfone, polyimide, polyphenylene ether, styrenic polymer, styrenic copolymer, polycarbonate, acrylic polymer, polyamide, polyacetal, epoxy resin, biodegradable polymer or a blend thereof.

13 . The flame retardant polymer composition according to claim 1 wherein the thermoset or thermoplastic polymer comprises one or more of a polyphenylene ether/styrenic resin blend, ABS, polyvinyl chloride/ABS blend, methacrylonitrile containing ABS, α-methylstyrene containing ABS, polyester/ABS, polycarbonate/ABS, impact modified polyester or impact modified polystyrene.

14 . The flame retardant polymer composition according to claim 2 wherein the thermoset or thermoplastic polymer comprises one or more of a polyolefin homopolymer, polyolefin copolymer, rubber, epoxy resin, polyester, polyurethane, polysulfone, polyimide, polyphenylene ether, styrenic polymer, styrenic copolymer, polycarbonate, acrylic polymer, polyamide, polyacetal, epoxy resin, biodegradable polymer or a blend thereof.

15 . The flame retardant polymer composition according to claim 14 wherein the thermoset or thermoplastic polymer comprises one or more of a styrenic polymer, polyolefin, polyester, epoxy resin, polycarbonate, polyamide, or polyurethane.

16 . The flame retardant polymer composi

Assignees

• Chemtura Corp

Inventors

• Stockdale Zachary D
• Timberlake Larry D
• Hanson Mark V
• Fielding William R

Classifications

• C09K21/04

  containing phosphorus · CPC title

• C08K3/32

  Phosphorus-containing compounds · CPC title

• C09K21/12

  containing phosphorus · CPC title

• C08K3/38

  Boron-containing compounds · CPC title

• C08K2003/387

  Borates · CPC title